Thermoplastic compositions comprising PVC and chlorinated polyethylene

Claim 2

Thermoplastic composition consisting of (a) 95 to 70% by weight of a vinyl chloride polymer and (b) 5 to 30% by weight of a chlorinated high-density polyethylene, wherein the chlorinated high-density polyethylene has a chlorine content of 38 to 42% by weight, a residue value of 55 to 70% by weight (determined by extraction with toluene/acetone in a ratio of 1:1) and a swelling value of less than 1% by weight (measured in methyl-cyclohexane) and has been prepared from high-density polyethylene having a density of 0.955 to 0.965 g/cm 3 , a melting index MFI 190/5 (DIN 53 735) of 20 to 65 g/10 min. and a reduced specific viscosity (ISO/R 1191) of 1 to 2 dl/g, by chlorinating in water or hydrochloric acid in the presence of 0 to 2% by weight of silicic acid and 0 to 1% by weight of siloxane oil, each time calculated on the high-density polyethylene used, at temperatures of from 50 to 120° C., while introducing at least the last 10% of chlorine at a temperature of from 110° to 120° C.

Claim 3

Thermoplastic composition as claimed in claim 1, the high-density polyethylene whereof has been prepared at a temperature of from 110° to 120° C.

Claim 4

Thermoplastic composition as claimed in claim 1, the high-density polyethylene whereof has been chlorinated at a temperature beginning in the range of from 70° to 90° C. and ending in the range of from 110° to 120° C.

Claim 5

Process for preparing a thermoplastic composition by mixing (a) 95 to 70% by weight of a vinyl chloride polymer ans (b) 5 to 30% by weight of a chlorinated high-density polyethylene wherein there is used a chlorinated high-density polyethylene that has a chlorine content of 38 to 42% by weight, a residue value of 55 to 70% by weight (determined by extraction with toluene/acetone in a ratio of 1:1) and a swelling value of less than 1% by weight (measured in methylcyclohexane) and that has been prepared from a high-density polyethylene having a density of 0.955 to 0.965 g/cm 3 , a melting index MFI 190/5(DIN 53 735) of 20 to 65 g/10 min. and a reduced specific viscosity (ISO/R 1191) of 1 to 2 dl/g, by chlorinating in water or in hydrochloric acid in the presance of 0 to 2% by weight of silicic acid and 0 to 1% by weight of siloxane oil, each time calculated on the high-density polyethylene used, at a temperature of from 50° to 120° C., while introducing at least the last 10% of chlorine at a temperature of from 110° to 120° C.

Claim 6

Process for preparing a thermoplastic composition by mixing (a) 95 to 70% by weight of a vinyl chloride polymer ans (b) 5 to 30% by weight of a chlorinated high-density polyethylene wherein there is used a chlorinated high-density polyethylene that has a chlorine content of 38 to 42% by weight, a residue value of 55 to 70% by weight (determined by extraction with toluene/acetone in a ratio of 1:1) and a swelling value of less than 1% by weight (measured in methylcyclohexane) and that has been prepared from a high-density polyethylene having a density of 0.955 to 0.965 g/cm 3 , a melting index MFI 190/5(DIN 53 735) of 20 to 65 g/10 min. and a reduced specific viscosity (ISO/R 1191) of 1 to 2 dl/g, by chlorinating in water or in hydrochloric acid in the presance of 0 to 2% by weight of silicic acid and 0 to 1% by weight of siloxane oil, each time calculated on the high-density polyethylene used, at a temperature of from 50° to 120° C., while introducing at least the last 10% of chlorine at a temperature of from 110° to 120° C.

Claim 7

Process as claimed in claim 4, which comprises using a high-density polyethylene which has been chlorinated at a temperature beginning in the range of from 70° to 90° C. and ending in the range of from 110° to 120° C.