Molding expandable styrene polymer particles
Assignee: Lyondell Chemical Technology LP
•
Filing: 1977-11-07
•
Granted: 1978-09-12
•
Expires: 1997-11-07
Abstract
Abstract Expandable styrene polymer particles having reduced flammability are made by incorporating from 0.1 to 15 weight percent of non-polymeric organic halogen compounds into the polymer during impregnation of the polymer particles with a blowing agent in aqueous suspension. The addition of 0.001 to 0.5 weight percent of dialkyl tin maleates or fumarates during the impregnation step produces expandable styrene polymer particles with greatly improved molding characteristics such as reduced pruning tendency, increased mold fusion, and greater dimensional stability. Addition of a synergistic amount of 0.001 to 0.4 weight percent of a hindered phenolic antioxidant with the tin compounds gives improved molding characteristics with retention of polymer molecular weight.
Inventors
- 👤 Walter O. Pillar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:00
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0014; C08J9/0052; C08J2325/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
173 words
In a process for making styrene polymer particles less flammable by impregnating the polymer particles by heating in aqueous suspension in the presence of a non-polymeric organic halogen compound and a blowing agent at temperatures between 100° C and 125° C, the improvement comprising adding, prior to heating for the impregnation, about 0.001 to 0.50 percent by weight, based on polymer particles, of a tin compound selected from the group consisting of dialkyl tin maleate, dialkyl tin fumarate and mixtures of these wherein the alkyl group may contain 1-20 carbon atoms and a synergistic amount of from 0.001 to 0.40 percent by weight based on polymer particles, of a hindered phenolic antioxidant consisting essentially of an alkylated phenol where said alkyl groups contain from 3 to 20 carbon atome and at least one such alkyl group is in the position ortho to the Hydroxy group of the phenol, whereby the polymer molecular weight is not degraded during the aqueous impregnation process and, whereby expandable styrene polymer particles having improved molding properties are made.
Claim 2
Dependent Claim
173 words
In a process for making styrene polymer particles less flammable by impregnating the polymer particles by heating in aqueous suspension in the presence of a non-polymeric organic halogen compound and a blowing agent at temperatures between 100° C and 125° C, the improvement comprising adding, prior to heating for the impregnation, about 0.001 to 0.50 percent by weight, based on polymer particles, of a tin compound selected from the group consisting of dialkyl tin maleate, dialkyl tin fumarate and mixtures of these wherein the alkyl group may contain 1-20 carbon atoms and a synergistic amount of from 0.001 to 0.40 percent by weight based on polymer particles, of a hindered phenolic antioxidant consisting essentially of an alkylated phenol where said alkyl groups contain from 3 to 20 carbon atome and at least one such alkyl group is in the position ortho to the Hydroxy group of the phenol, whereby the polymer molecular weight is not degraded during the aqueous impregnation process and, whereby expandable styrene polymer particles having improved molding properties are made.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein said tin compound is di-n-butyl tin maleate and said antioxidant is di-tert-butyl-p-cresol.
Claim 4
Dependent Claim
30 words
The process of claim 1 wherein said hindered phenolic antioxidant is selected from the group consisting of alkylated phenols, and their bis-, tris-and higher condensation products with aldehydes and ketones.
Claim 5
Dependent Claim
28 words
The process of claim 1 wherein said alkylated phenol is selected from the group consisting of 1-naphthol; 2,6-di-tert-butyl-p-cresol; 3-tert-butyl-4-methoxyphenol; 2-tert-butyl-4-methoxyphenol; 2,6-diisopropylphenol; 2,4,6-tri-tert-butylphenol; 2,6-di(1-methylheptadecyl)-p-cresol; octadecyl 3-(3',5'-di-tert-butyl-4-hydroxyphenyl)-propionate; and mixtures thereof.
Claim 6
Dependent Claim
58 words
The process of claim 1 wherein said styrene polymer particles are selected from the group consisting of polystyrene, a copolymer of styrene with less than 50% by weight of maleic anhydride, a copolymer of styrene with less than 50% by weight of acrylonitrile, and a copolymer of styrene with less than 50% by weight of methyl acid maleate.
Claim 7
Dependent Claim
31 words
The process of claim 3 wherein the antioxidant is a bis-condensation product of alkylated phenols with an aldehyde selected from the group consisting of formaldehyde, acetaldehyde, propionaldehyde, butyraldehyde, crotonaldehyde and benzaldehyde.
Claim 8
Dependent Claim
31 words
The process of claim 3 wherein the antioxidant is a bis-condensation product of alkylated phenols with a ketone selected from the group consisting of acetone, ethyl methyl ketone and diethyl ketone.
Claim 9
Dependent Claim
42 words
The process of claim 3 wherein the antioxidant is selected from the group consisting of 2,2'-methylenebis-(4-methyl-6-tert-butylphenol); 4,4'-methylenebis (2,6-dicyclohexylphenol); 4,4'-methylenebis (2,6-ditert-butyl-phenol); 2,2'-methylenebis [6-(2-methylcyclohexyl)-p-cresol]; 4,4'-ethylidenebis (2,6-di-tert-octylphenol); 2,2'-isopropylidenebis (6-tert-butyl-p-cresol); 4,4'-butylidenebis (6-tert-butyl-m-cresol); 4,4'-cyclohexylidenebis (2-cyclohexylphenol); 1,5-naphthalenediol; 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl)butane; 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene; and tetrakis [methylene 3-(3',5'-di-tert-butyl-4'-hydroxyphenyl) propionate] methane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-11 | 1982-03-13 | 1982-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-11 | 1986-03-13 | 1986-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-11 | 1990-03-13 | 1990-09-12 | $7700.00 | Window Closed / Lapsed |