Ceramic dielectric composition containing alkali metal oxide
Assignee: TDK Corp
•
Filing: 1977-08-10
•
Granted: 1978-10-10
•
Expires: 1997-08-10
Abstract
Abstract A ceramic dielectric composition is provided including 35 to 93.5% by weight of SrTiO3, 4 to 40% by weight of Bi2O3, at least 2.5% but less than 60% by weight of TiO2, and 0.1 to 5.0% by weight, of an alkali metal oxide based on the total amount of SrTiO3, Bi2O3 and TiO2. The ceramic dielectric composition has a high dielectric constant and low dielectric loss and exhibits reduced variations of dielectric constant and the dielectric loss with respect to variation of an applied voltage.
Inventors
- 👤 Shinobu Fujiwara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:30
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/47; C04B35/475; H; H01; H01B; H01B3/00; H01B3/02; H01B3/12; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
91 words
A ceramic dielectric composition containing as a first component 35 to 93.5% by weight of strontium titanate, 4 to 40% by weight of bismuth trioxide and at least 2.5 but less than 60% by weight of titanium dioxide based on the first component, wherein said composition further contains as a second component at least one alkali metal oxide selected from the group consisting of the oxides of lithium, sodium, potassium, rubidium and cesium, in an amount from 0.1 to 5.0% by weight based on the total amount of said first component.
Claim 2
Dependent Claim
91 words
A ceramic dielectric composition containing as a first component 35 to 93.5% by weight of strontium titanate, 4 to 40% by weight of bismuth trioxide and at least 2.5 but less than 60% by weight of titanium dioxide based on the first component, wherein said composition further contains as a second component at least one alkali metal oxide selected from the group consisting of the oxides of lithium, sodium, potassium, rubidium and cesium, in an amount from 0.1 to 5.0% by weight based on the total amount of said first component.
Claim 3
Dependent Claim
49 words
A ceramic dielectric composition according to claim 1, wherein not more than 30% by weight of the strontium oxide in the strontium titanate is replaced by at least one divalent metallic oxide selected from the group consisting of the oxides of calcium, zinc, magnesium, berylium, barium, cadmium and lead.
Claim 4
Dependent Claim
41 words
A ceramic dielectric composition according to claim 1, wherein not more than 30% by weight of the titanium oxide is replaced by at least one tetravalent metallic oxide selected from the group consisting of the oxides of zirconium, tin and hafnium.
Claim 5
Dependent Claim
41 words
A ceramic dielectric composition according to claim 2, wherein not more than 30% by weight of the titanium oxide, is replaced by at least one tetravalent metallic oxide selected from the group consisting of the oxides of zirconium, tin and hafnium.
Claim 6
Dependent Claim
66 words
A ceramic dielectric composition according to claim 1, wherein said dielectric ceramic composition further contains as a third component a minor but effective amount of at least one of the following: (a) at least one oxide selected from the group consisting of oxides of manganese, chromium, iron, cobalt, nickel, niobium and tantalum; (b) a clay material, and; (c) at least one of the rare earth oxides.
Claim 7
Dependent Claim
66 words
A ceramic dielectric composition according to claim 3, wherein said dielectric ceramic composition further comprises as a third component a minor but effective amount of at least one of the following: (a) at least one oxide selected from the group consisting of oxides of manganese, chromium, iron, cobalt, nickel, niobium and tantalum; (b) a clay material, and; (c) at least one of the rare earth oxides.
Claim 8
Dependent Claim
41 words
A ceramic dielectric composition according to claim 5, wherein not more than 30% by weight of the titanium oxide, is replaced by at least one tetravalent metallic oxide selected from the group consisting of the oxides of zirconium, tin and hafnium.
References Cited (Backward Citations)
GB689238A
Cited
US3352697A
Cited
US3709704A
Cited
US3869398A
Cited
US3933668A
Cited
US4058404A
Cited
US4017320A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |