Method of preparing metal oxide slurries
Assignee: Tronox Pigment UK Ltd
•
Filing: 1976-12-02
•
Granted: 1978-09-19
•
Expires: 1996-12-02
Abstract
Abstract A high solids metal oxides coated titanium dioxide aqueous slurry requires a negative charge and a high pH for use in aqueous paint media. A hot ageing of the coated titanium dioxide can alter the isoelectric point of the slurry and make practicable the avoidance of mixtures of metal oxide coating agents which give rise to processing difficulties and the use of mixtures of metal oxides which would not without the hot ageing step give suitable charge and pH characteristics. An example of a suitable mixture of metal oxide coating agents is a 1:1 molar Al 2 O 3 : TiO 2 mixture. An example of hot ageing conditions is the use of a temperature of 98° C - 100° C for 1 hour while avoiding loss of water and under alkaline conditions.
Inventors
- 👤 Hubert Harold Chambers
- 👤 Brian John Tear
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:13
CPC Classifications
C; C09; C09D; C09D17/00; C09D17/004; C09D17/007; C09D17/008; C09C; C09C1/00; C09C1/36; C09C1/3607; C09C1/3653; C09C1/3661; C01; C01P; C01P2004/00; C01P2004/80; C01P2004/82; C01P2004/84; C01P2006/00; C01P2006/22
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
187 words
A process for the production of an alkaline aqueous slurry having a negative charge and a solids content of at least 60% by weight, of a coated pigmentary titanium dioxide, which comprises; (a) providing an aqueous dispersion of pigmentary particles of titanium dioxide; (b) forming a coating on said particles by simultaneously precipitating in the dispersion at an alkaline pH, at least two different metal oxides, at least one of said metal oxides being selected from those giving an isoelectric point at a pH below 7 and at least one of said metal oxides being selected from those giving an isoelectric point at a pH above 7, under conditions such that a filterable, washable slurry is obtained; (c) filtering and washing the coated particles in the slurry to obtain a washed filter cake; (d) raising the concentration of the washed filter cake to at least 60% by weight of coated particles; (e) redispersing the particles of the raised concentration filter cake; and (f) maintaining the filtered, washed, coated particles at a temperature of from 40° C to 100° C for a duration of at least 20 minutes.
Claim 2
Dependent Claim
187 words
A process for the production of an alkaline aqueous slurry having a negative charge and a solids content of at least 60% by weight, of a coated pigmentary titanium dioxide, which comprises; (a) providing an aqueous dispersion of pigmentary particles of titanium dioxide; (b) forming a coating on said particles by simultaneously precipitating in the dispersion at an alkaline pH, at least two different metal oxides, at least one of said metal oxides being selected from those giving an isoelectric point at a pH below 7 and at least one of said metal oxides being selected from those giving an isoelectric point at a pH above 7, under conditions such that a filterable, washable slurry is obtained; (c) filtering and washing the coated particles in the slurry to obtain a washed filter cake; (d) raising the concentration of the washed filter cake to at least 60% by weight of coated particles; (e) redispersing the particles of the raised concentration filter cake; and (f) maintaining the filtered, washed, coated particles at a temperature of from 40° C to 100° C for a duration of at least 20 minutes.
Claim 3
Dependent Claim
26 words
A process as claimed in claim 1 wherein the precipitation of the metal oxide coating is conducted to a final pH of from 9.0 to 10.5.
Claim 4
Dependent Claim
34 words
A process as claimed in claim 1 wherein the coating comprises at least one oxide of aluminium, beryllium, lead or zinc and at least one oxide of cerium, antimony, silicon, titanium, zirconium or tin.
Claim 5
Dependent Claim
26 words
A process as claimed in claim 3 wherein the mixed metal oxide coating comprises alumina and titania in a molar ratio of from 0.5:1 to 1.25:1.
Claim 6
Dependent Claim
25 words
A process as claimed in claim 4 wherein the mixed metal oxide coating comprises alumina and titania in substantially equal quantities on a molar basis.
Claim 7
Dependent Claim
25 words
A process as claimed in claim 1 wherein the mixed metal oxide coating comprises from 0.5 to 15% of the weight of the titanium dioxide.
Claim 8
Dependent Claim
30 words
A process as claimed in claim 1 wherein the mixed metal oxide coating is precipitated onto the titanium dioxide particles at a temperature of from 10° C to 40° C.
Claim 9
Dependent Claim
57 words
A process as claimed in claim 1 wherein the concentration of the washed titanium dioxide is raised to at least the desired product concentration by filtering the coated titanium dioxide, drying a proportion of the coated titanium dioxide and blending the dried titanium dioxide with at least a portion of the remainder of the coated titanium dioxide.
Claim 10
Dependent Claim
20 words
A process as claimed in claim 1 wherein the desired product concentration is from 60% to 75% by weight solids.
Claim 11
Dependent Claim
31 words
A process as claimed in claim 1 wherein said temperature is from 80° C to 100° C for at least 30 minutes without allowing the coated titanium dioxide to dry out.
Claim 12
Dependent Claim
26 words
A process as claimed in claim 1 wherein said maintaining is conducted so as to reduce the isoelectric point of the slurry by at least 1.0.
Claim 13
Dependent Claim
20 words
A process as claimed in claim 11 wherein the isoelectric point of the maintained slurry is from 4.5 to 5.9.
Claim 14
Dependent Claim
119 words
A process for preparing a high solids content, alkaline, negatively charged, aqueous slurry of a metal oxide coated titanium dioxide pigment suitable for direct incorporation into an aqueous paint or paper media, which comprises; providing an alkaline, filtered, washed aqueous slurry of at least 60 percent by weight of a pigmentary titanium dioxide coated by precipitation of a mixture of hydrous metal oxides, at least one of said oxides being selected from those giving an isoelectric point at a pH above 7 and one being selected from those giving an isoelectric point at a pH below 7; and heating said slurry to a temperature of from 40° C to 100° C for a period of at least 20 minutes.
Claim 15
Dependent Claim
119 words
A process for preparing a high solids content, alkaline, negatively charged, aqueous slurry of a metal oxide coated titanium dioxide pigment suitable for direct incorporation into an aqueous paint or paper media, which comprises; providing an alkaline, filtered, washed aqueous slurry of at least 60 percent by weight of a pigmentary titanium dioxide coated by precipitation of a mixture of hydrous metal oxides, at least one of said oxides being selected from those giving an isoelectric point at a pH above 7 and one being selected from those giving an isoelectric point at a pH below 7; and heating said slurry to a temperature of from 40° C to 100° C for a period of at least 20 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |