Claim 2

A process for improving the yield and purity of a cyclotrisiloxane of the formula, (R R' Si O).sub.3 where R is selected from the class consisting of an alkyl radical of 1 to 8 carbon atoms cycloalkyl radicals of up to 8 carbon atoms and alkenyl radicals of 2 to 8 carbon atoms and R' is a fluoroalkyl radical of 3 to 8 carbon atoms comprising adding to a diorganodihalosilane hydrolyzate or a mixture of cyclopolysiloxanes, an effective amount of an alkali metal hydroxide, and an effective amount of a promoting additive selected from the class consisting of aliphatic alcohols, salts of aliphatic alcohols and aliphatic alcohols containing aliphatic unsaturation wherein such additives have from fourteen to thirty carbon atoms, where the organo groups are the same as R and R'; and heating the resulting mixture at a temperature above 100° C.

Claim 3

The process of claim 1 wherein the cyclotrisiloxane has the formula, (CH.sub.3, CF.sub.3 CH.sub.2 CH.sub.2 SiO).sub.3.

Claim 4

The process of claim 1 wherein said diorganodihalosilane hydrolyzate is prepared by adding said diorganodihalosilanes to water where the halo is chlorine and separating the silicone hydrolyzate from the excess water and acid that is formed.

Claim 5

The process of claim 3 wherein said silicone hydrolyzate contains mixtures of cyclic siloxanes with the predominate cyclic siloxanes being the cyclotetrasiloxanes and cyclotrisiloxanes and wherein there is also present in the mixtures low and/or high molecular weight silanol terminated diorganopolysiloxanes.

Claim 6

The process of claim 1 wherein the alkali metal hydroxide is selected from the class consisting of KOH, Na OH, and Cs OH.

Claim 7

The process of claim 5 wherein the alkali metal hydroxide is present at a concentration of 0.01 to 10% by weight of the hydrolyzate.

Claim 8

The process of claim 6 wherein the alkali metal hydroxide is present at a concentration of 0.1 to 1% weight of the hydrolyzates.

Claim 9

The process of claim 1 wherein the heating temperature varies from 120° to 300° C. at lower than atmospheric pressure for a period of time varying from 3 to 48 hours.

Claim 10

The process of claim 8 wherein the heating temperature varies from 120° to 250° C. at a pressure varying from 5 mm. to 100 mm. of Hg. with a reaction period varying from 3 to 8 hours.

Claim 11

The process of claim 5 wherein the alkali metal hydroxide added to hydrolyzate is a 10% to 50% by weight of alkali metal hydroxide aqueous solution and wherein the water is removed by applying a vacuum over the hydrolyzate just prior to the heating step.

Claim 12

The process of claim 1 wherein the stabilizing additive is present at a concentration of 0.5 to 30% by weight of the hydrolyzate.

Claim 13

The process of claim 11 wherein the stabilizing additive is octadecanol and is present at a concentration of 1 to 5% by weight of the hydrolyzate.

Claim 14

The process of claim 1 wherein during said heating there is continually distilled overhead the cyclotrisiloxane in substantially pure form and at a yield of over 80%.

Claim 15

The process of claim 13 wherein after most of said hydrolyzate has been distilled over as the cyclotrisiloxane there is added additional hydrolyzate to the reaction vessel and the process is continued in a semi-continuous manner.

Claim 16

The process of claim 14 wherein two or three batches of silicone hydrolyzate can be processed with the same initial alkali metal hydroxide and stabilizing additive.

Claim 17

A process for improving the yield and purity of a cyclotrisiloxane of the formula, (R R' SiO).sub.3 where R is selected from the class consisting of an alkyl radical of 1 to 8 carbon atoms cycloalkyl radicals of up to 8 carbon atoms and alkenyl radicals of 2 to 8 carbon atoms and R' is a fluoroalkyl radical of 3 to 8 carbon atoms comprising (a) adding a diorganohalosilane to water where the organo is the same as R and R' and the halo is chlorine (b) separating the silicone hydrolyzate that is formed from excess water and acid by-products; (c) adding to said hydrolyzate from 0.01 to 10% by weight of the hydrolyzate of an alkali metal hydroxide selected from the class consisting of KOH, NaOH and Cs OH and from 0.5 to 30% by weight of the hydrolyzate of a stabilizing additive selected from the class consisting of aliphatic alcohols; salts of aliphatic alcohols and aliphatic alcohols containing aliphatic unsaturation wherein said additives have from fourteen to thirty carbon atoms, (d) heating the mixture at a temperature of from 120° to 250° C. at a pressure varying from 6 to 60 mm. of Hg. for a period of time varying from 3 to 48 hours; (e) continuously distilling overhead the substantially pure cyclotrisiloxane and obtaining said cyclotrisiloxane at yields of at least 80% by weight of said hydrolyzate and (f) adding additional hydrolyzate to the reaction mixture having the alkali metal hydroxide and stabilizing additive therein after the initial hydrolyzate has been depleted to semi-continuously recover the desired substantially pure cyclotrisiloxane.

Claim 18

A process for improving the yield and purity of a cyclotrisiloxane of the formula, (R R' SiO).sub.3 where R is selected from the class consisting of an alkyl radical of 1 to 8 carbon atoms cycloalkyl radicals of up to 8 carbon atoms and alkenyl radicals of 2 to 8 carbon atoms and R' is a fluoroalkyl radical of 3 to 8 carbon atoms comprising (a) adding a diorganohalosilane to water where the organo is the same as R and R' and the halo is chlorine (b) separating the silicone hydrolyzate that is formed from excess water and acid by-products; (c) adding to said hydrolyzate from 0.01 to 10% by weight of the hydrolyzate of an alkali metal hydroxide selected from the class consisting of KOH, NaOH and Cs OH and from 0.5 to 30% by weight of the hydrolyzate of a stabilizing additive selected from the class consisting of aliphatic alcohols; salts of aliphatic alcohols and aliphatic alcohols containing aliphatic unsaturation wherein said additives have from fourteen to thirty carbon atoms, (d) heating the mixture at a temperature of from 120° to 250° C. at a pressure varying from 6 to 60 mm. of Hg. for a period of time varying from 3 to 48 hours; (e) continuously distilling overhead the substantially pure cyclotrisiloxane and obtaining said cyclotrisiloxane at yields of at least 80% by weight of said hydrolyzate and (f) adding additional hydrolyzate to the reaction mixture having the alkali metal hydroxide and stabilizing additive therein after the initial hydrolyzate has been depleted to semi-continuously recover the desired substantially pure cyclotrisiloxane.