Tarnish resistant copper alloy
Assignee: Chase Brass and Copper Co Inc
•
Filing: 1977-02-17
•
Granted: 1978-09-12
•
Expires: 1997-02-17
Abstract
Abstract A copper base alloy of superior tarnish resistance consisting essentially of 7.0 to 8.5% aluminum by weight and 1.5 to 2.5% nickel by weight with the balance (89-91.5 wt %) being essentially copper. The process by which the alloy is prepared is controlled so that the alloy is primarily single phased, i.e., a face centered cubic alpha phase solid solution containing a fine dispersion of nickel aluminide compound (NiAl) and less than 2 volume percent of the brittle intermetallic phases known as beta and gamma. By composition control and by producing an essentially single phased microstructure, the alloys of the invention are capable of forming a stable oxide film having high tarnish resistance. The alloy, upon prolonged exposure indoors to ambient air and frequent handling, develops a very thin, tight, uniform oxide film which, although visible, is still attractive and does not mask the basic warm tone of the base metal. This film, when intact, serves to protect the underlying metal from further oxidation, and when damaged, is self-healing and reestablishes itself to provide a uniform protective and decorative film.
Inventors
- 👤 Richard D. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:41
CPC Classifications
C; C22; C22C; C22C9/00; C22C9/01
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
104 words
A tarnish resistant wrought copper alloy consisting essentially of the following constituents in the following amounts in percent by weight: ______________________________________
Aluminum 7.0 - 8.5
Nickel 1.5 - 2.5
Copper 89.0 - 91.5
______________________________________
and having a film resistance of at least 95 kilohms which is a measure of
the alloys tarnish resistance and a microstructure containing less than 2
volume percent of intermetallic β and γ phases said alloy
having the following minimum properties in the annealed condition, yield
strength of 46,000 psi, tensile strength of 85,000 psi, elongation of
38.5%, limiting draw ratio of 2.12 and Olsen Bulge Height of 0.413 inches.
Claim 2
Dependent Claim
104 words
A tarnish resistant wrought copper alloy consisting essentially of the following constituents in the following amounts in percent by weight: ______________________________________
Aluminum 7.0 - 8.5
Nickel 1.5 - 2.5
Copper 89.0 - 91.5
______________________________________
and having a film resistance of at least 95 kilohms which is a measure of
the alloys tarnish resistance and a microstructure containing less than 2
volume percent of intermetallic β and γ phases said alloy
having the following minimum properties in the annealed condition, yield
strength of 46,000 psi, tensile strength of 85,000 psi, elongation of
38.5%, limiting draw ratio of 2.12 and Olsen Bulge Height of 0.413 inches.
Claim 3
Dependent Claim
22 words
The alloy as set forth in claim 1 wherein the alloy also includes conventional impurities typically found in commercial copper base alloys.
Claim 4
Dependent Claim
39 words
The alloy as set forth in claim 1 wherein the alloy includes impurities selected from the group consisting of lead, tin, phosphorus, iron, manganese, zinc, silicon and mixtures thereof in a total amount of 0.5 weight percent or less.
Claim 5
Dependent Claim
20 words
An alloy as set forth in claim 1 which is characterized by a film resistance of at least 100 kilohms.
Claim 6
Dependent Claim
102 words
A tarnish resistant, wrought copper alloy consisting essentially of the following constituents in the following amounts in percent by weight: ______________________________________
Aluminum 7.7 - 8.3
Nickel 1.8 - 2.2
Copper Balance
______________________________________ and having a film resistance of at least 95 kilohms which is a measure of the alloys tarnish resistance and a microstructure containing less than 2 volume percent of intermetallic β and γ phases said alloy having the following minimum properties in the annealed condition, yield strength of 46,000 psi, tensile strength of 85,000 psi, elongation of 38.5%, limiting draw ratio of 2.12 and Olsen Bulge Height of 0.413 inches.
Claim 7
Dependent Claim
102 words
A tarnish resistant, wrought copper alloy consisting essentially of the following constituents in the following amounts in percent by weight: ______________________________________
Aluminum 7.7 - 8.3
Nickel 1.8 - 2.2
Copper Balance
______________________________________ and having a film resistance of at least 95 kilohms which is a measure of the alloys tarnish resistance and a microstructure containing less than 2 volume percent of intermetallic β and γ phases said alloy having the following minimum properties in the annealed condition, yield strength of 46,000 psi, tensile strength of 85,000 psi, elongation of 38.5%, limiting draw ratio of 2.12 and Olsen Bulge Height of 0.413 inches.
Claim 8
Dependent Claim
21 words
The alloy as set forth in claim 5 wherein the alloy also includes conventional impurities typically found in commercial base alloys.
Claim 9
Dependent Claim
39 words
The alloy as set forth in claim 5 wherein the alloy includes impurities selected from the group consisting of lead, tin, phosphorus, iron, manganese, zinc, silicon and mixtures thereof in a total amount of 0.5 weight percent or less.
Claim 10
Dependent Claim
20 words
An alloy as set forth in claim 5 which is characterized by a film resistance of at least 100 kilohms.
References Cited (Backward Citations)
US1496269A
Cited
US2210671A
Cited
US2210672A
Cited
US2210673A
Cited
US2430419A
Cited
US2715577A
Cited
US2798826A
Cited
US2870051A
Cited
US3297437A
Cited
US3259491A
Cited
US3364016A
Cited
US3341369A
Cited
US3416915A
Cited
US3402043A
Cited
US3347717A
Cited
US3901692A
Cited
US3783037A
Cited
US3923500A
Cited
US3976479A
Cited
US4016010A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-11 | 1982-03-13 | 1982-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-11 | 1986-03-13 | 1986-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-11 | 1990-03-13 | 1990-09-12 | $7700.00 | Window Closed / Lapsed |