Method and apparatus for the manufacture of concrete products
Assignee: Conger Murray Systems Inc
•
Filing: 1976-05-19
•
Granted: 1978-09-26
•
Expires: 1996-05-19
Abstract
Abstract A method and apparatus is provided for the manufacture of concrete products in which a mixture comprised of cement, aggregate, a vinyl acetate-dibutyl maleate copolymer and an amount of water sufficient to make a relatively dry mixture is initially compressed into the desired configuration. This compressed-shaped article is then cured in a chamber charged with carbon dioxide gas to provide a fully cured concrete product having excellent physical properties. The method and apparatus of this invention is especially useful in the manufacture of terrazzo panels and the like.
Inventors
- 👤 John A. Murray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:58
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; B; B28; B28B; B28B1/00; B28B11/00; B28B11/24; B28B11/245; B29; B29C; B29C67/00; B29C67/24; B29C67/242; B29C67/243; B29C43/00; B29K; B29K2031/00; Y; Y10; Y10S; Y10S264/00; Y10S264/43
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
114 words
The method of manufacturing concrete products of a given shape comprising the steps of blending together about 60-75% by weight of an aggregate, about 20-25% by weight of hydraulic cement, about 1-2% by weight of a vinyl acetate-dibutyl maleate copolymer, and about 5-10% by weight of water; compressing said mixture into said given shape in a mold with sufficient pressure to maintain the mixture in said given shape when the mold is removed; curing the compressed shape in an atmosphere consisting essentially of carbon dioxide gas while simultaneously feeding said carbon dioxide gas so as to cause an exothermic temperature rise in the mixture of at least 20°-40° in less than about 5 minutes.
Claim 2
Independent Claim
114 words
The method of manufacturing concrete products of a given shape comprising the steps of blending together about 60-75% by weight of an aggregate, about 20-25% by weight of hydraulic cement, about 1-2% by weight of a vinyl acetate-dibutyl maleate copolymer, and about 5-10% by weight of water; compressing said mixture into said given shape in a mold with sufficient pressure to maintain the mixture in said given shape when the mold is removed; curing the compressed shape in an atmosphere consisting essentially of carbon dioxide gas while simultaneously feeding said carbon dioxide gas so as to cause an exothermic temperature rise in the mixture of at least 20°-40° in less than about 5 minutes.
Claim 3
Dependent Claim
13 words
The method according to claim 1 wherein said hydraulic cement is portland cement.
Claim 4
Dependent Claim
28 words
The method according to claim 1 wherein said copolymer is comprised of about 3 parts by weight of vinyl acetate and 1 part by weight of dibutyl maleate.
Claim 5
Dependent Claim
22 words
The method according to claim 1 for producing terrazzo concrete products wherein the product after curing is ground to expose the aggregate.
Claim 6
Dependent Claim
46 words
The method according to claim 1 wherein the aggregate is comprised of at least one member selected from the group consisting of marble dust, marble chips, granite dust, granite chips, crushed glass and sea shells, and the product after curing is ground to expose the aggregate.
Claim 7
Dependent Claim
151 words
In a method for manufacturing concrete products from a moist cementitious mixture consisting of about 60-75% by weight of an aggregate; about 20-25% by weight of hydraulic cement; about 1-2% by weight of vinyl acetate-dibutyl maleate copolymer and about 5-10% by weight of water, which is compressed to form uncured free-standing shaped members of predetermined height, the method which comprises continuously conveying successive shaped member to and through a chamber, treating said free-standing shaped members with carbon dioxide in said chamber, maintaining said chamber relatively gas tight and flexibly sealed, introducing carbon dioxide into said chamber at the top and bottom sides thereof in amounts sufficient to maintain the carbon dioxide in said chamber at a sufficiently positive pressure to prevent the infusion of substantial amounts of atmospheric air into the chamber, and maintaining the height of said chamber in the range of 11/2-4 times said predetermined height of said shapes.
Claim 8
Dependent Claim
151 words
In a method for manufacturing concrete products from a moist cementitious mixture consisting of about 60-75% by weight of an aggregate; about 20-25% by weight of hydraulic cement; about 1-2% by weight of vinyl acetate-dibutyl maleate copolymer and about 5-10% by weight of water, which is compressed to form uncured free-standing shaped members of predetermined height, the method which comprises continuously conveying successive shaped member to and through a chamber, treating said free-standing shaped members with carbon dioxide in said chamber, maintaining said chamber relatively gas tight and flexibly sealed, introducing carbon dioxide into said chamber at the top and bottom sides thereof in amounts sufficient to maintain the carbon dioxide in said chamber at a sufficiently positive pressure to prevent the infusion of substantial amounts of atmospheric air into the chamber, and maintaining the height of said chamber in the range of 11/2-4 times said predetermined height of said shapes.
Claim 9
Dependent Claim
22 words
The method according to claim 6 in which the height of the chamber is approximately twice said predetermined height of said shapes.
Claim 10
Dependent Claim
23 words
The method according to claim 6 which further includes, after said carbon dioxide treatment, finishing the aggregate to produce a terrazzo concrete product.
Claim 11
Independent Claim
100 words
The method of manufacturing concrete products comprising the steps of blending together about 60-75% by weight of an aggregate, about 20-25% by weight of hydraulic cement, about 1-2% by weight of a vinyl acetate-dibutyl maleate copolymer, and about 5-10% by weight of water; compressing said mixture into a shape of predetermined height, continuously conveying said compressed shape to and through a chamber, and curing the compressed shape in said chamber with carbon dioxide gas while simultaneously feeding said carbon dioxide gas into said chamber, and maintaining the height of said chamber at about 11/2-4 times the height of said shape.
Claim 12
Independent Claim
100 words
The method of manufacturing concrete products comprising the steps of blending together about 60-75% by weight of an aggregate, about 20-25% by weight of hydraulic cement, about 1-2% by weight of a vinyl acetate-dibutyl maleate copolymer, and about 5-10% by weight of water; compressing said mixture into a shape of predetermined height, continuously conveying said compressed shape to and through a chamber, and curing the compressed shape in said chamber with carbon dioxide gas while simultaneously feeding said carbon dioxide gas into said chamber, and maintaining the height of said chamber at about 11/2-4 times the height of said shape.
Claim 13
Dependent Claim
13 words
The method according to claim 9 wherein said hydraulic cement is portland cement.
Claim 14
Dependent Claim
28 words
The method according to claim 9 wherein said copolymer is comprised of about 3 parts by weight of vinyl acetate and 1 part by weight of dibutyl maleate.
Claim 15
Dependent Claim
22 words
The method according to claim 9 for producing terrazzo concrete products wherein the product after curing is ground to expose the aggregate.
Claim 16
Dependent Claim
45 words
The method according to claim 9 wherein the aggregate comprises at least one member selected from the group consisting of marble dust, marble chips, granite dust, granite chips, crushed glass and sea shells, and wherein the product after curing is ground to expose the aggregate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |