Method for the production of light-reflecting layers on a surface of a transparent glass article
Assignee: GLASWERK SCHOTT and GEN
•
Filing: 1972-08-21
•
Granted: 1978-09-05
•
Expires: 1992-08-21
Abstract
Abstract The invention relates to a method of producing on a transparent article, particularly a glass article, layers having a reflection degree of at least 10 percent on a first surface of the article and dereflecting layers on a second surface of the article. The method includes the steps of first by an immersion process providing both said surfaces with a dereflecting multiple-layered coating, and then providing said first surface with a single layer of a reflection increasing transparent coating.
Inventors
- 👤 Hubert Schroder
- 👤 Werner Klein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:58
CPC Classifications
B; B44; B44F; B44F1/00; B44F1/02; B44F1/04; C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3417; C03C17/3429; C03C17/3464; C03C2218/00; C03C2218/30; C03C2218/365
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
184 words
A method of making a reflecting plate having a non-reflecting surface comprising the the steps of simultaneously coating both surfaces of light permeable glass plate by sequentially (A) immersing said glass plate in an organic mixed solution containing decomposible Ti and Si compounds in an amount of equal parts by weight per unit of volume calculated as TiO 2 and SiO 2 , withdrawing said plate from said solution and drying said plate, (B) immersing the resulting glass plate in a solution of an organic titanium compound decomposible into TiO 2 , withdrawing said resulting plate from said solution and drying said resulting plate, (C) immersing the so-coated plate in a solution of organic silicon compound decomposible into SiO 2 , withdrawing the resulting plate from said solution, and drying it (D) heating the product plate to a temperature ranging from 400° to 480° to produce a hardened, anti-reflection coating which shows a reflectance curve in the visible spectral range having at least two minima, (E) and coating only the surface whose degree of reflection is to be increased with a reflection increasing coating.
Claim 2
Independent Claim
184 words
A method of making a reflecting plate having a non-reflecting surface comprising the the steps of simultaneously coating both surfaces of light permeable glass plate by sequentially (A) immersing said glass plate in an organic mixed solution containing decomposible Ti and Si compounds in an amount of equal parts by weight per unit of volume calculated as TiO 2 and SiO 2 , withdrawing said plate from said solution and drying said plate, (B) immersing the resulting glass plate in a solution of an organic titanium compound decomposible into TiO 2 , withdrawing said resulting plate from said solution and drying said resulting plate, (C) immersing the so-coated plate in a solution of organic silicon compound decomposible into SiO 2 , withdrawing the resulting plate from said solution, and drying it (D) heating the product plate to a temperature ranging from 400° to 480° to produce a hardened, anti-reflection coating which shows a reflectance curve in the visible spectral range having at least two minima, (E) and coating only the surface whose degree of reflection is to be increased with a reflection increasing coating.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said reflection increasing coating has a thickness of about one-fourth of a predetermined light wave length.
Claim 4
Dependent Claim
87 words
The method of claim 1 wherein said reflection increasing coating is applied by the steps of (A) coating one of said opposed faces with a removable protective lacquer, (B) immersing both of said opposed faces in a solution of an organic titanium compound decomposible into TiO 2 , withdrawing said so lacquered plate from said solution, and drying said so lacquered plate, (C) heating the resulting plate to a temperature sufficient to produce a hardened TiO 2 layer, and (D) removing said lacquer from said one face.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein said reflection increasing coating is applied by vacuum vapor deposition of metal.
Claim 6
Dependent Claim
23 words
The method of claim 4 wherein said metal coating is overcoated with a light transmissive SiO 2 layer for improvement of durability thereof.
Claim 7
Dependent Claim
10 words
The method of claim 5 wherein said metal is aluminum.
Claim 8
Dependent Claim
10 words
The method of claim 4 wherein said metal is aluminum.
References Cited (Backward Citations)
US2220862A
Cited
US2366516A
Cited
US2466119A
Cited
US2478385A
Cited
US3094436A
Cited
US3185020A
Cited
US3432225A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |