Method of electrolyzing brine
Assignee: BASF Corp
•
Filing: 1976-10-22
•
Granted: 1978-09-19
•
Expires: 1996-10-22
Abstract
Abstract A practical method of electrolyzing sodium chloride brine on a commercial scale, obtaining in good yield a caustic product exceptionally low in salt content, is provided. The process necessarily involves working with a brine of lower calcium-ion content than is ordinarily used, using dimensionally stable anodes, using, preferably but not necessarily, a heat-treated ion-exchange membrane as a separator within the cell, and periodically taking action to reduce the cell voltage, by reducing the current or interrupting it, alone or with a concomitant flushing of the catholyte portion of the cell.
Inventors
- 👤 Michael Krumpelt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:19
CPC Classifications
C; C25; C25B; C25B1/00; C25B1/01; C25B1/34; C25B1/46
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
125 words
A process for electrolyzing sodium chloride brine in an electrolytic cell having a dimensionally stable anode, a cathode, and between said anode and said cathode a membrane of copolymerized tetrafluoroethylene and perfluorovinylether sulfonylfluoride having an equivalent weight number of approximately 1000 to 1500 and a thickness of approximately 0.1 to 0.5 millimeters, said process involving the electrolysis of brine containing a membrane obstructing proportion of calcium not exceeding 6 parts per million of calcium, said process including the use at intervals of approximately once per month or less frequently of a voltage-reduction action, said voltage-reduction action comprising reducing the current through said electrolytic cell for a period of 0.5 to 90 minutes to a value of less than 20 percent of the current normally used.
Claim 2
Dependent Claim
125 words
A process for electrolyzing sodium chloride brine in an electrolytic cell having a dimensionally stable anode, a cathode, and between said anode and said cathode a membrane of copolymerized tetrafluoroethylene and perfluorovinylether sulfonylfluoride having an equivalent weight number of approximately 1000 to 1500 and a thickness of approximately 0.1 to 0.5 millimeters, said process involving the electrolysis of brine containing a membrane obstructing proportion of calcium not exceeding 6 parts per million of calcium, said process including the use at intervals of approximately once per month or less frequently of a voltage-reduction action, said voltage-reduction action comprising reducing the current through said electrolytic cell for a period of 0.5 to 90 minutes to a value of less than 20 percent of the current normally used.
Claim 3
Dependent Claim
41 words
A process as defined in claim 1, wherein said voltage-reducing step comprises reducing the flow of current through said cell to a value of less than 5 percent of the value normally used for a period of 1 to 20 minutes.
Claim 4
Dependent Claim
61 words
A process as defined in claim 2, characterized in that said voltage-reducing step further comprises the practice of increasing the flow of liquid, during said time of current reduction, through the portion of said cell between said membrane and said cathode to a value of five to twenty times the flow during normal operation by addition of water to said portion.
Claim 5
Dependent Claim
61 words
A process as defined in claim 1, characterized in that said voltage-reducing step further comprises the practice of increasing the flow of liquid, during said time of current reduction, through the portion of said cell between said membrane and said cathode to a value of 5 to 20 times the flow during normal operation by addition of water to said portion.
Claim 6
Dependent Claim
114 words
A process for electrolyzing sodium chloride brine in an electrolytic cell having a dimensionally stable anode, a cathode, and between said anode and said cathode a membrane of copolymerized tetrafluoroethylene and perfluorovinylether sulfonylfluoride having an equivalent weight number of approximately 1000 to 1500 and a thickness of approximately 0.1 to 0.5 millimeters, said process involving the electrolysis of brine containing a membrane obstructing proportion of calcium not exceeding 6 parts per million of calcium, said process including the use at intervals of approximately once per month or less frequently of a voltage-reduction action, said voltage-reduction action comprising interrupting the flow of current through said electrolytic cell for a period of 0.5 to 90 minutes.
Claim 7
Dependent Claim
114 words
A process for electrolyzing sodium chloride brine in an electrolytic cell having a dimensionally stable anode, a cathode, and between said anode and said cathode a membrane of copolymerized tetrafluoroethylene and perfluorovinylether sulfonylfluoride having an equivalent weight number of approximately 1000 to 1500 and a thickness of approximately 0.1 to 0.5 millimeters, said process involving the electrolysis of brine containing a membrane obstructing proportion of calcium not exceeding 6 parts per million of calcium, said process including the use at intervals of approximately once per month or less frequently of a voltage-reduction action, said voltage-reduction action comprising interrupting the flow of current through said electrolytic cell for a period of 0.5 to 90 minutes.
Claim 8
Dependent Claim
29 words
A process as defined in claim 5, wherein said voltage-reducing step comprises interrupting the flow of the current through said cell for a period of 1 to 20 minutes.
Claim 9
Dependent Claim
61 words
A process as defined in claim 6, characterized in that said voltage-reducing step further comprises the practice of increasing the flow of liquid, during said time of current interruption, through the portion of said cell between said membrane and said cathode to a value of 5 to 20 times the flow during normal operation by addition of water to said portion.
Claim 10
Dependent Claim
61 words
A process as defined in claim 5, characterized in that said voltage-reducing step further comprises the practice of increasing the flow of liquid during said time of current interruption, through the portion of said cell between said membrane and said cathode to a value of 5 to 20 times the flow during normal operation by addition of water to said portion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |