Synergistic fire retardant additives for plasticized polyvinyl chloride consisting essential of boric acid and zinc oxide or zinc phosphate
Assignee: Motors Liquidation Co
•
Filing: 1977-07-25
•
Granted: 1978-09-05
•
Expires: 1997-07-25
Abstract
Abstract In a preferred embodiment, polyvinyl chloride resin plasticized with aliphatic carboxylic acid esters is imparted with superior flame and fire retardancy by a synergistic fire retarding additive. The additives of the invention comprise boric acid in combination with zinc oxide and/or zinc phosphate. These constituents together provide greater fire retardancy to the plasticized PVC than the sum of the effects of each constituent employed alone.
Inventors
- 👤 Ismat A. Abu-Isa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 17:31
CPC Classifications
C; C08; C08K; C08K13/00; C08K13/02; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/32; C08K3/38; C08K5/00; C08K5/04; C08K5/10
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
105 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and a fire retarding additive mixed therewith, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, said boric acid and said component being added in such relative amounts that the fire retarding effect provided to the composition thereby is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
Claim 2
Dependent Claim
105 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and a fire retarding additive mixed therewith, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, said boric acid and said component being added in such relative amounts that the fire retarding effect provided to the composition thereby is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
Claim 3
Dependent Claim
122 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and mixed therewith at least 3 parts by weight of a fire retarding additive per 100 parts by weight of said polyvinyl chloride resin, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, said boric acid and said component being added in such relative amounts that the fire retarding effect provided to the composition thereby is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
Claim 4
Dependent Claim
122 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and mixed therewith at least 3 parts by weight of a fire retarding additive per 100 parts by weight of said polyvinyl chloride resin, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, said boric acid and said component being added in such relative amounts that the fire retarding effect provided to the composition thereby is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
Claim 5
Dependent Claim
133 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and mixed therewith at least 3 parts by weight of a fire retarding additive per 100 parts by weight of said polyvinyl chloride resin, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, the weight ratio of the boric acid to said component being in the range of from about 2:1 to 1:2 such that the fire retarding effect provided to the composition by said additive is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
Claim 6
Dependent Claim
133 words
A fire retardant plasticized polyvinyl chloride composition comprising polyvinyl chloride resin, an aliphatic dicarboxylic acid ester plasticizer, and mixed therewith at least 3 parts by weight of a fire retarding additive per 100 parts by weight of said polyvinyl chloride resin, said additive consisting essentially of boric acid and a component selected from the group consisting of zinc oxide and zinc phosphate, the weight ratio of the boric acid to said component being in the range of from about 2:1 to 1:2 such that the fire retarding effect provided to the composition by said additive is greater as measured by the limiting oxygen index determined by ASTM D2863 than the sum of the fire retarding effects provided by each component alone to a like composition of said polyvinyl chloride resin and said plasticizer.
References Cited (Backward Citations)
US2617783A
Cited
US2949439A
Cited
US3131164A
Cited
US3375209A
Cited
US3524761A
Cited
US3718615A
Cited
US3945974A
Cited
US3933742A
Cited
US3965068A
Cited
US3957723A
Cited
US4076682A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |