Assignee: Wyeth Holdings LLC
•
Filing: 1977-10-17
•
Granted: 1978-10-17
•
Expires: 1997-10-17
Abstract
Abstract Disclosed is a method for forming shaped catalysts from a rehydratable alumina composition. The method includes a staged rehydration procedure to stabilize the rehydratable alumina to facilitate extrusion processing.
Inventors
- 👤 Donald P. Spitzer
- 👤 William Edward Bambrick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:01
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/0009; B01J21/00; B01J21/02; B01J21/04; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J37/06; C; C10; C10G; C10G45/00; C10G45/02; C10G45/04; C10G45/44; C10G45/46
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
115 words
A method of preparing formed alumina extrudates from a partially dehydrated, rehydratable alumina prepared by flash calcining Bayer process alumina, and having LOI in the range from 3 to 15 and rehydration index in the range from 15 to 80, said method comprising: rehydrating said partially dehydrated alumina by mixing with water which contains acid at pH below 7 and heating the mixture to 80°-100° C. for the time needed for rehydration; solidifying the rehydrated alumina; mulling the solidified, rehydrated alumina with sufficient water to make a mulled mixture suitable for extrusion; extruding the mulled mixture into a desired extrudate shape; and drying said extrudate shapes and calcining the dried extrudate to activate the alumina.
Claim 2
Independent Claim
115 words
A method of preparing formed alumina extrudates from a partially dehydrated, rehydratable alumina prepared by flash calcining Bayer process alumina, and having LOI in the range from 3 to 15 and rehydration index in the range from 15 to 80, said method comprising: rehydrating said partially dehydrated alumina by mixing with water which contains acid at pH below 7 and heating the mixture to 80°-100° C. for the time needed for rehydration; solidifying the rehydrated alumina; mulling the solidified, rehydrated alumina with sufficient water to make a mulled mixture suitable for extrusion; extruding the mulled mixture into a desired extrudate shape; and drying said extrudate shapes and calcining the dried extrudate to activate the alumina.
Claim 3
Dependent Claim
16 words
The method of claim 1 including a washing step to remove soda impurities from the alumina.
Claim 4
Dependent Claim
67 words
The method of claim 2 wherein said rehydrating comprises: mixing the rehydratable alumina composition with water to form an aqueous slurry; adding acid to said slurry to main a pH level below 7; filtering said aqueous slurry of alumina to form a high solids filter cake; washing said filter cake with water to remove soda impurities; and heating the washed filter cake to rehydrate said rehydratable alumina.
Claim 5
Dependent Claim
20 words
The method of claim 2 including a curing step to harden the extrudate shape before the drying and calcining step.
Claim 6
Dependent Claim
17 words
The method of claim 4 wherein said curing step comprises steam treatment of the defined extrudate shape.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein said pH level below 7 is maintained by the introduction of CO 2 .
Claim 8
Dependent Claim
39 words
The method of claim 1 wherein pH of the water in the defined rehydrating step is maintained below pH7 by addition of an acid selected from the group consisting of nitric acid, sulfuric acid, phosphoric acid and carbonic acid.
Claim 9
Dependent Claim
19 words
The method of claim 7 wherein said pH level below 7 is maintained by the addition of nitric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-16 | 1982-04-17 | 1982-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-16 | 1986-04-17 | 1986-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-16 | 1990-04-17 | 1990-10-17 | $7700.00 | Window Closed / Lapsed |