US4117209A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrochemical cells
Assignee: Chloride Silent Power Ltd
•
Filing: 1977-11-21
•
Granted: 1978-09-26
•
Expires: 1997-11-21
Abstract
Abstract In a sodium-sulphur cell having a solid electrolyte separating sodium from a cathodic region containing sulphur/polysulphides in a graphite felt, a cathode current collector is formed of an aluminium substrate on which is an interstrate layer of nickel-chromium alloy covered by a coating of titanium oxide or other electronically conductive oxide intrinsically inert to the cathodic reactant.
Inventors
- 👤 Trevor Leslie Markin
- 👤 Roger John Bones
- 👤 Keith Taylor Scott
- 👤 Geoffrey John May
- 👤 Graham Robinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:23
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/64; H01M4/66; H01M4/661; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; H01M4/664; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
133 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material with respect to the cathodic reactant over the interstrate layer, said interstrate layer being of a nickel chromium alloy containing at least 10% by weight of nickel and at least 10% by weight of chromium, the combined nickel and chromium amounting to at least 50% by weight of the nickel-chromium alloy and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 2
Dependent Claim
133 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material with respect to the cathodic reactant over the interstrate layer, said interstrate layer being of a nickel chromium alloy containing at least 10% by weight of nickel and at least 10% by weight of chromium, the combined nickel and chromium amounting to at least 50% by weight of the nickel-chromium alloy and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 3
Dependent Claim
20 words
A sodium-sulphur cell as claimed in claim 1 wherein the nickel-chromium alloy is a binary alloy of nickel and chromium.
Claim 4
Dependent Claim
16 words
A sodium-sulphur cell as claimed in claim 1 wherein the interstrate layer is a plasma-sprayed layer.
Claim 5
Dependent Claim
18 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is a conductive titanium oxide coating.
Claim 6
Dependent Claim
25 words
A sodium-sulphur cell as claimed in claim 4 wherein the oxide coating is of titanium oxide doped with a metal ion of valency of 5.
Claim 7
Dependent Claim
16 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is strontium-doped lanthanum chromite.
Claim 8
Dependent Claim
15 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is strontium titanate.
Claim 9
Dependent Claim
16 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is iron-doped calcium titanate.
Claim 10
Dependent Claim
15 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is lanthanum cobaltite.
Claim 11
Dependent Claim
21 words
A sodium-sulphur cell as claimed in claim 1 wherein the oxide coating is a mixture of aluminium oxide and titanium dioxide.
Claim 12
Dependent Claim
141 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material inert with respect to the cathodic reactant over the interstrate layer, said interstrate layer being of a nickel chromium alloy containing at least 10% by weight of nickel and at least 10% by weight of chromium, the combined nickel and chromium amounting to at least 50% by weight of the nickel-chromium alloy, the balance comprising substantially iron and/or cobalt, and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 13
Dependent Claim
141 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material inert with respect to the cathodic reactant over the interstrate layer, said interstrate layer being of a nickel chromium alloy containing at least 10% by weight of nickel and at least 10% by weight of chromium, the combined nickel and chromium amounting to at least 50% by weight of the nickel-chromium alloy, the balance comprising substantially iron and/or cobalt, and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 14
Dependent Claim
16 words
A sodium sulphur cell as claimed in claim 11 wherein the conductive oxide material is titania.
Claim 15
Dependent Claim
130 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongate form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer being of a nickel-chromium alloy containing at least 10% by weight of Ni and at least 10% by weight of Cr, the combined nickel and chromium being at least 50% by weight of the total, the balance of said alloy being comprised mainly of iron and/or cobalt.
Claim 16
Dependent Claim
130 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongate form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer being of a nickel-chromium alloy containing at least 10% by weight of Ni and at least 10% by weight of Cr, the combined nickel and chromium being at least 50% by weight of the total, the balance of said alloy being comprised mainly of iron and/or cobalt.
Claim 17
Dependent Claim
15 words
A sodium-sulphur cell as claimed in claim 13 wherein the conductive oxide is titanium oxide.
Claim 18
Dependent Claim
30 words
A sodium-sulphur cell as claimed in claim 13 wherein the conductive oxide is selected from the group consisting of strontium-doped lanthanum chromite, iron-doped calcium titanate, strontium titanate, and lanthanum cobaltite.
Claim 19
Dependent Claim
21 words
A sodium-sulphur cell as claimed in claim 13 wherein the conductive oxide is a mixture of aluminum oxide and titanium oxide.
Claim 20
Dependent Claim
18 words
A sodium-sulphur cell as claimed in claim 13 wherein the conductive oxide is niobium-doped or tantalum-doped titanium oxide.
Claim 21
Dependent Claim
118 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material inert with respect to the cathodic reactant over the interstrate layer, said interstrate layer comprising a nickel chromium alloy consisting of at least 10% by weight of nickel and at least 10% by weight of chromium, and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 22
Dependent Claim
118 words
In a sodium-sulphur cell having a solid electrolyte separating sodium forming an anode from a cathodic reactant comprising sulphur/polysulphides and having a cathode current collector electrically in contact with the cathodic reactant; wherein the improvement comprises a cathode current collector comprising an aluminum substrate, an interstrate layer over the surface of the substrate exposed to cathodic reactant and a coating of electronically conductive oxide material inert with respect to the cathodic reactant over the interstrate layer, said interstrate layer comprising a nickel chromium alloy consisting of at least 10% by weight of nickel and at least 10% by weight of chromium, and the oxide coating being a plasma-sprayed or detonation-gun sprayed protective layer completely covering the interstrate layer.
Claim 23
Dependent Claim
104 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongate form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer comprising a nickel-chromium alloy consisting of at least 10% by weight of Ni and at least 10% by weight of Cr.
Claim 24
Dependent Claim
104 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongate form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer comprising a nickel-chromium alloy consisting of at least 10% by weight of Ni and at least 10% by weight of Cr.
Claim 25
Dependent Claim
153 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongated form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer being a nickel-chromium alloy containing at least 10% by weight of Ni and at least 10% by weight of Cr, the combined nickel and chromium being at least 50% by weight of the total, not more than 5% by weight of at least one element selected from the group consisting of molybdenum, tungsten, niobium, aluminum, titanium, manganese, carbon and yttrium, and the balance being comprised mainly of iron and/or cobalt.
Claim 26
Dependent Claim
153 words
A sodium-sulphur cell comprising a solid electrolyte tube separating sodium around the outside of the electrolyte tube from sulphur/polysulphides constituting the cathodic reactant inside the tube wherein a cathode current collector of elongated form is provided axially located inside the electrolyte tube, which cathode current collector is an aluminum rod or tube, an interstrate layer on the surface of the current collector exposed to the cathodic reactant, and a plasma-sprayed or detonation-gun sprayed conductive oxide coating over the interstrate layer, the interstrate layer being a nickel-chromium alloy containing at least 10% by weight of Ni and at least 10% by weight of Cr, the combined nickel and chromium being at least 50% by weight of the total, not more than 5% by weight of at least one element selected from the group consisting of molybdenum, tungsten, niobium, aluminum, titanium, manganese, carbon and yttrium, and the balance being comprised mainly of iron and/or cobalt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |