Assignee: Vereinigte Aluminium Werke AG
•
Filing: 1977-03-07
•
Granted: 1978-10-10
•
Expires: 1997-03-07
Abstract
Abstract Disclosed herein are a process and apparatus for manufacturing vanadium pentoxide in powder form by the thermal decomposition of ammonium metavanadate containing more than 10% NH3 in a single operation.
Inventors
- 👤 Roland Thome
- 👤 Hubert Bings
- 👤 Hans Obermaier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:32
CPC Classifications
C; C01; C01G; C01G31/00; C01G31/02; C01P; C01P2006/00; C01P2006/80; Y; Y02; Y02P; Y02P20/00; Y02P20/10; Y02P20/129
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
178 words
A process for the manufacture of vanadium pentoxide in powder form which comprises: heating a predetermined quantity of ammonium metavanadate composition comprising more than 10% ammonia in a first zone to between about 300° and 500° C. until the water contained in said composition has been substantially removed to form an essentially dry material and water vapor, conducting said essentially dry composition from said first zone to a second zone, heating said essentially dry material in said second zone to between about 500° and 600° C. to form vanadium oxides and ammonia in the presence of said water vapor from said first zone, diluting said ammonia with said water vapor, conducting said vanadium oxides from said second zone to a third zone, heating said vanadium oxides in said third zone through which air is flowing in a countercurrent direction to between about 550° and 650° C. to form dry vanadium pentoxide powder, and continuously performing said process in a single enclosure wherein said first, second and third zones are adjacent to and in open communication with one another.
Claim 2
Dependent Claim
178 words
A process for the manufacture of vanadium pentoxide in powder form which comprises: heating a predetermined quantity of ammonium metavanadate composition comprising more than 10% ammonia in a first zone to between about 300° and 500° C. until the water contained in said composition has been substantially removed to form an essentially dry material and water vapor, conducting said essentially dry composition from said first zone to a second zone, heating said essentially dry material in said second zone to between about 500° and 600° C. to form vanadium oxides and ammonia in the presence of said water vapor from said first zone, diluting said ammonia with said water vapor, conducting said vanadium oxides from said second zone to a third zone, heating said vanadium oxides in said third zone through which air is flowing in a countercurrent direction to between about 550° and 650° C. to form dry vanadium pentoxide powder, and continuously performing said process in a single enclosure wherein said first, second and third zones are adjacent to and in open communication with one another.
Claim 3
Dependent Claim
11 words
The process of claim 1 which comprises cooling said vanadium pentoxide.
Claim 4
Dependent Claim
14 words
The process according to claim 1 wherein said enclosure is a tubular steel reactor.
Claim 5
Dependent Claim
18 words
The process of claim 3 which comprises rotating said reactor about its longitudinal axis during said heating operations.
Claim 6
Dependent Claim
31 words
The process of claim 4 which comprises admixing said ammonium metavanadate composition with air which is flowing countercurrent to the direction in which said composition is being conducted through said reactor.
Claim 7
Dependent Claim
26 words
The process according to claim 5 which comprises preheating the air admitted to said reactor to a temperature of between about 100° and about 600° C.
Claim 8
Dependent Claim
27 words
The process according to claim 4 which comprises withdrawing said admixed ammonia and water vapor from said reactor before said admixture can contact the countercurrent flowing air.
Claim 9
Dependent Claim
23 words
The process of claim 7 which comprises filling said reactor to between about 10 to about 30% by volume of said vanadate material.
Claim 10
Dependent Claim
24 words
The process of claim 8 which comprises withdrawing said ammonia and water vapor mixture from said reactor in the area of said second zone.
Claim 11
Dependent Claim
22 words
The process according to claim 6 wherein said ammonium metavanadate comprises up to 30% moisture at the entry of said first zone.
Claim 12
Dependent Claim
29 words
The process according to claim 10, which comprises admitting between about 0.2 and about 0.6 cubic meters of air per hour to said reactor per kilogram of ammonium metavanadate.
Claim 13
Dependent Claim
30 words
The process of claim 11 which comprises filling said reactor with said composition and said material to between about 10 and about 30% of the internal volume of said reactor.
Claim 14
Dependent Claim
25 words
The process of claim 12 which comprises maintaining the interior of the revolving reactor at a vacuum pressure between about 2 and about 20 mbar.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |