Nylon or polyester slip set fabric chemically treated to adhere neoprene, EPDM or butyl film

Claim 2

A process of bonding a woven fabric to a rubber substrate including the steps of: (1) applying to an open mesh, woven nylon or polyester scrim fabric an elastomeric coating of a dispersion of a carboxylated chloroprene latex said latex consisting essentially of chloroprene, as the primary monomer, with from about 2 to about 5% by weight of methacrylic acid as comonomer, and having a carboxyl functionality of about 0.033/100 grams of latex solids; (2) drying the elastomeric coating applied in step (1) thereby mechanically securing the warp and fill yarns of said fabric together at their cross over points and preventing substantial movement or distortion of the individual yarns or thread members of said fabric; and thereafter (3) contacting at least one planar surface of the coated fabric of step (2) with a rubber substrate to form a ply; and (4) curing the fabric/rubber ply of step (3) under rubber-curing conditions to cure the rubber and to form chemical bonds between said fabric and the coating elastomer thereon.

Claim 3

A process of bonding a woven fabric to a rubber substrate including the steps of: (1) applying to an open mesh, woven nylon or polyester scrim fabric an elastomeric coating of a dispersion of a carboxylated chloroprene latex copolymer said latex consisting essentially of chloroprene, as the primary monomer, with from about 2 to about 5% by weight of methacrylic acid as comonomer, having a carbonyl functionality of about 0.033/100 grams of latex solids and a chlorine content of about 36% by weight; (2) drying the elastomeric coating applied in step (1) thereby mechanically securing the warp and fill yarns of said fabric together at their cross over points and preventing substantial movement or distortion of the individual yarns or thread members of said fabric, and thereafter (3) contacting at least one planar surface of the coated fabric of step (2) with a rubber substrate to form a ply; and (4) curing the fabric/rubber ply of step (3) under rubber-curing conditions to cure the rubber and form chemical bonds between said fabric and the coating elastomer thereon.

Claim 4

A process of bonding a woven fabric to a rubber substrate including the steps of: (1) applying to an open mesh, woven nylon or polyester scrim fabric an elastomeric coating of a dispersion of a carboxylated chloroprene latex copolymer said latex consisting essentially of chloroprene, as the primary monomer, with from about 2 to about 5% by weight of methacrylic acid as comonomer, having a carbonyl functionality of about 0.033/100 grams of latex solids and a chlorine content of about 36% by weight; (2) drying the elastomeric coating applied in step (1) thereby mechanically securing the warp and fill yarns of said fabric together at their cross over points and preventing substantial movement or distortion of the individual yarns or thread members of said fabric, and thereafter (3) contacting at least one planar surface of the coated fabric of step (2) with a rubber substrate to form a ply; and (4) curing the fabric/rubber ply of step (3) under rubber-curing conditions to cure the rubber and form chemical bonds between said fabric and the coating elastomer thereon.