Abstract
Abstract A magnetic coating composition in which magnetic iron oxide particles are dispersed into a solution of three components, which upon evaporation of the solvent and curing with elevated temperatures, results in a very smooth durable polymer coating having the magnetic particles dispersed uniformly therein. The three components in solution are an epoxy resin having an epoxide equivalent weight of approximately 400 or above, a polyamine whch has a minimum of one primary amine group and a cellulose acetate butyrate resin which has approximately 17 weight % butyral content or above. The polyamine, which acts as a catalyst to crosslink the composition, can be substituted for by hydroxyl compounds, a preferred one being formic acid (HCOOH) - an organic acid.
Inventors
- 👤 Virgil Allan Lohoff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:50
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/702; G11B5/7023; C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K5/00; C08K5/16; C08K5/17; C08L; C08L1/00; C08L1/08; C08L1/10; C08L1/14; C08L63/00; C09; C09D; C09D163/00; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31786; Y10T428/3179
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
177 words
A heat hardenable liquid magnetic film forming composition comprising: an epoxy resin having an epoxide equivalent weight lying in the range from about 185 to about 6,000 a cellulose acetate butyrate resin having a butyral content of at least 17%, an amine catalyst having at least one primary amine group, the amount of cellulose acetate butyrate lying in the range from about 5 to about 30 weight percent of the combined weights of said epoxy resin, said cellulose acetate butyrate resin and said amine, the ratio of epoxy equivalents to amine equivalents lying in the range from about 1/4 to about 4/1, a solvent blend providing a viscosity for said composition lying in the range from about 150 to about 600 centipoise at 24° Centrigrade, and magnetizable particles dispersed within said composition, said composition having the above ingredients in the following proportionate ranges: ______________________________________
Ingredient Parts By Weight
Weight % Solids
______________________________________
Magnetizable particles
50-60 50-60
Epoxy resin plus solvent
40-65 30-40
Cellulose acetate butyrate
30-190 3-6
plus solvent
Amine catalyst 2-5 2-5
Remaining solvent
135-190
______________________________________
Claim 2
Dependent Claim
177 words
A heat hardenable liquid magnetic film forming composition comprising: an epoxy resin having an epoxide equivalent weight lying in the range from about 185 to about 6,000 a cellulose acetate butyrate resin having a butyral content of at least 17%, an amine catalyst having at least one primary amine group, the amount of cellulose acetate butyrate lying in the range from about 5 to about 30 weight percent of the combined weights of said epoxy resin, said cellulose acetate butyrate resin and said amine, the ratio of epoxy equivalents to amine equivalents lying in the range from about 1/4 to about 4/1, a solvent blend providing a viscosity for said composition lying in the range from about 150 to about 600 centipoise at 24° Centrigrade, and magnetizable particles dispersed within said composition, said composition having the above ingredients in the following proportionate ranges: ______________________________________
Ingredient Parts By Weight
Weight % Solids
______________________________________
Magnetizable particles
50-60 50-60
Epoxy resin plus solvent
40-65 30-40
Cellulose acetate butyrate
30-190 3-6
plus solvent
Amine catalyst 2-5 2-5
Remaining solvent
135-190
______________________________________
Claim 3
Dependent Claim
10 words
The composition of claim 1 wherein said amine comprises N-aminoethylpiperazine.
Claim 4
Dependent Claim
11 words
The composition of claim 1 wherein said magnetizable particles are ferromagnetic.
Claim 5
Dependent Claim
12 words
The composition of claim 3 wherein said particles comprise magnetic iron oxide.
Claim 6
Dependent Claim
33 words
The combination of claim 4 wherein said particles have a coercive force lying in the range from about 250 to about 1000 oersteds and a specific magnetic moment of at least 78 emu/gm.
Claim 7
Dependent Claim
76 words
A magnetic memory element comprising a substrate having an upper surface and a heat hardened layer adhered to said upper surface and formed from the composition of claim 1, said layer comprising a polymer resulting from the cross-linking of said epoxy resin having an equivalent weight of from about 185 to about 6,000 said cellulose acetate butyrate resin having a butyral content of at least 17 weight percent and said catalyst, and magnetizable particles dispersed therein.
Claim 8
Dependent Claim
39 words
The combination of claim 6 wherein said substrate further includes a lower surface, and further including a heat hardened layer adhered to said lower surface which is substantially identical to said heat hardened layer adhered to said upper surface.
Claim 9
Dependent Claim
11 words
The combination of claim 6 wherein said substrate is substantially rigid.
Claim 10
Dependent Claim
14 words
The combination of claim 6 wherein said substrate is fabricated from a flexible material.
Claim 11
Dependent Claim
10 words
The combination of claim 6 wherein said polyamine is N-aminoethylpiperazine.
Claim 12
Independent Claim
154 words
A method of making a heat hardenable liquid film-forming composition with particles dispersed therein, said method comprising the steps of: (a) providing an epoxy resin having epoxy equivalent weights in the range from about 185 to about 6,000, a cellulose acetate butyrate resin having a butyral content of at least 17 percent, an amine catalyst with at least one primary amine group, magnetizable particulate material and a solvent blend; the amount of said cellulose acetate butyrate lying in the range from about 5 to about 30 weight percent of the combined weights of said epoxy resin, said cellulose acetate butyrate and said amine; and (b) mixing the ingredients of step (a) together in the following proportions to form said composition: ______________________________________
Ingredient Parts By Weight
Weight % Solids
______________________________________
Magnetizable particles
50-60 50-60
Epoxy resin plus solvent
40-65 30-40
Cellulose acetate butyrate
30-190 3-6
plus solvent
Amine catalyst 2-5 2-5
Remaining solvent
135-190
______________________________________
Claim 13
Independent Claim
154 words
A method of making a heat hardenable liquid film-forming composition with particles dispersed therein, said method comprising the steps of: (a) providing an epoxy resin having epoxy equivalent weights in the range from about 185 to about 6,000, a cellulose acetate butyrate resin having a butyral content of at least 17 percent, an amine catalyst with at least one primary amine group, magnetizable particulate material and a solvent blend; the amount of said cellulose acetate butyrate lying in the range from about 5 to about 30 weight percent of the combined weights of said epoxy resin, said cellulose acetate butyrate and said amine; and (b) mixing the ingredients of step (a) together in the following proportions to form said composition: ______________________________________
Ingredient Parts By Weight
Weight % Solids
______________________________________
Magnetizable particles
50-60 50-60
Epoxy resin plus solvent
40-65 30-40
Cellulose acetate butyrate
30-190 3-6
plus solvent
Amine catalyst 2-5 2-5
Remaining solvent
135-190
______________________________________
Claim 14
Dependent Claim
27 words
The method of claim 11 wherein said magnetizable particulate material comprises individual particles having a size in the range from about 0.10 micron to about 1.0 micron.
Claim 15
Dependent Claim
23 words
The method of claim 12 wherein said particles have a length to width ratio in the range from about 4/1 to about 15/1.
Claim 16
Dependent Claim
19 words
The method of claim 11 wherein said epoxy resin has between one and three epoxy groups per polymer unit.
Claim 17
Dependent Claim
11 words
The method of claim 11 wherein said amine catalyst comprises N-aminoethylpiperazine.
Claim 18
Dependent Claim
21 words
The method of claim 11 wherein said step of mixing includes the step of treating said ingredients to substantially eliminate agglomerates.
Claim 19
Dependent Claim
17 words
The method of claim 16 wherein said step of treating includes the step of milling said ingredients.
Claim 20
Dependent Claim
54 words
The method of claim 11 further including the steps of: (c) providing a substrate material with a substantially flat surface; (d) coating said surface with said composition; and (e) curing the composition coating on said surface to provide a polymer film resulting from the cross-linking of said epoxy resin and said cellulose acetate butyrate.
Claim 21
Dependent Claim
35 words
The method of claim 18 wherein said step of curing includes the step of heating the composition coated on said surface to a temperature of at least about 210° Centigrade for a predetermined time period.
Claim 22
Dependent Claim
14 words
The method of claim 19 wherein said predetermined time period is substantially 3 hours.
Claim 23
Dependent Claim
33 words
The method of claim 18 wherein said substrate material comprises a disc, and further including the step of orienting said particles circumferentially of said disc while said composition is in the liquid state.
References Cited (Backward Citations)
US2732367A
Cited
US2710845A
Cited
US3009847A
Cited
US3474073A
Cited
US3808079A
Cited
US4074012A
Cited
US4070522A
Cited
US4075384A
Cited
US4049566A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |