Olefin polymerization catalyst
Assignee: Millennium Petrochemicals Inc
•
Filing: 1977-06-22
•
Granted: 1978-10-10
•
Expires: 1997-06-22
Abstract
Abstract An olefin polymerization catalyst is prepared by depositing the chromium (III) compound obtained from the reaction of a chromium (III) carboxylate with an aluminum alkoxide upon an inorganic support material and calcining the impregnated support material in a non-reducing atmosphere above 300 DEG C, up to the decomposition temperature of the support material to provide an activated catalyst.
Inventors
- 👤 Anthony N. Speca
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:00
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
67 words
A process for the preparation of an olefin polymerization catalyst which comprises: (a) depositing on an inorganic support material, the chromium (III) compound preformed obtained from the reaction of a chromium (III) carboxylate with an aluminum alkoxide; and (b) heating said support material having the chromium (III) reaction product deposited thereon in a non-reducing atmosphere above 300° C. up to the decomposition temperature of the support material.
Claim 2
Dependent Claim
67 words
A process for the preparation of an olefin polymerization catalyst which comprises: (a) depositing on an inorganic support material, the chromium (III) compound preformed obtained from the reaction of a chromium (III) carboxylate with an aluminum alkoxide; and (b) heating said support material having the chromium (III) reaction product deposited thereon in a non-reducing atmosphere above 300° C. up to the decomposition temperature of the support material.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein an aluminum alkoxide is deposited upon the support material after the deposition of the chromium (III) reaction product but prior to the heating step.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein the chromium (III) carboxylate reacted with aluminum alkoxide is chromium (III) acetate.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein the chromium (III) compound is reacted with aluminum sec-butoxide.
Claim 6
Dependent Claim
23 words
The process of claim 1 wherein the chromium (III) reaction product is obtained from the reaction of chromium (III) acetate with aluminum sec-butoxide.
Claim 7
Dependent Claim
12 words
The process of claim 2 wherein the aluminum alkoxide is aluminum sec-butoxide.
Claim 8
Dependent Claim
64 words
The process of claim 1 wherein the heat-treated polymerization catalyst is combined with a metallic or non-metallic reducing agent, the metallic reducing agent being selected from among the trialkyl aluminums, alkyl aluminum halides, alkyl aluminum alkoxides, dialkyl zinc, dialkyl magnesium, and the alkali metal and magnesium, beryllium and aluminum borohydrides, and the non-metallic reducing agent being selected from among the alkyl boranes and hydrides.
Claim 9
Dependent Claim
58 words
The process of claim 1 wherein the inorganic support material is a silica xerogel having a surface area in the range of 200 to 500 m 2 /g, a pore volume greater than about 2.0 cc/g and a major portion of the pore volume being provided by pores having diameters in the range of 300 to 600 A.
Claim 10
Dependent Claim
31 words
The process of claim 1 wherein the heating step is carried out in air at from about 800° C. to about 1,000° C. for from about 4 to about 6 hours.
Claim 11
Dependent Claim
39 words
A heat activated olefin polymerization catalyst comprising the preformed reaction product of a chromium (III) carboxylate and an aluminum alkoxide on an inorganic oxide support, the catalyst comprising 0.25 to 2.5 percent of Cr by weight of the support.
Claim 12
Dependent Claim
39 words
A heat activated olefin polymerization catalyst comprising the preformed reaction product of a chromium (III) carboxylate and an aluminum alkoxide on an inorganic oxide support, the catalyst comprising 0.25 to 2.5 percent of Cr by weight of the support.
Claim 13
Dependent Claim
25 words
The olefin polymerization catalyst of claim 10 wherein the chromium (III) reaction product is obtained from the reaction of chromium (III) acetate with aluminum sec-butoxide.
Claim 14
Dependent Claim
60 words
The olefin polymerization catalyst of claim 10 combined with a metallic or non-metallic reducing agent, the metallic reducing agent being selected from among the trialkyl aluminums, alkyl aluminum halides, alkyl aluminum alkoxides, dialkyl zinc, dialkyl magnesium, and the alkali metal and magnesium, beryllium and aluminum borohydrides, and the non-metallic reducing agent being selected from among the alkyl boranes and hydrides.
Claim 15
Dependent Claim
60 words
The olefin polymerization catalyst of claim 10 wherein the inorganic support material is a silica xerogel having a surface area in the range of 200 to 500 m 2 /g, a pore volume greater than about 2.0 cc/g and a major portion of the pore volume being provided by pores having diameters in the range of 300 to 600 A.
Claim 16
Dependent Claim
20 words
In the catalyzed polymerization of alpha olefins the improvement which comprises employing as said catalyst the catalyst of claim 13.
Claim 17
Dependent Claim
22 words
The process of claim 1 wherein the aluminum alkoxide is represented by the general formula (RO) 2 AlOR wherein R is alkyl.
References Cited (Backward Citations)
US3622521A
Cited
US3984351A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |