Acid ferric sulfate leaching of copper sulfide concentrates
Assignee: University of Utah Research Foundation Inc
•
Filing: 1977-02-28
•
Granted: 1978-09-19
•
Expires: 1997-02-28
Abstract
Abstract A process for hydrometallurgically recovering copper from concentrates of chalcopyrite and other sulfide and mixed sulfide ores utilizes the pretreatment step of fine grinding of the concentrates coupled with subsequent leaching steps. As a pretreatment for the copper-containing concentrates, the concentrates are ground, preferrably with an attritor-type grinding device, to reduce the particle size of the copper bearing concentrate to one micron or less in size. The finely ground copper concentrate is then leached in an acidified ferric sulfate solution to recover the copper contained therein. Following the leching step, a solid-liquid separation is effected. Elemental sulfur may be recovered, and iron removal is achieved by crystallization of iron salts. Ferrous ion is then oxidized to ferric ion for recycling to the leaching step.
Inventors
- 👤 Milton E. Wadsworth
- 👤 Jan D. Miller
- 👤 John A. Herbst
- 👤 John L. Kolbe
- 👤 Howard Wayne Hayden
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:12
CPC Classifications
C; C22; C22B; C22B15/00; C22B15/0063; C22B15/0065; C22B15/0067; C22B15/0071; C22B15/0002; C22B15/0004; C22B15/0006; C22B15/0084; C22B15/0086; C22B15/0089; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
123 words
A process for removing copper from copper sulfide bearing materials comprising the steps of: fine-grinding copper sulfide-bearing materials to a particle size of at most one micron; leaching said finely-ground copper sulfide-bearing material in an acidic solution containing a stoichiometric amount of ferric ions to oxidize the copper ions contained in the copper sulfide-bearing material and form a pregnant leach solution containing said copper ions and ferrous ions; separating said copper ion-bearing pregnant leach solution from any remaining solid materials; crystallizing iron salts in the pregnant leach solution; electrolyzing the pregnant leach solution and ferrous sulfate to produce elemental copper and ferrous ion in solution; and introducing oxygen and sulfuric acid to the ferrous ion-bearing solution to oxidize the ferrous to ferric ions.
Claim 2
Dependent Claim
123 words
A process for removing copper from copper sulfide bearing materials comprising the steps of: fine-grinding copper sulfide-bearing materials to a particle size of at most one micron; leaching said finely-ground copper sulfide-bearing material in an acidic solution containing a stoichiometric amount of ferric ions to oxidize the copper ions contained in the copper sulfide-bearing material and form a pregnant leach solution containing said copper ions and ferrous ions; separating said copper ion-bearing pregnant leach solution from any remaining solid materials; crystallizing iron salts in the pregnant leach solution; electrolyzing the pregnant leach solution and ferrous sulfate to produce elemental copper and ferrous ion in solution; and introducing oxygen and sulfuric acid to the ferrous ion-bearing solution to oxidize the ferrous to ferric ions.
Claim 3
Dependent Claim
28 words
A process as set forth in claim 1, wherein said ferric ions produced by oxidizing ferrous ions are recycled to the leaching step for a continuous, closed system.
Claim 4
Dependent Claim
31 words
A process as set forth in claim 1, wherein elemental sulfur formed in said leaching step is removed from said pregnant leach solution with other solids at the liquid-solid separation step.
Claim 5
Dependent Claim
26 words
A process as set forth in claim 1, wherein said nonreacted copper sulfide-bearing material separated from said pregnant leach solution is recycled to said leaching step.
Claim 6
Dependent Claim
22 words
A process as set forth in claim 1, wherein said leaching step is carried out at a temperature of approximately 90° C.
Claim 7
Dependent Claim
32 words
A process as set forth in claim 1, wherein ferrous ions in the remaining solution are oxidized to ferric ions and recycled into the leaching step to form a closed, continuous system.
Claim 8
Dependent Claim
26 words
A process as set forth in claim 6, wherein said ferrous ions are oxidized to ferric ions in the presence of oxygen gas and sulfuric acid.
Claim 9
Dependent Claim
19 words
A process as set forth in claim 1, wherein said leaching step is carried out at approximately 90° C.
Claim 10
Dependent Claim
21 words
A process as set forth in claim 1, wherein dissolved iron in the remaining solution is precipitated as an iron salt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |