Moulding of filled synthetic plastics moulding compositions
Assignee: British Industrial Plastics Ltd
•
Filing: 1977-10-25
•
Granted: 1978-09-19
•
Expires: 1997-10-25
Abstract
Abstract Cured thermoset plastics artefacts, (including extrusions) are made directly from a non-homogeneous blend of a filler and a solid particulate thermosetting material, by use of a screw injection moulding machine (or screw extruder) which is operated to cause the non-homogeneous blend to plasticize or flux so that a homogeneous intimate mixture of the filler and the thermosetting material is formed in the barrel of the machine. Thus, the moulding (or extrusion) sequence includes the provision or formation of the non-homogeneous blend in the barrel.
Inventors
- 👤 Brian John Kendall-Smith
- 👤 Michael Glynn Bonnington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:29
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/17; B29C45/18; B29C45/1816; B29C45/0013; B29C48/00; B29C48/25; B29C48/285; B29C48/288; B29C48/2886; B29C48/29; B29C48/03; B29K; B29K2105/00; B29K2105/0005; B29K2105/06; B29K2105/16; B29K2511/00; B29K2511/14; B29K2995/00; B29K2995/0018; B29K2995/002
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
173 words
The method of injection moulding amino-formaldehyde thermosetting material to produce a cured artefact having filler homogeneously dispersed therewithin without requiring the preliminary step of compounding a moulding powder having the filler already homogeneously dispersed therein, which comprises the steps of: (a) providing a dry thermosetting amino-formaldehyde material which is partly condensed but essentially solid at ambient temperatures; (b) introducing said dry material and filler in at best a rough, non-homogeneous blend directly into the barrel of an injection moulding machine in the absence of solubilizing quantities of solvent, said machine having a heated barrel and a rotary screw which is axially movable in said barrel; (c) rotating said screw simultaneously to feed the blend along the barrel, further condense the material, plasticize said material and impregnate the filler with the plasticized material to provide a homogeneous blend, and effect transfer of homogeneous blend ahead of the screw by screw-back of the screw; (d) injecting homogeneous blend from ahead of the screw into a heated mould; and (e) curing the artefact in the mould.
Claim 2
Independent Claim
173 words
The method of injection moulding amino-formaldehyde thermosetting material to produce a cured artefact having filler homogeneously dispersed therewithin without requiring the preliminary step of compounding a moulding powder having the filler already homogeneously dispersed therein, which comprises the steps of: (a) providing a dry thermosetting amino-formaldehyde material which is partly condensed but essentially solid at ambient temperatures; (b) introducing said dry material and filler in at best a rough, non-homogeneous blend directly into the barrel of an injection moulding machine in the absence of solubilizing quantities of solvent, said machine having a heated barrel and a rotary screw which is axially movable in said barrel; (c) rotating said screw simultaneously to feed the blend along the barrel, further condense the material, plasticize said material and impregnate the filler with the plasticized material to provide a homogeneous blend, and effect transfer of homogeneous blend ahead of the screw by screw-back of the screw; (d) injecting homogeneous blend from ahead of the screw into a heated mould; and (e) curing the artefact in the mould.
Claim 3
Dependent Claim
18 words
The method as defined in claim 1 wherein the material of step (a) is partly condensed melamine-formaldehyde material.
Claim 4
Dependent Claim
18 words
The method as defined in claim 1 wherein the material of step (a) is partly condensed urea-formaldehyde material.
Claim 5
Dependent Claim
22 words
The method as defined in claim 1 wherein the material of step (a) is a blend of partly condensed melamine-formaldehyde and urea-formaldehyde.
Claim 6
Independent Claim
185 words
The method of injection moulding amino-formaldehyde thermosetting material to produce a cured artefact having pigment as well as filler homogeneously dispersed therewithin without requiring the preliminary step of compounding a moulding powder having the filler and pigment already homogeneously dispersed therein, which comprises the steps of: (a) providing a dry thermosetting amino-formaldehyde material which is partly condensed but essentially solid at ambient temperatures; (b) introducing said dry material, pigment and filler in at best a rough, non-homogeneous blend directly into the barrel of an injection moulding machine in the absence of solubilizing quantities of solvent, said machine having a heated barrel and a rotary screw which is axially movable in said barrel; (c) rotating said screw simultaneously to feed the blend along the barrel, further condense the material, plasticize said material and impregnate the filler with the plasticized material and disperse the pigment therein to provide a homogeneous blend, and effect transfer of homogeneous blend ahead of the screw by screw-back of the screw; (d) injecting homogeneous blend from ahead of the screw into a heated mould; and (e) curing the artefact in the mould.
Claim 7
Independent Claim
185 words
The method of injection moulding amino-formaldehyde thermosetting material to produce a cured artefact having pigment as well as filler homogeneously dispersed therewithin without requiring the preliminary step of compounding a moulding powder having the filler and pigment already homogeneously dispersed therein, which comprises the steps of: (a) providing a dry thermosetting amino-formaldehyde material which is partly condensed but essentially solid at ambient temperatures; (b) introducing said dry material, pigment and filler in at best a rough, non-homogeneous blend directly into the barrel of an injection moulding machine in the absence of solubilizing quantities of solvent, said machine having a heated barrel and a rotary screw which is axially movable in said barrel; (c) rotating said screw simultaneously to feed the blend along the barrel, further condense the material, plasticize said material and impregnate the filler with the plasticized material and disperse the pigment therein to provide a homogeneous blend, and effect transfer of homogeneous blend ahead of the screw by screw-back of the screw; (d) injecting homogeneous blend from ahead of the screw into a heated mould; and (e) curing the artefact in the mould.
Claim 8
Dependent Claim
18 words
The method as defined in claim 5 wherein the material of step (a) is partly condensed melamine-formaldehyde material.
Claim 9
Dependent Claim
18 words
The method as defined in claim 5 wherein the material of step (a) is partly condensed urea-formaldehyde material.
Claim 10
Dependent Claim
22 words
The method as defined in claim 5 wherein the material of step (a) is a blend of partly condensed melamine-formaldehyde and urea-formaldehyde.
References Cited (Backward Citations)
US2615205A
Cited
GB779364A
Cited
US2936487A
Cited
US3078511A
Cited
US3137038A
Cited
US3194868A
Cited
US3789103A
Cited
US3746489A
Cited
US3816558A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |