US4121924A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Alloy for rare earth treatment of molten metals and method
Assignee: Huntington Alloys Corp
•
Filing: 1976-09-16
•
Granted: 1978-10-24
•
Expires: 1996-09-16
Abstract
Abstract Alloy containing special ternary proportions of nickel, iron and rare earths of group cerium, lanthanum, neodymium and praseodymium has density, melting temperature, toughness, stability and other characteristics specially beneficial for production and use as addition agent in rare earth treatment of molten iron-group metals, particularly including steels and nickel-base alloys.
Inventors
- 👤 II John Joseph de Barbadillo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:26
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/007
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
167 words
An alloy consisting essentially of nickel, iron and rare earth metal from the group consisting of cerium, lanthanum, neodymium, praseodymium and mixtures thereof in amounts totaling at least 90% of the alloy and in proportions correlated to each other in a ternary percentage on area ABCDA in the triaxial ternary percentage diagram of the accompanying drawing, up to 2% carbon, up to 5% manganese and up to 5% silicon, and further characterized by the following combination of characteristics: (i) good castability in air, (ii) a density of about 7.3 or greater to promote sinking, (iii) good dispersibility promoted by a melting temperature of 2500° F. or lower, (iv) good durability by reason of the ability to resist shock, both thermal and mechanical, (v) good compatability with steel, and (vi) a peritectic microstructure having (a) a dendritic lattice of an iron-rich nickel-iron solid solution phase comprising at least 10 volume-percent of the as-cast structure together with (b) at least one nickel-rich phase containing iron and rare earth metals.
Claim 2
Dependent Claim
167 words
An alloy consisting essentially of nickel, iron and rare earth metal from the group consisting of cerium, lanthanum, neodymium, praseodymium and mixtures thereof in amounts totaling at least 90% of the alloy and in proportions correlated to each other in a ternary percentage on area ABCDA in the triaxial ternary percentage diagram of the accompanying drawing, up to 2% carbon, up to 5% manganese and up to 5% silicon, and further characterized by the following combination of characteristics: (i) good castability in air, (ii) a density of about 7.3 or greater to promote sinking, (iii) good dispersibility promoted by a melting temperature of 2500° F. or lower, (iv) good durability by reason of the ability to resist shock, both thermal and mechanical, (v) good compatability with steel, and (vi) a peritectic microstructure having (a) a dendritic lattice of an iron-rich nickel-iron solid solution phase comprising at least 10 volume-percent of the as-cast structure together with (b) at least one nickel-rich phase containing iron and rare earth metals.
Claim 3
Dependent Claim
24 words
An alloy as set forth in claim 1 wherein the total of nickel and rare earth metal is at least 65% of the alloy.
Claim 4
Dependent Claim
23 words
An alloy as set forth in claim 1 containing 15% to 25% iron, 35% to 45% rare earth metal and balance essentially nickel.
Claim 5
Dependent Claim
13 words
An alloy as set forth in claim 1 containing 1% to 4% magnesium.
Claim 6
Dependent Claim
27 words
An alloy as set forth in claim 1 containing 15% to 25% iron, 20% to 30% rare earth metal, 2% to 3% magnesium and balance essentially nickel.
Claim 7
Dependent Claim
104 words
A process for rare-earth metal treatment of a high melting temperature iron-group metal containing a major proportion of metal from the iron-group consisting of iron, nickel, cobalt and mixtures thereof and characterized by melting temperatures of about 2000° F. or higher comprising establishing a molten bath of the iron-group metal at a treatment temperature of about 2100° F. or higher and introducing into the bath while at a temperature of at least 2100° F. a previously solidified, rare earth-containing alloy as set forth in claim 1 and maintaining the bath temperature sufficiently to result in dispersion of the rare earth metal throughout the bath.
Claim 8
Dependent Claim
30 words
A process as set forth in claim 6 wherein the bath temperature is not greater than about 3100° F. at the time the rare-earth alloy is introduced into the bath.
Claim 9
Dependent Claim
17 words
A process as set forth in claim 6 wherein the rare-earth alloy contains 1% to 4% magnesium.
Claim 10
Dependent Claim
16 words
A process as set forth in claim 6 wherein the bath metal is an iron-base alloy.
Claim 11
Dependent Claim
16 words
A process as set forth in claim 6 wherein the bath metal is a nickel-base alloy.
Claim 12
Dependent Claim
13 words
An alloy as set forth in claim 1 containing 0.1% to 0.25% carbon.
Claim 13
Dependent Claim
13 words
An alloy as set forth in claim 1 containing 0.1% to 0.5% manganese.
Claim 14
Dependent Claim
13 words
An alloy as set forth in claim 1 containing 0.1% to 0.5% silicon.
Claim 15
Dependent Claim
22 words
An alloy as set forth in claim 1 containing 0.1% to 0.25% carbon, 0.1% to 0.5% manganese and 0.1% to 0.5% silicon.
References Cited (Backward Citations)
GB190316853A
Cited
GB190916210A
Cited
US2841488A
Cited
US2850381A
Cited
US2829973A
Cited
US2771359A
Cited
US2810640A
Cited
US3189445A
Cited
DE1181430B
Cited
US3801311A
Cited
US3980468A
Cited
US3894867A
Cited
US3949351A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |