Method of preparing blown thermoplastic articles having multiaxial orientation
Assignee: Dow Chemical Co
•
Filing: 1975-01-06
•
Granted: 1978-10-24
•
Expires: 1995-01-06
Abstract
Abstract A method for manufacturing blown articles is disclosed wherein the article is manufactured from a parison having a high degree of multi-axial orientation. The method permits molecular orientation within the parison to be superposed with orientation imparted during the blowing step, whereby a blown article of greatly improved properties is manufactured.
Inventors
- 👤 Kenneth J. Cleereman
- 👤 Walter J. Schrenk
- 👤 Grant W. Cheney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 08:47
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/42; B29C49/64; B29C49/6409; B29C49/071; B29C67/00; B29C67/0003; B29C2949/00; B29C2949/07; B29C2949/0715; B29C2949/072; B29C2949/073; B29C2949/0733; B29C2949/076; B29C2949/0768; B29C2949/0769; B29C2949/077; B29C2949/0771; B29C2949/078; B29C2949/081; B29C2949/082; B29C2949/0829; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/26; B29C2949/28; B29C2949/30; B29C2949/3024; B29C2949/3032; B29C2949/3064; B29C49/02; B29C49/06; B29K; B29K2025/00; B29K2027/00; B29K2027/06; B29K2995/00; B29K2995/0037; B29K2995/005; B29K2995/0054
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
224 words
A method for preparing a blown thermoplastic article of significantly improved properties comprising the steps of: (i) preparing from a molecular orientatable thermoplastic, a hollow parison preform, the molecules of which possess multiaxial orientation, the preform being prepared in an injection mold with a rotatable element and being characterized by exhibiting generally helicoidal shrinkage of strips cut from the side wall of the preform; (ii) removing the preform from the injection mold and thereafter applying heat to condition the preform for blow molding, such conditioning step being of sufficiently short duration and under a temperature condition which maintains the preform sufficiently cool to prevent substantial relaxation of the molecular orientation imparted to the preform in the injection molding step (i); (iii) simultaneously with said heat conditioning step (ii), restraining said preform from substantial shrinkage in the hoop and axial directions, said restraining step comprising supporting the preform on a mandrel generally intimately contacting the interior of the hollow preform; (iv) containing the preform in a hollow blow mold, the preform being supported on said mandrel; (v) and before the multiaxial orientation substantially relaxes out of the preform, expanding the oriented preform to the configuration of the blow mold, the process being characterized by the blown article prepared thereby possessing a significantly higher magnitude of molecular orientation than the molecular orientation possessed by the preform.
Claim 2
Independent Claim
224 words
A method for preparing a blown thermoplastic article of significantly improved properties comprising the steps of: (i) preparing from a molecular orientatable thermoplastic, a hollow parison preform, the molecules of which possess multiaxial orientation, the preform being prepared in an injection mold with a rotatable element and being characterized by exhibiting generally helicoidal shrinkage of strips cut from the side wall of the preform; (ii) removing the preform from the injection mold and thereafter applying heat to condition the preform for blow molding, such conditioning step being of sufficiently short duration and under a temperature condition which maintains the preform sufficiently cool to prevent substantial relaxation of the molecular orientation imparted to the preform in the injection molding step (i); (iii) simultaneously with said heat conditioning step (ii), restraining said preform from substantial shrinkage in the hoop and axial directions, said restraining step comprising supporting the preform on a mandrel generally intimately contacting the interior of the hollow preform; (iv) containing the preform in a hollow blow mold, the preform being supported on said mandrel; (v) and before the multiaxial orientation substantially relaxes out of the preform, expanding the oriented preform to the configuration of the blow mold, the process being characterized by the blown article prepared thereby possessing a significantly higher magnitude of molecular orientation than the molecular orientation possessed by the preform.
Claim 3
Dependent Claim
34 words
The method of claim 1 wherein step (i) comprises preparing the preform in an injection mold cavity wherein one of the elements defining the cavity is rotated after the cavity is filled with thermoplastic.
Claim 4
Dependent Claim
15 words
The method of claim 2 wherein said heat conditioning step comprises heating the blowing mandrel.
Claim 5
Dependent Claim
20 words
The method of claim 2 wherein said heat conditioning step comprises applying heat to said parison preform by radiant heating.
Claim 6
Dependent Claim
27 words
The method of claim 2 wherein said heat conditioning step comprises heating the blowing mandrel and simultaneously applying heat to the opposite surface of the parison preform.
Claim 7
Dependent Claim
17 words
The method of claim 2 wherein said heat conditioning step comprises reheating a substantially cold parison preform.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |