US4120729A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Novel low temperature maturing dental glaze
Assignee: Johnson and Johnson
•
Filing: 1977-10-27
•
Granted: 1978-10-17
•
Expires: 1997-10-27
Abstract
Abstract The instant invention relates to a novel dental glaze which matures at a temperature of from 1400 DEG to 1600 DEG F, that is, at least 200 DEG lower than the vitrifying temperature of dental porcelain. The chemical composition of this novel glaze may be thusly represented, on a weight basis: }SiO2 45-52% }B2O3 15-20% }Al2O3 10-15% }K2O 3.5-7.5% }Na2O 12-17% }CaO 0-1% }ZnO 0-1% }F 1-3% } Preferably the instant novel glaze is further characterized as having an average particle size of 10 +/- 4 microns and not more than 1% of the particles having a diameter greater than 30 microns.
Inventors
- 👤 Milagros B. Smyth
- 👤 James Lee-You
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:08
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/02; C03C8/06; A; A61; A61K; A61K6/00; A61K6/15; A61K6/16; A61K6/17; A61K6/70; A61K6/78; A61K6/80; A61K6/802; A61K6/807
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
131 words
A translucent dental glaze composition suitable for application to a dental porcelain coated metal substrate, said glaze having (a) an average particle size of 10 ± 4 microns and not more than 1% of the particles having a diameter greater than 30 microns, (b) a maturing temperature of from 1400° to 1600° F. and at least about 200° F. lower than the vitrifying temperature of the dental porcelain of the substrate, and (c) a coefficient of thermal expansion of from 9 to 12 × 10 -6 /° C. which is lower than the coefficient of thermal expansion of the dental porcelain, and consisting essentially of, on a weight basis: ______________________________________
SiO.sub.2 45-52%
B.sub.2 O.sub.3
15-20%
Al.sub.2 O.sub.3
10-15%
K.sub.2 O 3.5-7.5%
Na.sub.2 O 12-17%
CaO 0-1%
ZnO 0-1%
F 1-3%
______________________________________
Claim 2
Dependent Claim
131 words
A translucent dental glaze composition suitable for application to a dental porcelain coated metal substrate, said glaze having (a) an average particle size of 10 ± 4 microns and not more than 1% of the particles having a diameter greater than 30 microns, (b) a maturing temperature of from 1400° to 1600° F. and at least about 200° F. lower than the vitrifying temperature of the dental porcelain of the substrate, and (c) a coefficient of thermal expansion of from 9 to 12 × 10 -6 /° C. which is lower than the coefficient of thermal expansion of the dental porcelain, and consisting essentially of, on a weight basis: ______________________________________
SiO.sub.2 45-52%
B.sub.2 O.sub.3
15-20%
Al.sub.2 O.sub.3
10-15%
K.sub.2 O 3.5-7.5%
Na.sub.2 O 12-17%
CaO 0-1%
ZnO 0-1%
F 1-3%
______________________________________
Claim 3
Dependent Claim
50 words
The glaze of claim 1 consisting essentially of, on a weight basis: ______________________________________
SiO.sub.2 48.5 - 50.6
B.sub.2 O.sub.3
16.9 - 17.9
Al.sub.2 O.sub.3
10.0 - 12.0
K.sub.2 O 4.8 - 5.1
Na.sub.2 O 13.2 - 13.6
CaO 0.8 - 1.0
ZnO 0.8 - 1.0
F 0.7 - 1.2
______________________________________
Claim 4
Dependent Claim
18 words
The glaze of claim 2 having a coefficient of thermal expansion of about 9.1 × 10 -6 .
Claim 5
Dependent Claim
83 words
In a method for glazing an artificial tooth comprising a dental porcelain coated metal substrate which has been previously fired and ground comprising the steps of coating said tooth with a dispersion of a glaze in a liquid vehicle, drying said tooth to remove said liquid, and firing said dried tooth, the improvement whereby the tooth is fired to a glossy, slightly textured finish at a temperature of from 1400° to 1600° F. and the glaze is a composition according to claim 1.
References Cited (Backward Citations)
GB1072689A
Cited
US3640738A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-16 | 1982-04-17 | 1982-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-16 | 1986-04-17 | 1986-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-16 | 1990-04-17 | 1990-10-17 | $7700.00 | Window Closed / Lapsed |