Process for the polymerization of cyclic diorganopolysiloxanes with cation-complex catalysts
Assignee: General Electric Co
•
Filing: 1977-06-22
•
Granted: 1978-10-24
•
Expires: 1997-06-22
Abstract
Abstract Diorganopolysiloxane homo- and copolymers having a viscosity from 50 to 200,000,000 centipoise at 25° C, are produced by (a) reacting a composition of (i) a first cyclic siloxane having 3 to 6 units alone or admixed with (ii) a second cyclic siloxane having 3 to 6 units, (i) being present in an amount of 30 to 100 mol % of the composition, at a temperature in the range of 90° to 150° C and in the presence of 5 to 500 parts per million, as alkali metal hydroxide of a catalyst comprising alkali metal hydroxide or a silanolate of an alkali metal hydroxide complexed with a low molecular weight polymer of ethylene oxide (polyethylene glycol) soluble in the cyclic siloxanes. Especially useful products of the process are homopolymers and copolymers including siloxane chain units of the formula R R 1 SiO wherein R 1 is alkyl, halogenated alkyl or cycloalkyl, and preferably, perfluoroalkyl, and R is the same as R 1 and, in addition, vinyl or phenyl.
Inventors
- 👤 Edwin Robert Evans
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:04
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/06; C08G77/08; C08G65/00; C08G65/02; C08G65/32; C08G65/329; C08G65/336
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
226 words
A process for producing a diorganopolysiloxane having a viscosity of from 50 to 200,000,000 centipoise at 25° C., comprising (A) reacting a compositon comprising (i) a cyclic polysiloxane of the formula, (R R.sup.1 SiO).sub.x or a mixed such plysiloxane wherein R is selected from the class consisting of methyl, ethyl, vinyl or phenyl and R 1 is selected from the class consisting of alkyl radicals of 3 to 8 carbon atoms, halogenated alkyl radicals of 3 to 8 carbon atoms and cycloalkyl radicals of 3 to 8 carbon atoms and x is from 3 to 6, and (ii) a cyclic polysiloxane of the formula, R.sub.2.sup.2 SiO).sub.y wherein R 2 is, independently, selected from the class consisting of methyl, ethyl, vinyl or phenyl and y is from 3 to 6 or a mixed such polysiloxane, (i) being present in an amount of from 30 to 100 mol % of the composition, at a temperature in the range of 20° C. to 160° C. in the presence of 5 to 500 parts per million, as alkali metal hydroxide, of a catalyst comprising (a) alkali metal hydroxide complexed with a low molecular weight polymer of ethylene oxide, or (b) a silanolate of alkali metal hydroxide complexed with a low molecular weight polymer of ethylene oxide, and (B) neutralizing the catalyst in the reaction mixture after equilibrium has been reached.
Claim 2
Dependent Claim
226 words
A process for producing a diorganopolysiloxane having a viscosity of from 50 to 200,000,000 centipoise at 25° C., comprising (A) reacting a compositon comprising (i) a cyclic polysiloxane of the formula, (R R.sup.1 SiO).sub.x or a mixed such plysiloxane wherein R is selected from the class consisting of methyl, ethyl, vinyl or phenyl and R 1 is selected from the class consisting of alkyl radicals of 3 to 8 carbon atoms, halogenated alkyl radicals of 3 to 8 carbon atoms and cycloalkyl radicals of 3 to 8 carbon atoms and x is from 3 to 6, and (ii) a cyclic polysiloxane of the formula, R.sub.2.sup.2 SiO).sub.y wherein R 2 is, independently, selected from the class consisting of methyl, ethyl, vinyl or phenyl and y is from 3 to 6 or a mixed such polysiloxane, (i) being present in an amount of from 30 to 100 mol % of the composition, at a temperature in the range of 20° C. to 160° C. in the presence of 5 to 500 parts per million, as alkali metal hydroxide, of a catalyst comprising (a) alkali metal hydroxide complexed with a low molecular weight polymer of ethylene oxide, or (b) a silanolate of alkali metal hydroxide complexed with a low molecular weight polymer of ethylene oxide, and (B) neutralizing the catalyst in the reaction mixture after equilibrium has been reached.
Claim 3
Dependent Claim
43 words
A process as defined in claim 1, wherein the low molecular weight polymer of ethylene oxide is of the general formula, HO--(CH.sub.2 --CH.sub.2 O).sub.x --CH.sub.2 --CH.sub.2 --O--R wherein R is hydrogen or methyl and x is an integer of from 8 to 30.
Claim 4
Dependent Claim
44 words
A process as defined in claim 1 wherein the silanolate includes units of the formula R 2 4 SiO wherein the R 4 groups, independently, are alkyl of from 1 to 8 carbon atoms, cycloalkyl of from 4 to 8 carbon atoms or phenyl.
Claim 5
Dependent Claim
12 words
A process as defined in claim 3 wherein R 4 is methyl.
Claim 6
Dependent Claim
51 words
A process as defined in claim 1, wherein the catalyst is neutralized with phosphoric acid, a compound of the formula, R b 6 SiX 4-b , where R 6 is alkyl, cycloalkyl, vinyl or phenyl, X is bromine or chlorine, and b is from 0 to 3, or a hydrolyzed tris(haloalkyl)phosphite.
Claim 7
Dependent Claim
18 words
A process as defined in claim 1, wherein the alkali metal hydroxide is sodium hydroxide or potassium hydroxide.
Claim 8
Dependent Claim
23 words
A process as defined in claim 1, wherein the cyclic polysiloxanes are reacted with the catalyst for from 1/2 hour to 20 hours.
Claim 9
Dependent Claim
42 words
A process as defined in claim 1, wherein the cyclic polysiloxanes and mixtures thereof contain less than 20 parts per million of trifunctional siloxanes, less than 200 parts per million of monofunctional siloxanes, and less than 10 parts per million of water.
Claim 10
Dependent Claim
28 words
A process as defined in claim 1, wherein R 1 is R 7 CH 2 CH 2 --and R 7 is perfluoroalkyl of 1 to 6 carbon atoms.
Claim 11
Dependent Claim
33 words
A process as defined in claim 1, wherein R 1 is CF 3 CH 2 CH 2 --; R and R 2 are each methyl; and x and y are 3 or 4.
Claim 12
Dependent Claim
17 words
A process as defined in claim 10, wherein x is 4 and y is 3 or 4.
Claim 13
Dependent Claim
17 words
A process as defined in claim 1, wherein component (i) comprises 100 mol % of the composition.
Claim 14
Dependent Claim
26 words
A process as defined in claim 1, wherein cyclic polysiloxane (i) is present in an amount of from 30 to 96 mol % of the composition.
Claim 15
Dependent Claim
26 words
A process as defined in claim 1, wherein cyclic polysiloxane (i) is present in an amount of from 30 to 85 mol % of the composition.
Claim 16
Dependent Claim
25 words
A process as defined in claim 1, wherein step (A) is carried out at a temperature in the range of 90° C. to 150° C.
References Cited (Backward Citations)
US4003917A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |