Treating wells to mitigate flow-after-cementing
Assignee: Mobil Oil AS
•
Filing: 1977-05-16
•
Granted: 1978-10-17
•
Expires: 1997-05-16
Abstract
Abstract This specification discloses a method of treating a well drilled into the earth. In carrying out this method there is formed a lightweight thixotropic cement slurry that is comprised of a low density calcined shale cement, attapulgite and water, in ratios to provide a pumpable slurry that has zero water separation. This lightweight thixotropic cement slurry having zero water separation is placed in a well and allowed to set.
Inventors
- 👤 Joseph U. Messenger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:09
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/42; C09K8/46; C04; C04B; C04B14/00; C04B14/02; C04B14/04; C04B14/10; C04B14/102; C04B28/00; C04B28/02; C04B7/00; C04B7/24; C04B7/30; Y; Y02; Y02P; Y02P40/00; Y02P40/10
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
83 words
A method of cementing a well that penetrates the earth, comprising the steps of: blending a low-density calcined shale cement with attapulgite in an amount no greater than about 2 weight percent based on cement and water in an amount to form a thixotropic cement slurry having a density within the range of 11.5 lb/gal to 13.5 lb/gal and having essentially zero water separation; injecting said slurry down said well; and maintaining said slurry in said well to allow said slurry to set.
Claim 2
Independent Claim
83 words
A method of cementing a well that penetrates the earth, comprising the steps of: blending a low-density calcined shale cement with attapulgite in an amount no greater than about 2 weight percent based on cement and water in an amount to form a thixotropic cement slurry having a density within the range of 11.5 lb/gal to 13.5 lb/gal and having essentially zero water separation; injecting said slurry down said well; and maintaining said slurry in said well to allow said slurry to set.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein said water is sea water.
Claim 4
Dependent Claim
51 words
The method of claim 1 further comprising including in said cement slurry an accelerator selected from the salts consisting of sodium chloride in an amount no greater than about 10 weight percent based on water and calcium chloride in an amount no greater than about 3 weight percent based on cement.
Claim 5
Independent Claim
95 words
A method of cementing pipe in a well penetrating an active gas zone to prevent flow-after-cementing, comprising: blending a low-density calcined shale cement with attapulgite in an amount no greater than about 2 weight percent based on cement and sea water in an amount to form a thixotropic cement slurry having a density within the range of 12.5 lb/gal to 13.5 lb/gal and having essentially zero water separation; injecting said slurry down said well and into the annulus formed about said pipe; and maintaining said slurry in said annulus to allow said slurry to set.
Claim 6
Independent Claim
95 words
A method of cementing pipe in a well penetrating an active gas zone to prevent flow-after-cementing, comprising: blending a low-density calcined shale cement with attapulgite in an amount no greater than about 2 weight percent based on cement and sea water in an amount to form a thixotropic cement slurry having a density within the range of 12.5 lb/gal to 13.5 lb/gal and having essentially zero water separation; injecting said slurry down said well and into the annulus formed about said pipe; and maintaining said slurry in said annulus to allow said slurry to set.
Claim 7
Dependent Claim
33 words
The method of claim 4 wherein said low-density calcined shale cement is blended with 0.5 weight percent attapulgite based on cement and about 8.9 gallons of sea water per 75 pounds of cement.
Claim 8
Dependent Claim
52 words
The method of claim 5 further comprising including in said cement slurry an accelerator selected from the salts consisting of sodium chloride in an amount no greater than about 7 weight percent based on sea water and calcium chloride in an amount no greater than about 3 weight percent based on cement.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-16 | 1982-04-17 | 1982-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-16 | 1986-04-17 | 1986-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-16 | 1990-04-17 | 1990-10-17 | $7700.00 | Window Closed / Lapsed |