Method of producing ferrous sintered alloy of improved wear resistance
Assignee: Nippon Piston Ring Co Ltd
•
Filing: 1977-02-23
•
Granted: 1978-10-31
•
Expires: 1997-02-23
Abstract
Abstract A method of producing a ferrous alloy material having improved wear resistance comprising (1) mixing powders of a ferrous alloy, tungsten and optionally at least one element selected from the group consisting of C, Ni, Mn, Mo, Cr, and Cu, (2) sintering the mixture of powders of step (1) to form a sintered product, (3) infiltrating the sintered product of step (2) with molten copper or a copper alloy to produce an infiltrated sintered product and (4) cooling the infiltrated sintered product of step (3).
Inventors
- 👤 Kentaro Takahashi
- 👤 Shigeru Urano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:05
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/24; B22F3/26; C; C22; C22C; C22C33/00; C22C33/02; C22C33/0242; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/1216; Y10T428/12174
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
169 words
A method of producing a wear-resistant sintered ferrous alloy including the steps of (1) mixing powders of a ferrous alloy containing more than about 50% by weight iron, tungsten in the range of about 0.5 to 5.0% by weight, and optionally at least one of an element selected from the group consisting of C, Ni, Mn, Mo, Cr and Cu, (2) sintering the mixture of powders of step (1) to produce a sintered product, (3) infiltrating into the sintered product of step (2) a component selected from the group consisting of copper or a copper alloy principally containing copper at a temperature above the melting point of the copper or the copper alloy to produce an infiltrated sintered product and (4) cooling the infiltrated sintered product of step (3); the improvement comprising said mixture of powders of step (1) having a composition sufficient to cause the production of martensite and bainite matrixes during the cooling step (4) in an amount of at least about 10% of the alloy microstructure.
Claim 2
Independent Claim
169 words
A method of producing a wear-resistant sintered ferrous alloy including the steps of (1) mixing powders of a ferrous alloy containing more than about 50% by weight iron, tungsten in the range of about 0.5 to 5.0% by weight, and optionally at least one of an element selected from the group consisting of C, Ni, Mn, Mo, Cr and Cu, (2) sintering the mixture of powders of step (1) to produce a sintered product, (3) infiltrating into the sintered product of step (2) a component selected from the group consisting of copper or a copper alloy principally containing copper at a temperature above the melting point of the copper or the copper alloy to produce an infiltrated sintered product and (4) cooling the infiltrated sintered product of step (3); the improvement comprising said mixture of powders of step (1) having a composition sufficient to cause the production of martensite and bainite matrixes during the cooling step (4) in an amount of at least about 10% of the alloy microstructure.
Claim 3
Dependent Claim
20 words
The method of claim 1, including machining the sintered product of step (2) prior to said infiltration of step (3).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |