US4112183A — Flexible resin rich epoxide-mica winding tape ins…

Claim 1

Independent Claim 266 words

A method of making a highly flexible, mica insulation winding tape sheet material comprising the steps of: (a) mixing epoxide resin selected from the group consisting of semi-solid epoxide, a mixture of solid epoxide and liquid epoxide and a mixture of semi-solid epoxide and liquid epoxide, with solvent for the epoxide resin, where the weight ratio of total epoxide:total solvent is from about 85:15 to 30:70; and then (b) mixing the epoxide resin-solvent mixture, with from 0.01 to 5.0 parts per 100 parts epoxide resin of an organo-tin compound, having a structural formula selected from the group consisting of: ##STR24## where R 1 , R 2 and R 3 are organic groups and each X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate, and dimethyl phosphate, to form a homogeneous admixture; and then (c) applying the homogeneous epoxide resin-solvent-organo-tin admixture to a flexible sheet material comprising mica, so that organo-tin compound contacts mica causing the organo-tin compound to act as a latent catalyst; and then (d) removing at least 95 weight percent of the solvent from the epoxide resin-solvent-organo-tin catalyst admixture in the sheet material without any substantial curing of the epoxide resin or reaction of the organo-tin compound, forming a flexible sheet with substantially unreacted epoxide resin and causing an increased amount of substantially unreacted organo-tin compound to contact mica in the sheet material; wherein the amount of organo-tin compound added is effective to advance the epoxide resin in the sheet material from the substantially unreacted state to a cured thermoset state upon heating over a resin-catalyst temperature of 120° C.

Claim 2

Independent Claim 266 words

A method of making a highly flexible, mica insulation winding tape sheet material comprising the steps of: (a) mixing epoxide resin selected from the group consisting of semi-solid epoxide, a mixture of solid epoxide and liquid epoxide and a mixture of semi-solid epoxide and liquid epoxide, with solvent for the epoxide resin, where the weight ratio of total epoxide:total solvent is from about 85:15 to 30:70; and then (b) mixing the epoxide resin-solvent mixture, with from 0.01 to 5.0 parts per 100 parts epoxide resin of an organo-tin compound, having a structural formula selected from the group consisting of: ##STR24## where R 1 , R 2 and R 3 are organic groups and each X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate, and dimethyl phosphate, to form a homogeneous admixture; and then (c) applying the homogeneous epoxide resin-solvent-organo-tin admixture to a flexible sheet material comprising mica, so that organo-tin compound contacts mica causing the organo-tin compound to act as a latent catalyst; and then (d) removing at least 95 weight percent of the solvent from the epoxide resin-solvent-organo-tin catalyst admixture in the sheet material without any substantial curing of the epoxide resin or reaction of the organo-tin compound, forming a flexible sheet with substantially unreacted epoxide resin and causing an increased amount of substantially unreacted organo-tin compound to contact mica in the sheet material; wherein the amount of organo-tin compound added is effective to advance the epoxide resin in the sheet material from the substantially unreacted state to a cured thermoset state upon heating over a resin-catalyst temperature of 120° C.

Claim 3

Dependent Claim 116 words

The method of claim 1 also including cooling the mica sheet after removing solvent, where in step (d), the solvent is removed by heating at a resin-solvent-catalyst temperature of up to 120° C, to form a resin saturated, mica insulation sheet that will remain tack-free at 25° C for over 6 months and which upon complete cure will provide an insulation with power factor values of below 15% at 150° C, the solvent being selected from the group consisting of ketones having from 3 to 6 total carbon atoms in the molecule, aromatic hydrocarbons and mixtures thereof, and where in steps (c) and (d), the organo-tin and mica interact to form a stable organo-tin-mica latent complex.

Claim 4

Dependent Claim 176 words

The method of claim 1 wherein the epoxide resin is selected from the group consisting of a mixture of solid epoxides and liquid epoxides, wherein the weight ratio of solid epoxide:liquid epoxide is from about 1.5:1 to 8.0:1, a mixture of semi-solid epoxides and liquid epoxides, wherein the weight ratio of semi-solid epoxide: liquid epoxide is from about 0.2:1 to 20:1, and semi-solid epoxides, the solvent is a mixture of ketone and aromatic hydrocarbon co-solvent selected from the group consisting of benzene and arene solvents and mixtures thereof, wherein the ratio of ketone:co-solvent is from about 70:30 to 30:70, and the arene is selected from the group consisting of toluene, ethylbenzene, xylene and mixtures thereof; and wherein, in step (b), mixing is carried out at temperatures of up to about 35° C, to form an admixture having a viscosity of between about 25 to 200 cps. at 25° C, and the solvent is removed in step (d) by heating at a resin-solvent catalyst temperature of between 65° to 120° C for about 1 to 10 minutes.

Claim 5

Dependent Claim 22 words

The method of claim 3, wherein about 0.05 to about 1.0 part of organo-tin is used per 100 parts of total epoxide.

Claim 6

Dependent Claim 149 words

The method of claim 3 wherein the organo-tin compound is selected from covalently bonded compounds having the structural formula selected from the group consisting of: ##STR25## where R 1 , R 2 and R 3 are selected from the group consisting of alkyl groups having from about 1 to 10 carbon atoms, aryl groups, Cl, Br or NO 2 substituted aryl groups, alkaryl groups with the alkyl constituent having from 1 to 10 carbon atoms, Cl,Br or NO 2 substituted alkaryl groups with the alkyl constituent having from about 1 to 10carbon atoms, aralkyl groups with the alkyl constituent having from about 1 to 10 carbon atoms, cyclopentane groups, cyclopentene groups, cyclopentadiene groups, cyclohexane groups, cyclohexane groups, cyclohexadiene groups, pyrrolidine groups, pyrrole groups, tetrahydrofuran groups, dioxane groups, pyridine groups and piperidine groups, and X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate and dimethyl phosphate.

Claim 7

Independent Claim 286 words

A method of making a void free, highly flexible mica insulation winding tape sheet material comprising the steps of: (a) mixing solid epoxide resin, liquid epoxide resin, and solvent selected from the group consisting of ketones having from 3 to 6 carbon atoms in the molecule, benzene, toluene, ethylbenzene, xylene and mixtures thereof; wherein the weight ratio of solid epoxide:liquid epoxide is from about 1.5:1 to 8.0:1, and the weight ratio of total epoxide:total solvent is from about 85:15 to 30:70; and then (b) mixing the epoxide resin-solvent mixture with from 0.01 to 5.0 parts per 100 parts epoxide resin of an organo-tin compound selected from the group consisting of triphenyl-tin chloride, tri-n-butyl-tin chloride, tribenzyl-tin chloride and mixtures thereof, at a temperature up to about 35° C, to form a homogeneous admixture having a viscosity of between about 25 to 200 cps. at 25° C; and then (c) applying the homogeneous epoxide resin-solvent-organo-tin admixture to a flexible sheet material comprising mica, to that organo-tin compound contacts mica causing the organo-tin compound to act as a latent catalyst; and then (d) removing at least 95 weight percent of the solvent from the epoxide resin-solvent-organo-tin catalyst admixture in the sheet material, at a resin-solvent-catalyst temperature of up to 120° C, without any substantial curing of the epoxide resin or reaction of the organo-tin compound, forming a flexible sheet with substantially unreacted epoxide resin and causing an increased amount of substantially unreacted organo-tin compound to contact mica in the sheet material; wherein the amount of organo-tin added is effective to advance the epoxide resin in the sheet material from the substantially unreacted state to a cured thermoset state upon heating at a resin-catalyst temperature of at least 120° C.

Claim 8

Independent Claim 286 words

A method of making a void free, highly flexible mica insulation winding tape sheet material comprising the steps of: (a) mixing solid epoxide resin, liquid epoxide resin, and solvent selected from the group consisting of ketones having from 3 to 6 carbon atoms in the molecule, benzene, toluene, ethylbenzene, xylene and mixtures thereof; wherein the weight ratio of solid epoxide:liquid epoxide is from about 1.5:1 to 8.0:1, and the weight ratio of total epoxide:total solvent is from about 85:15 to 30:70; and then (b) mixing the epoxide resin-solvent mixture with from 0.01 to 5.0 parts per 100 parts epoxide resin of an organo-tin compound selected from the group consisting of triphenyl-tin chloride, tri-n-butyl-tin chloride, tribenzyl-tin chloride and mixtures thereof, at a temperature up to about 35° C, to form a homogeneous admixture having a viscosity of between about 25 to 200 cps. at 25° C; and then (c) applying the homogeneous epoxide resin-solvent-organo-tin admixture to a flexible sheet material comprising mica, to that organo-tin compound contacts mica causing the organo-tin compound to act as a latent catalyst; and then (d) removing at least 95 weight percent of the solvent from the epoxide resin-solvent-organo-tin catalyst admixture in the sheet material, at a resin-solvent-catalyst temperature of up to 120° C, without any substantial curing of the epoxide resin or reaction of the organo-tin compound, forming a flexible sheet with substantially unreacted epoxide resin and causing an increased amount of substantially unreacted organo-tin compound to contact mica in the sheet material; wherein the amount of organo-tin added is effective to advance the epoxide resin in the sheet material from the substantially unreacted state to a cured thermoset state upon heating at a resin-catalyst temperature of at least 120° C.

Claim 9

Dependent Claim 19 words

A highly flexible, void free, high voltage capability insulation winding tape material made by the method of claim 6.

Claim 10

Dependent Claim 67 words

The method of claim 6, where the solvent is removed to form a resin saturated, mica insulation sheet that will remain tack-free at 25° C for over 6 months and which upon complete cure will provide an insulation with power factors values of below 15% at 150° C, and where in steps (c) and (d) the organo-tin and mica interact to form a stable organo-tin-mica latent complex.

Claim 11

Dependent Claim 191 words

A highly flexible, void free, high voltage capability, resin saturated, insulation winding tape sheet material, comprising mica and a contacting, polymerizable, 95 to 99 weight percent solids resinous composition consisting of a homogeneous mixture of substantially unreacted epoxide resin selected from the group consisting of semi-solid epoxide, a mixture of solid epoxide and liquid epoxide and a mixture of semi-solid epoxide and liquid epoxide and from 0.01 to 5.0 parts per 100 parts epoxide resin of a substantially unreacted organo-tin compound effective to cure the epoxide at resin-catalyst temperatures of at least 120° C; wherein the organo-tin compound has the structural formula selected from the group consisting of: ##STR26## where R 1 , R 2 and R 3 are organic groups and each X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate and dimethyl phosphate, said organo-tin compound contacting an interacting with mica causing the organo-tin compound to act as a latent catalyst, said flexible winding tape being capable of remaining tack-free at 25° C for over 6 months and upon complete cure will provide an insulation with power factor values of below 15% at 150° C.

Claim 12

Dependent Claim 191 words

A highly flexible, void free, high voltage capability, resin saturated, insulation winding tape sheet material, comprising mica and a contacting, polymerizable, 95 to 99 weight percent solids resinous composition consisting of a homogeneous mixture of substantially unreacted epoxide resin selected from the group consisting of semi-solid epoxide, a mixture of solid epoxide and liquid epoxide and a mixture of semi-solid epoxide and liquid epoxide and from 0.01 to 5.0 parts per 100 parts epoxide resin of a substantially unreacted organo-tin compound effective to cure the epoxide at resin-catalyst temperatures of at least 120° C; wherein the organo-tin compound has the structural formula selected from the group consisting of: ##STR26## where R 1 , R 2 and R 3 are organic groups and each X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate and dimethyl phosphate, said organo-tin compound contacting an interacting with mica causing the organo-tin compound to act as a latent catalyst, said flexible winding tape being capable of remaining tack-free at 25° C for over 6 months and upon complete cure will provide an insulation with power factor values of below 15% at 150° C.

Claim 13

Dependent Claim 31 words

The sheet material of claim 8 wrapped around an electrical conductor selected from the group consisting of copper and aluminum and cured at a resin-catalyst temperature of at least 120° C.

Claim 14

Dependent Claim 76 words

The highly flexible winding tape material of claim 9 wherein the organo-tin compound is selected from compounds having the structural formula selected from the group consisting of: ##STR27## where R 1 , R 2 and R 3 are selected from the group consisting of alkyl groups having from about 1 to 10 carbon atoms, benzyl groups and phenyl groups and X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate and dimethyl phosphate.

Claim 15

Dependent Claim 154 words

The highly flexible winding tape material of claim 11 wherein the organo-tin compound is selected from compounds having the structural formula selected from the group consisting of: ##STR28## wherein R 1 , R 2 and R 3 are selected from the group consisting of alkyl groups having from about 1 to 10 carbon atoms, aryl groups, Cl, Br or NO 2 substituted aryl groups, alkaryl groups with the alkyl constituent having from about 1 to 10 carbon atoms, Cl, Br or NO 2 substituted alkaryl groups with the alkyl constituent having from about 1 to 10 carbon atoms, aralkyl groups with the alkyl constituent having from about 1 to 10 carbon atoms, cyclopentane groups, cyclopentene groups, cyclopentadiene groups, cyclohexane groups, cyclohexane groups, cyclohexadiene groups, pyrrolidine groups, pyrrole groups, tetrahydrofuran groups, dioxane groups, pyridine groups and piperidine groups, and X is selected from the group consisting of halide, hydroxide, acetate, butyrate, propionate and dimethyl phosphate.

Claim 16

Dependent Claim 27 words

The highly flexible winding tape material of claim 8 wherein about 0.05 to about 1.0 part of organo-tin compound is used per 100 parts of total epoxide.

Claim 17

Dependent Claim 54 words

An insulated high voltage electrical apparatus comprising a metal stator having slots therein surrounding a metal rotor, conducting electrical coil windings disposed within the slots of the stator, and a body of cured resinous insulation applied to and completely impregnating the electrical coil windings, the insulation comprising the cured winding tape of claim 11.

Claim 18

Dependent Claim 55 words

The electrical apparatus of claim 14 being a generator; wherein the windings are wrapped with plural layers of mica tape, the rotor has slots therein containing conducting electrical coil windings having a body of cured resinous insulation applied to and completely impregnating the coil windings, the insulation comprising the cured winding tape of claim 11.

Claim 19

Dependent Claim 54 words

An insulated high voltage electrical apparatus comprising a metal stator having slots therein surrounding a metal armature, conducting electrical coil windings disposed within the slots of the stator, and a body of cured resinous insulation applied to and completely impregnating the electrical coil windings, the insulation comprising the cured winding tape of claim 9.

Claim 20

Dependent Claim 56 words

The electrical apparatus of claim 16 being a motor; wherein the coil windings are wrapped with plural layers of mica tape, the armature has slots therein containing conducting electrical coil windings having a body of cured resinous insulation applied to and completely impregnating the coil windings, the insulation comprising the cured winding tape of claim 11.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1981-09-04	1982-03-06	1982-09-05	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1985-09-04	1986-03-06	1986-09-05	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1989-09-04	1990-03-06	1990-09-05	$7700.00	Window Closed / Lapsed

Flexible resin rich epoxide-mica winding tape insulation containing organo-tin catalysts

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag