US4119571A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Pellet type oxidation catalyst
Assignee: Motors Liquidation Co
•
Filing: 1977-07-15
•
Granted: 1978-10-10
•
Expires: 1997-07-15
Abstract
Abstract This invention relates to oxidation catalysts wherein the catalytically active metallic material has an impregnation depth of at least 90 microns up to about 250 microns on the porous support which has a surface area of at least 100 m2/g. up to about 250 m2/g. and a pore structure characterized by a macropore volume of at least 0.020 cm3/g. and a macropore radius greater than about 10,000 A DEG , the maximum value for macropore volume being that at which the catalyst is unable to sustain the load and vibration forces to which it is subjected in the converter.
Inventors
- 👤 Louis Hegedus
- 👤 Jack C. Summers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:26
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J35/00; B01J35/60; B01J35/19; B01J35/61; B01J35/615; B01J35/63; B01J35/635; B01J35/64; B01J35/647; B01J35/66; B01J35/69
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
168 words
A noble metal pellet-type oxidation catalyst comprising a porous alumina support member having a surface area of at least 100 m 2 /g. up to about 250 m 2 /g., a pore structure characterized by a macropore volume of at least 0.020 cm 3 /g. up to the value at which the catalyst is not able to sustain the load and vibration forces in the converter and a macropore radius greater than about 10,000 A°, and a catalyst material selected from the group consisting of platinum and platinum/palladium deposited on said support to a depth of at least 90 microns up to about 250 microns, said pore structure serving to increase the diffusivity of the reactants into the interior of the catalyst, the surface area serving to compensate for the otherwise accelerated rate of poisoning caused by the increase in diffusivity, and the depth of deposit being such that the catalyst poisons do not break through the zone of deposit prior to the desired lifetime of the catalyst.
Claim 2
Dependent Claim
168 words
A noble metal pellet-type oxidation catalyst comprising a porous alumina support member having a surface area of at least 100 m 2 /g. up to about 250 m 2 /g., a pore structure characterized by a macropore volume of at least 0.020 cm 3 /g. up to the value at which the catalyst is not able to sustain the load and vibration forces in the converter and a macropore radius greater than about 10,000 A°, and a catalyst material selected from the group consisting of platinum and platinum/palladium deposited on said support to a depth of at least 90 microns up to about 250 microns, said pore structure serving to increase the diffusivity of the reactants into the interior of the catalyst, the surface area serving to compensate for the otherwise accelerated rate of poisoning caused by the increase in diffusivity, and the depth of deposit being such that the catalyst poisons do not break through the zone of deposit prior to the desired lifetime of the catalyst.
Claim 3
Dependent Claim
45 words
A catalyst as in claim 1 wherein the surface area is from about 110 to 150 m 2 /g., the macrovolume from about 0.025 to 0.45 cm 3 /g., and the depth of penetration of said catalyst material is from about 100 to 245 microns.
Claim 4
Dependent Claim
31 words
A catalyst as in claim 2 wherein the surface area is about 131 m 2 /g., the macrovolume about 0.170 cm 3 /g., and the depth of penetration about 103 microns.
Claim 5
Dependent Claim
31 words
A catalyst as in claim 2 wherein the surface area is about 125 m 2 /g., the macrovolume about 0.025 cm 3 /g., and the depth of penetration about 227 microns.
Claim 6
Dependent Claim
31 words
A catalyst as in claim 2 wherein the surface area is about 118 m 2 /g., the macrovolume about 0.179 cm 3 /g., and the depth of penetration about 152 microns.
Claim 7
Dependent Claim
31 words
A catalyst as in claim 2 wherein the surface area is about 119 m 2 /g., the macrovolume about 0.260 cm 3 /g., and the depth of penetration about 100 microns.
Claim 8
Dependent Claim
23 words
A catalyst as in claim 6 wherein the macrovolume is about 0.440 cm 3 /g., and the depth of penetration about 137 microns.
References Cited (Backward Citations)
US3565830A
Cited
US3928237A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |