Anti-corrosion weldable coatings
Assignee: Occidental Chemical Corp
•
Filing: 1976-03-29
•
Granted: 1978-10-10
•
Expires: 1996-03-29
Abstract
Abstract A composition suitable for the protection of corrodible metal surfaces which comprises a binder and a filler. The filler is constituted of a mixture of a comminuted refractory ferro alloy and a non-metallic inhibitor such as zinc chromate or zinc yellow, the latter being present in an amount sufficient to enhance the corrosion protection and weldability of the coated metal surfaces. Various binders, both inorganic and organic, may be used and the filler is preferably a mixture of a major amount of ferrophos (Fe2P) and a minor amount, e.g., about 10 percent by weight of the filler, of zinc yellow.
Inventors
- 👤 Noel D. Blair
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:37
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/10; B; B23; B23K; B23K35/00; B23K35/22; B23K35/226; C09D5/082; C09D5/084; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12104; Y10T428/12111; Y10T428/12125; Y10T428/12132; Y10T428/25; Y10T428/256
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
73 words
A weldable article having a metal surface, coated with a composition which comprises about 3 to about 80 percent by weight of a binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a major amount of a comminuted refractory ferro alloy and a minor amount of a non-metallic corrosion inhibitor selected from the group consisting of chromates, nitrites, phosphates, molybdates, tungstates, silicates and benzoates.
Claim 2
Dependent Claim
73 words
A weldable article having a metal surface, coated with a composition which comprises about 3 to about 80 percent by weight of a binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a major amount of a comminuted refractory ferro alloy and a minor amount of a non-metallic corrosion inhibitor selected from the group consisting of chromates, nitrites, phosphates, molybdates, tungstates, silicates and benzoates.
Claim 3
Dependent Claim
27 words
The article of claim 1 wherein the comminuted refractory ferro alloy is selected from ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrovanadium, ferrozirconium, ferrotitanium, ferrotungsten, ferroboron, ferrophosphorus and iron carbide.
Claim 4
Dependent Claim
43 words
The article of claim 1 wherein the comminuted non-metallic corrosion inhibitor is selected from zinc chromate, zinc yellow, lead silicon-chromate, zinc molybdate, iron phosphate, potassium dichromate, sodium phosphate, calcium tungstate, aluminum silicate, zinc pyrophosphate, lithium dichromate, aluminum benzoate, stannous nitrite and mixtures thereof.
Claim 5
Dependent Claim
18 words
The article of claim 3 wherein the non-metallic corrosion inhibitor is selected from zinc chromate and zinc yellow.
Claim 6
Dependent Claim
24 words
The article of claim 4 wherein the non-metallic corrosion inhibitor has an average particle size within the range of about 2 to 10 microns.
Claim 7
Dependent Claim
24 words
The article of claim 1 wherein the filler includes zinc metal particles in an amount less than that which will substantially detrimentally affect weldability.
Claim 8
Dependent Claim
20 words
The article of claim 6 wherein the zinc metal particles comprise up to about 10 percent by weight of filler.
Claim 9
Dependent Claim
105 words
A weldable article having a metal surface coated with a composition which comprises about 3 to about 80 percent by weight of a binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a major amount of a comminuted refractory ferro alloy selected from ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrovanadium, ferrozirconium, ferrotitanium, ferrotungsten, ferroboron, ferrophosphorus and iron carbide and a minor amount of a non-metallic corrosion inhibitor selected from zinc chromate, zinc yellow, lead silicon-chromate, zinc molybdate, iron phosphate, potassium dichromate, sodium phosphate, calcium tungstate, aluminum silicate, zinc pyrophosphate, lithium dichromate, aluminum benzoate, stannous nitrite and mixtures thereof.
Claim 10
Dependent Claim
105 words
A weldable article having a metal surface coated with a composition which comprises about 3 to about 80 percent by weight of a binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a major amount of a comminuted refractory ferro alloy selected from ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrovanadium, ferrozirconium, ferrotitanium, ferrotungsten, ferroboron, ferrophosphorus and iron carbide and a minor amount of a non-metallic corrosion inhibitor selected from zinc chromate, zinc yellow, lead silicon-chromate, zinc molybdate, iron phosphate, potassium dichromate, sodium phosphate, calcium tungstate, aluminum silicate, zinc pyrophosphate, lithium dichromate, aluminum benzoate, stannous nitrite and mixtures thereof.
Claim 11
Dependent Claim
24 words
The article of claim 8 wherein the filler includes zinc metal particles in an amount less than that which will substantially detrimentally affect weldability.
Claim 12
Dependent Claim
21 words
The article of claim 9 wherein the zinc metal particles comprise up to about 10 percent by weight of the filler.
Claim 13
Dependent Claim
38 words
The article of claim 8 wherein the binder constitutes from about 3 to about 50 percent by weight and the filler is present in an amount within the range of about 40 to about 93 percent by weight.
Claim 14
Dependent Claim
28 words
The article of claim 8 wherein the comminuted refractory ferro alloy is present in the amount of from about 60 to 99 percent by weight of the filler.
Claim 15
Dependent Claim
31 words
The article of claim 8 wherein the non-metallic corrosion inhibitor is present in an amount within the range of from about 1 to about 40 percent by weight of the filler.
Claim 16
Dependent Claim
18 words
The article of claim 13 wherein the non-metallic corrosion inhibitor is selected from zinc chromate and zinc yellow.
Claim 17
Dependent Claim
24 words
The article of claim 14 wherein the non-metallic corrosion inhibitor has an average particle size within the range of about 2 to 10 microns.
Claim 18
Dependent Claim
13 words
The article of claim 8 wherein the refractory ferro alloy is ferro phosphorus.
Claim 19
Dependent Claim
22 words
The article of claim 16 wherein the ferrophosphorus has an average particle size within the range of about 1 to 10 microns.
Claim 20
Independent Claim
89 words
A method of forming a weldable corrosion protective coating on a metal substrate which comprises contacting the metal substrate with a composition which comprises about 3 to about 80 percent by weight of binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a comminuted refractory ferro alloy and a minor amount of a non-metallic corrosion inhibitor selected from the group consisting of chromates, nitrites, phosphates, molybdates, tungstates, silicates and benzoates, and forming a coating of said composition on the substrate.
Claim 21
Independent Claim
89 words
A method of forming a weldable corrosion protective coating on a metal substrate which comprises contacting the metal substrate with a composition which comprises about 3 to about 80 percent by weight of binder and about 20 to about 97 percent by weight of a filler, the filler being comprised of a comminuted refractory ferro alloy and a minor amount of a non-metallic corrosion inhibitor selected from the group consisting of chromates, nitrites, phosphates, molybdates, tungstates, silicates and benzoates, and forming a coating of said composition on the substrate.
Claim 22
Dependent Claim
63 words
The method of claim 18 wherein the refractory ferro alloy is selected from ferromanganese, ferromolybdenum, ferrosilicon, ferrochromium, ferrovanadium, ferrozirconium, ferrotitanium, ferrotungsten, ferroboron, ferrophosphorus and iron carbide and the non-metallic corrosion inhibitor is selected from zinc chromate, zinc yellow, lead siliconchromate, zinc molybdate, iron phosphate, potassium dichromate, sodium phosphate, calcium tungstate, aluminum silicate, zinc pyrophosphate, lithium dichromate, aluminum benzoate, stannous nitrite and mixtures thereof.
Claim 23
Dependent Claim
25 words
The method of claim 19 wherein the refractory ferro alloy is ferrophosphorus and the non-metallic corrosion inhibitor is selected from zinc chromate and ainc yellow.
Claim 24
Dependent Claim
42 words
The method of claim 20 wherein the comminuted refractory ferro alloy is present in an amount within the range of about 85 to 95 percent by weight of the filler and has an average particle size within the range of 1-10 microns.
Claim 25
Dependent Claim
20 words
The method of claim 19 wherein the refractory ferro alloy is ferrophosphorus and the non-metallic corrosion inhibitor is zinc chromate.
Claim 26
Dependent Claim
20 words
The method of claim 18 wherein the filler includes less than about 10 percent by weight of zinc metal particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |