Production of high temperature resistant polymer compositions capable of forming superior fiber reinforced composite articles

Claim 2

A process for providing a high temperature resistant composition from a normally intractable high temperature resistant polymer, which composition is capable of forming a three dimensional shaped article which comprises: I. providing a solution of a substance selected from the group consisting of: (a) a nitrogenous intractable high temperature resistant polymer which does not have a glass transition temperature below its decomposition temperature, or precursors capable of forming the same; and (b) an admixture comprising from about 60 to about 95 parts by weight of the intractable polymer of (a) and from about 5 to about 40 parts by weight of at least one cross-linkable polymer exhibiting a glass transition temperature above 200° C and below its decomposition temperature, or precursors capable of forming the same; Ii. providing a suspension of partially plasticized organic fibers derived from polymers selected from the group consisting of: (a) the intractable polymer of step I(a), (b) polybenzimidazoles, (c) high temperature resistant aromatic polyamides, (d) high temperature resistant aromatic polyesters, and mixtures thereof; Iii. combining the suspension of II and the solution of I in a manner sufficient to provide a precipitation of a major portion of the dissolved substance of I affixed to the suspended organic fibers of II thereby forming a mixture containing a fiber-particle aggregate; Iv. combining the mixture of III with a non-solvent in a manner sufficient, and with properties sufficient to precipitate, affix, and incorporate the remaining portion of the dissolved substance of I from the mixture of III into the fiber-particle aggregate to form a fiber-particle aggregate composition comprising from about 95 to about 50%, by composition weight, of the substance present in the solution of I affixed to and intimately admixed with from about 5 to about 50%, by composition weight, of said organic fibers of II; and V. filtering and washing the composition to remove residual solvent.

Claim 3

The process of claim 1 wherein the suspension of partially plasticized organic fibers is provided by then contacting the organic fibers with a mixture of sulfuric acid and water having a ratio by volume of about 60:40 to about 75:25 for a period of about 5 to about 20 minutes.

Claim 4

The process of claim 1 wherein the organic fibers of II have an average length of about 0.25 to about 2.0 inches.

Claim 5

The process of claim 1 wherein the cross-linkable polymer is selected from the group consisting of polybenzimidazoles, polybenzoxazoles, polyoxadiazoles, polyquinoxalines, polybenzothiazoles, and mixtures thereof.

Claim 6

The process of claim 1 wherein the aromatic polyamide of II(c) is poly(m-phenyleneisophthalamide).

Claim 7

The process of claim 1 wherein about 60 to about 95% of the totally dissolved substance of the solution of I is precipitated onto the surface of the suspended organic fibers of step II.

Claim 8

The process of claim 1 wherein the solution of step I is added to the solution of step II at a slow rate of addition.

Claim 9

The process of claim 1 wherein the fiber-particle aggregate composition of step IV comprises from about 10 to about 40% of organic fibers and from about 90 to about 60% of the substance utilized in step I.

Claim 10

The process of claim 1 wherein the nitrogenous intractable high temperature resistant polymer of step I which lacks a glass transition temperature below its decomposition temperature is a condensation product of at least one organic tetra-amine with at least one tetra-carboxylic acid or corresponding anhydride.

Claim 11

A process for providing a composition from a normally intractable high temperature resistant polymer, which composition is capable of being molded into a shaped article which comprises: I. providing a solution of a substance selected from the group consisting of: (a) an intractable high temperature resistant polymer which is the condensation product of at least one organic tetraamine with at least one tetracarboxylic acid or corresponding anhydride and which does not have a glass transition temperature below its decomposition temperature; (b) an admixture comprising from about 60 to about 95 parts by weight of the intractable polymer of (a) and from about 5 to about 40 parts by weight of at least one cross-linkable polymer exhibiting a glass transition temperature above 200° C and below its decomposition temperature, or precursors capable of forming the same; Ii. providing a suspension of partially plasticized organic fibers having an average length of from about 0.25 to about 2.0 inches which fibers are derived from polymers selected from the group consisting of: (a) the intractable polymer of step I(a), (b) polybenzimidazoles, (c) high temperature resistant aromatic polyamides, (d) high temperature resistant aromatic polyesters, and mixtures thereof; Iii. adding the solution of I to the suspension of II at a slow rate of addition to affix a precipitate of about 60% to about 95% of the total amount of the dissolved substance of I onto the suspended organic fibers of step II thereby forming a mixture containing a fiber-particle aggregate; Iv. combining the mixture of III with a non-solvent medium, under high shear conditions, to precipitate affix and incorporate the remaining portion of the dissolved substance of step I from the mixture of III into the fiber particle aggregate to form a fiber-particle aggregate composition comprising from about 95 to about 50% by weight of the total composition of the substance present in the solution of I affixed to and intimately admixed with from about 5 to about 50%, by composition weight, of said organic fibers of II; and V. filtering and washing the composition while submerged under water to remove residual solvent.

Claim 12

A process for providing a composition from a normally intractable high temperature resistant polymer, which composition is capable of being molded into a shaped article which comprises: I. providing a solution of a substance selected from the group consisting of: (a) an intractable high temperature resistant polymer which is the condensation product of at least one organic tetraamine with at least one tetracarboxylic acid or corresponding anhydride and which does not have a glass transition temperature below its decomposition temperature; (b) an admixture comprising from about 60 to about 95 parts by weight of the intractable polymer of (a) and from about 5 to about 40 parts by weight of at least one cross-linkable polymer exhibiting a glass transition temperature above 200° C and below its decomposition temperature, or precursors capable of forming the same; Ii. providing a suspension of partially plasticized organic fibers having an average length of from about 0.25 to about 2.0 inches which fibers are derived from polymers selected from the group consisting of: (a) the intractable polymer of step I(a), (b) polybenzimidazoles, (c) high temperature resistant aromatic polyamides, (d) high temperature resistant aromatic polyesters, and mixtures thereof; Iii. adding the solution of I to the suspension of II at a slow rate of addition to affix a precipitate of about 60% to about 95% of the total amount of the dissolved substance of I onto the suspended organic fibers of step II thereby forming a mixture containing a fiber-particle aggregate; Iv. combining the mixture of III with a non-solvent medium, under high shear conditions, to precipitate affix and incorporate the remaining portion of the dissolved substance of step I from the mixture of III into the fiber particle aggregate to form a fiber-particle aggregate composition comprising from about 95 to about 50% by weight of the total composition of the substance present in the solution of I affixed to and intimately admixed with from about 5 to about 50%, by composition weight, of said organic fibers of II; and V. filtering and washing the composition while submerged under water to remove residual solvent.

Claim 13

The process of claim 10 wherein the aromatic polyamide of step II(c) is poly(m-phenyleneisophthalamide).

Claim 14

The process of claim 10 wherein said cross-linkable polymer is selected from the group consisting of polybenzimidazoles, polybenzoxazoles, polyoxadiazoles, polyquinoxalines, polybenzothiazoles and mixtures thereof.

Claim 15

The process of claim 10 wherein the suspension of partially plasticized organic fibers is provided by suspending them in a plasticizing agent for a period of not less than 5 minutes.

Claim 16

The process of claim 10 wherein the suspension of partially plasticized organic fibers is provided by suspending them in a mixture of sulfuric acid and water having a ratio by volume of about 60:40 to about 75:25 respectively for a period of about 10 to about 15 minutes.

Claim 17

The process of claim 10 wherein the admixture of step I(b) comprises about 80 to about 90 parts by weight of said intractable polymer of step I(a) and about 10 to 20 parts of polybenzimidazole.

Claim 18

The process of claim 10 wherein the poybenzimidazole is poly 2,2'-(m-phenylene)5,5'-bibenzimidazole.

Claim 19

The process of claim 9 wherein the solution of step I is added to the suspension of step II under conditions of low agitation.

Claim 20

The process of claim 10 wherein the non-solvent medium of step IV is a C 1 to C 3 alcohol.

Claim 21

The process of claim 10 wherein the solution of step I is provided by dissolving said substance in a solvent selected from the group consisting of sulfuric acid, methane sulfonic acid, polyphosphoric acid, chlorosulfonic acid, trifluoromethane sulfonic acid, benzenesulfonic acid and mixtures thereof.

Claim 22

A reinforced high temperature resistant composition capable of forming a three-dimensional shaped article having a mean flexural strength of at least 5000 psi at room temperature which composition is prepared by a process which comprises: I. providing a solution of a substance selected from the group consisting of: (a) a nitrogenous intractable high temperature resistant polymer which does not have a glass transition temperature below its decomposition temperature, or precursors capable of forming the same; and (b) an admixture comprising from about 60 to about 95 parts by weight of the intractable polymer of (a) and from about 5 to about 40 parts by weight of at least one cross-linkable polymer exhibiting a glass transition temperature above 200° C and below its decomposition temperature, or precursors capable of forming the same; Ii. providing a suspension of partially plasticized organic fibers derived from polymers selected from the group consisting of (a) the intractable polymer of step I(a), (b) polybenzimidazoles, (c) high temperature resistant aromatic polyamides, (d) high temperature resistant aromatic polyesters, and mixtures thereof; Iii. combining the suspension of II and the solution of I in a manner sufficient to provide a precipitation of a major portion of the dissolved substance of I affixed to the suspended organic fibers of II thereby forming a mixture containing a fiber-particle aggregate; Iv. combining said mixture with a non-solvent medium under high shear conditions to precipitate affix and incorporate the remainder of the dissolved substance of I from said mixture into said partially plasticized organic fibers having the partial precipitate affixed thereto to form a fiber-particle aggregate composition comprising from about 95 to about 50%, by composition weight, of the substance of solution I and from about 5 to about 50% by composition, weight of the organic fibers of II and filtering and washing the composition to remove residual solvent.

Claim 23

A reinforced high temperature resistant composition capable of forming a three-dimensional shaped article having a mean flexural strength of at least 5000 psi at room temperature which composition is prepared by a process which comprises: I. providing a solution of a substance selected from the group consisting of: (a) a nitrogenous intractable high temperature resistant polymer which does not have a glass transition temperature below its decomposition temperature, or precursors capable of forming the same; and (b) an admixture comprising from about 60 to about 95 parts by weight of the intractable polymer of (a) and from about 5 to about 40 parts by weight of at least one cross-linkable polymer exhibiting a glass transition temperature above 200° C and below its decomposition temperature, or precursors capable of forming the same; Ii. providing a suspension of partially plasticized organic fibers derived from polymers selected from the group consisting of (a) the intractable polymer of step I(a), (b) polybenzimidazoles, (c) high temperature resistant aromatic polyamides, (d) high temperature resistant aromatic polyesters, and mixtures thereof; Iii. combining the suspension of II and the solution of I in a manner sufficient to provide a precipitation of a major portion of the dissolved substance of I affixed to the suspended organic fibers of II thereby forming a mixture containing a fiber-particle aggregate; Iv. combining said mixture with a non-solvent medium under high shear conditions to precipitate affix and incorporate the remainder of the dissolved substance of I from said mixture into said partially plasticized organic fibers having the partial precipitate affixed thereto to form a fiber-particle aggregate composition comprising from about 95 to about 50%, by composition weight, of the substance of solution I and from about 5 to about 50% by composition, weight of the organic fibers of II and filtering and washing the composition to remove residual solvent.

Claim 24

A high temperature resistant three dimensional shaped article having a flexural strength of at least 5000 psi comprising the high temperature resistant composition of claim 20 which has been molded under elevated temperature and pressure.

Claim 25

The composition of claim 20 wherein said cross-linkable polymer is selected from the group consisting of polybenzimidazoles, polybenzoxazoles, polyoxadiazoles, polyquinoxalines, polybenzothiazoles and mixtures thereof.

Claim 26

The composition of claim 20 wherein the admixture of I(b) comprises about 80 to about 90 parts by weight of said intractable polymer of step I(a) and about 10 to 20 parts of polybenzimidazole.

Claim 27

The composition of claim 20 wherein the polybenzimidazole is poly 2,2'-(m-phenylene)5,5'-bibenzimidazole.

Claim 28

The composition of claim 20 wherein the fiber-particle aggregate composition is filtered and washed while submerged under water.

Claim 29

The composition of claim 20 wherein the suspension of partially plasticized organic fibers is provided by contacting said organic fibers with a mixture of sulfuric acid and water at a ratio of about 60:40 to 75:25 for a period of about 10 to about 15 minutes.

Claim 30

The composition of claim 20 wherein the organic fibers are suspended in a 60:40 mixture of H 2 SO 4 and water respectively.

Claim 31

The composition of claim 20 wherein said solution is added to said suspension under conditions of low agitation.

Claim 32

The composition of claim 20 wherein the non-solvent medium of step IV is a C 1 to C 3 alcohol.

Claim 33

The composition of claim 20 wherein the aromatic polyamide of II(c) is poly(m-phenyleneisophthalamide).