Foundry processes and compositions

Claim 1

A method of making a foundry mold or core comprising forming a fluid mixture comprising foundry sand and a foamed aqueous phase comprising resin condensate, said resin condensate being an oligomeric form of formaldehyde with one or more of furfuryl alcohol phenol and urea, surfactant foaming agent, acidic curing agent and a silane, said silane having the general formula R'Si(OR) 3 in which R' is a C 2 -C 6 alkylene group bonded to an amino, epoxy, mercapto, hydroxy, hydroxy-C 1 -C 6 alkylamino, amino-C 1 -C 6 alkylamino, C 2 -C 6 alkenyl or C 2 -C 6 alkenyl-carboxy group and the groups R may be the same or different and are selected from C 1 -C 6 alkyl and C 1 -C 6 alkoxy-substituted-C 1 -C 6 alkyl, pouring the composition while fluid into a mould or core box which is immobile, and allowing the fluid composition to set without vibration of the mould or core box or ramming of the fluid mixture or other consolidation techniques, in which process the amount of silane is from 0.05 to 0.5% by weight based on the weight of silane and resin condensate, and the total amount of water in the mixture is less than 2% by weight of the mixture but is more than the minimum necessary to cause foaming of the aqueous phase to render the mixture fluid and in which the foamed aqueous phase retains its foamed structure until setting starts.

Claim 2

A method of making a foundry mold or core comprising forming a fluid mixture comprising foundry sand and a foamed aqueous phase comprising resin condensate, said resin condensate being an oligomeric form of formaldehyde with one or more of furfuryl alcohol phenol and urea, surfactant foaming agent, acidic curing agent and a silane, said silane having the general formula R'Si(OR) 3 in which R' is a C 2 -C 6 alkylene group bonded to an amino, epoxy, mercapto, hydroxy, hydroxy-C 1 -C 6 alkylamino, amino-C 1 -C 6 alkylamino, C 2 -C 6 alkenyl or C 2 -C 6 alkenyl-carboxy group and the groups R may be the same or different and are selected from C 1 -C 6 alkyl and C 1 -C 6 alkoxy-substituted-C 1 -C 6 alkyl, pouring the composition while fluid into a mould or core box which is immobile, and allowing the fluid composition to set without vibration of the mould or core box or ramming of the fluid mixture or other consolidation techniques, in which process the amount of silane is from 0.05 to 0.5% by weight based on the weight of silane and resin condensate, and the total amount of water in the mixture is less than 2% by weight of the mixture but is more than the minimum necessary to cause foaming of the aqueous phase to render the mixture fluid and in which the foamed aqueous phase retains its foamed structure until setting starts.

Claim 8

A method of making a foundry mould or core comprising forming a fluid mixture comprising foundry sand and a foamed aqueous phase comprising 1 to 5% of an aqueous resin condensate containing 1 to 30% water and an oligomeric form of formaldehyde with one or more of furfuryl alcohol, phenol and urea, 0.05 to 0.5% by weight based on the weight of the aqueous resin condensate of a silane which has the general formula R'Si(OR) 3 in which R' is a C 2 -C 6 alkylene group bonded to an amino, epoxy, mercapto, hydroxy, hydroxy-C 1 -C 6 alkylamino, amino-C 1 -C 6 alkylamino, C 2 -C 6 alkylene or C 2 -C 6 alkenyl-carboxy group and the groups R may be the same or different and are selected from C 1 -C 6 alkyl and C 1 -C 6 alkoxy-substituted-C 1 -C 6 alkyl, and sufficient sodium lauryl ether sulphate to render the foam stable, in which the fluid mixture has a total water content of 1 to 2% and is poured into a mould or core box and allowed to set without vibration, ramming or other consolidation technique, wherein the foamed phase retains its foamed structure until setting starts.

Claim 9

A method of making a foundry mould or core comprising forming a fluid mixture comprising foundry sand and a foamed aqueous phase comprising 1 to 5% of an aqueous resin condensate containing 1 to 30% water and an oligomeric form of formaldehyde with one or more of furfuryl alcohol, phenol and urea, 0.05 to 0.5% by weight based on the weight of the aqueous resin condensate of a silane which has the general formula R'Si(OR) 3 in which R' is a C 2 -C 6 alkylene group bonded to an amino, epoxy, mercapto, hydroxy, hydroxy-C 1 -C 6 alkylamino, amino-C 1 -C 6 alkylamino, C 2 -C 6 alkylene or C 2 -C 6 alkenyl-carboxy group and the groups R may be the same or different and are selected from C 1 -C 6 alkyl and C 1 -C 6 alkoxy-substituted-C 1 -C 6 alkyl, and sufficient sodium lauryl ether sulphate to render the foam stable, in which the fluid mixture has a total water content of 1 to 2% and is poured into a mould or core box and allowed to set without vibration, ramming or other consolidation technique, wherein the foamed phase retains its foamed structure until setting starts.