US4119582A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for manufacturing high-resilient flexible urethan foams
Assignee: NUC Corp
•
Filing: 1976-02-10
•
Granted: 1978-10-10
•
Expires: 1996-02-10
Abstract
Abstract A process for manufacturing high-resilient flexible urethan foams characterized by, reacting and foaming polyalkylene ether polyol and an organic polyisocyanate in the presence of a blowing agent, a surfactant and catalyst, (1) using as said polyalkylene ether polyol one which contains 2 to 10% by weight of a vinyl type polymer and in which its hydroxyl number ranges from 25 to 60 mg KOH/g, of its hydroxyl groups 20 to 70 mol% are primary hydroxyl groups and the remaining hydroxyl groups are secondary hydroxyl groups; (2) using as said organic polyisocyanate a mixture of tolylene diisocyanate with diphenylmethane diisocyanate or a crude diphenylmethane diisocyanate; and (3) using as said surfactant a mixture of a high-molecular-weight siloxane-oxyalkylene copolymer with a low-molecular-weight siloxane-oxyalkylene copolymer.
Inventors
- 👤 Kiyoshi Matsubara
- 👤 Yuichi Nomura
- 👤 Tadashi Yatomi
- 👤 Tadashi Hamamura
- 👤 Isao Noda
- 👤 Terumi Watanabe
- 👤 Takao Nomura
- 👤 Isao Sakata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 00:54
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/63; C08G18/632; C08G18/70; C08G18/72; C08G18/74; C08G18/76; C08G18/7607; Y; Y10; Y10S; Y10S521/00; Y10S521/904
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
428 words
In a process for manufacturing high-resilient flexible urethan foams by reacting and foaming polyalkylene ether polyol component and an organic polyisocyanate component in the presence of a blowing agent, a surfactant and catalyst, the improvement comprising (1) using, as said polyalkylene ether polyol component, a polyalkylene ether polyol (a) containing 2 to 10% by weight of a vinyl polymer which is prepared by dissolving a vinyl monomer in polyalkylene ether polyol and by polymerizing said vinyl monomer in said polyalkylene ether polyol, (b) having a hydroxyl number which ranges from 25 to 60 mg KOH/g, and (c) having a primary hydroxyl group content of 20 to 70 mol% and the remaining hydroxyl groups being secondary hydroxyl groups; (2) using, as said organic polyisocyanate component, a mixture of tolylene diisocyanate with either diphenylmethane diisocyanate or a crude diphenylmethane diisocyanate; and (3) using, as said surfactant, a mixture of a high-molecular-weight siloxane-oxyalkylene copolymer with a separately prepared low-molecular-weight siloxane-oxyalkylene copolymer, said high-molecular-weight siloxane-oxyalkylene copolymer being a hydrolyzable siloxane-oxyalkylene copolymer expressed by the general formula (R')(SiO.sub.3).sub.x (R.sub.2 SiO).sub.y {(C.sub.n H.sub.2n O).sub.z R"}.sub.a {R'"}.sub.3x-a wherein x is an integer of at least 1; y is an integer of at least 3; z is an integer of at least 5; a is an integer of 1 to 3x; n is an integer of 2 to 4; R is a monovalent hydrocarbon group; R' is an x-valent hydrocarbon group; R" is a monovalent hydrocarbon group; and R'"is an alkyl group or trihydrocarbylsilyl group, said copolymer containing 10 to 80% by weight of polysiloxane units and 90 to 20% by weight of polyoxyalkylene units, having polysiloxane chains and polyoxyalkylene chains bonded with a C--O--Si bond and having a molecular weight of 1,000 to 16,000 and said low-molecular-weight siloxane-oxyalkylene copolymer being a hydrolyzable siloxane-oxyalkylene copolymer expressed by the formula (R')(SiO 3 ).sub.x (R 2 SiO) y {(C n H 2n O) z R"} a {R'"} 3x-a wherein x is an integer of at least 1; y is an integer of at least 3; z is an integer of 0 or 1 to 4; a is an integer of 1 to 3x; n is an integer of 2 to 4; R is a monovalent hydrocarbon group; R' is an x-valent hydrocarbon group; R" is a monovalent hydrocarbon group; and R'" is an alkyl group or trihydrocarbylsilyl group, said copolymer containing more than 80% by weight of polysiloxane units and less than 20% by weight of polyoxyalkylene units, having polysiloxane chains and polyoxyalkylene chains bonded with a C--O--Si bond and having a molecular weight of 500 to 10,000.
Claim 2
Dependent Claim
428 words
In a process for manufacturing high-resilient flexible urethan foams by reacting and foaming polyalkylene ether polyol component and an organic polyisocyanate component in the presence of a blowing agent, a surfactant and catalyst, the improvement comprising (1) using, as said polyalkylene ether polyol component, a polyalkylene ether polyol (a) containing 2 to 10% by weight of a vinyl polymer which is prepared by dissolving a vinyl monomer in polyalkylene ether polyol and by polymerizing said vinyl monomer in said polyalkylene ether polyol, (b) having a hydroxyl number which ranges from 25 to 60 mg KOH/g, and (c) having a primary hydroxyl group content of 20 to 70 mol% and the remaining hydroxyl groups being secondary hydroxyl groups; (2) using, as said organic polyisocyanate component, a mixture of tolylene diisocyanate with either diphenylmethane diisocyanate or a crude diphenylmethane diisocyanate; and (3) using, as said surfactant, a mixture of a high-molecular-weight siloxane-oxyalkylene copolymer with a separately prepared low-molecular-weight siloxane-oxyalkylene copolymer, said high-molecular-weight siloxane-oxyalkylene copolymer being a hydrolyzable siloxane-oxyalkylene copolymer expressed by the general formula (R')(SiO.sub.3).sub.x (R.sub.2 SiO).sub.y {(C.sub.n H.sub.2n O).sub.z R"}.sub.a {R'"}.sub.3x-a wherein x is an integer of at least 1; y is an integer of at least 3; z is an integer of at least 5; a is an integer of 1 to 3x; n is an integer of 2 to 4; R is a monovalent hydrocarbon group; R' is an x-valent hydrocarbon group; R" is a monovalent hydrocarbon group; and R'"is an alkyl group or trihydrocarbylsilyl group, said copolymer containing 10 to 80% by weight of polysiloxane units and 90 to 20% by weight of polyoxyalkylene units, having polysiloxane chains and polyoxyalkylene chains bonded with a C--O--Si bond and having a molecular weight of 1,000 to 16,000 and said low-molecular-weight siloxane-oxyalkylene copolymer being a hydrolyzable siloxane-oxyalkylene copolymer expressed by the formula (R')(SiO 3 ).sub.x (R 2 SiO) y {(C n H 2n O) z R"} a {R'"} 3x-a wherein x is an integer of at least 1; y is an integer of at least 3; z is an integer of 0 or 1 to 4; a is an integer of 1 to 3x; n is an integer of 2 to 4; R is a monovalent hydrocarbon group; R' is an x-valent hydrocarbon group; R" is a monovalent hydrocarbon group; and R'" is an alkyl group or trihydrocarbylsilyl group, said copolymer containing more than 80% by weight of polysiloxane units and less than 20% by weight of polyoxyalkylene units, having polysiloxane chains and polyoxyalkylene chains bonded with a C--O--Si bond and having a molecular weight of 500 to 10,000.
Claim 3
Dependent Claim
28 words
The process as set forth in claim 1 wherein the polyalkylene ether polyol is a product obtained by adding ethylene oxide and propylene oxide to glycerin or trimethylolpropane.
Claim 4
Dependent Claim
20 words
The process as set forth in claim 1 wherein the vinyl polymer is a polymer of acrylonitrile, styrene or methylmethacrylate.
Claim 5
Dependent Claim
24 words
The process as set forth in claim 1 wherein the organic polyisocyanate is a mixture consisting of tolylene-2,4-diisocyanate, tolylene-2,6-diisocyanate and a crude diphenylmethane diisocyanate.
Claim 6
Dependent Claim
34 words
The process as set forth in claim 1 wherein the organic polyisocyanate is used in amounts 0.95 to 1.15 times the theoretical amount necessary to react with polyalkylene ether polyol and a blowing agent.
Claim 7
Dependent Claim
70 words
The process as set forth in claim 1 wherein said organic polyisocyanate component (2) is a mixture of 70 to 95% by weight of tolylene diisocyanate with 5 to 30% by weight of either diphenylmethane diisocyanate or a crude diphenylmethane diisocyanate, and said surfactant (3) is a mixture of 84.0 to 99.8% by weight of the high-molecular-weight siloxane-oxyalkylene copolymer with 0.2 to 16.0% by weight of the low-molecular-weight siloxane-oxyalkylene copolymer.
Claim 8
Dependent Claim
150 words
The process as set forth in claim 1 wherein said polyalkylene ether polyol component (1) is a polyalkylene ether polyol containing 3 to 6% by weight of a vinyl polymer which is prepared by dissolving a vinyl monomer in polyalkylene ether polyol and by polymerizing said vinyl monomer in said polyalkylene ether polyol and in which its hydroxyl number ranges from 35 to 55 mg KOH/g, of its hydroxyl groups 40 to 55 mol% is a primary hydroxyl group, said organic polyisocyanate component (2) is a mixture of 80 to 90% by weight of tolyene diisocyanate with 10 to 20% by weight of either diphenylmethane diisocyanate with 10 to 20% by weight of either diphenylmethane diisocyanate or a crude diphenylmethane diisocyanate, and said surfactant (3) is a mixture of 92.0 to 99.6% by weight of the high-molecular-weight siloxane-oxyalkylene copolymer with 0.4 to 8.0% by weight of the low-molecular-weight siloxane-oxyalkylene copolymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |