Dual coat ceramic layer prepared by single firing
Assignee: Vibrantz Corp
•
Filing: 1976-10-28
•
Granted: 1978-08-29
•
Expires: 1996-10-28
Abstract
Abstract A process and resulting product are disclosed characterized by superimposing two layers of essentially dry, differing frit compositions onto a substrate and then firing only once to form a dual coat coherent ceramic layer. The composition of the two frits is such that the first or base coat fuses and stabilizes during the firing operation at temperatures below that at which the second or cover coat fuses and stabilizes. Desirably, the first layer forms an amorphous glass adherent to the substrate that is predominantly an alkaline oxide borosilicate glass and preferably an alkaline borofluorosilicate glass.
Inventors
- 👤 Richard G. Rion
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:46
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/02; C03C8/04; C03C8/06; C03C8/08; C03C8/10; C03C8/12; C23; C23D; C23D5/00; C23D5/04; C03C2205/00; C03C2205/04; C03C2207/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
179 words
A process for applying a dual coat ceramic layer to a substrate in a single firing operation, comprising applying to the substrate a first coat of an essentially dry powder of a first frit composition adapted to form a glass adherent to said substrate, applying to said first coat a second coat of an essentially dry powder of a second frit composition normally not adapted as a glass to adhere to said substrate, subjecting said substrate and coats to a single firing operation, initially fusing and completely stabilizing said first frit composition within a temperature range below that at which said second frit composition first fuses and stabilizes, then fusing and stabilizing said second frit composition within a temperature range higher than said first temperature range, whereby said first coat reaches a state of neither tension nor compression at a temperature below that at which said second coat first reaches a state of neither tension nor compression, and finally cooling to form a coherent ceramic layer of two substantially continuous coats on said substrate from the two frit compositions.
Claim 2
Dependent Claim
179 words
A process for applying a dual coat ceramic layer to a substrate in a single firing operation, comprising applying to the substrate a first coat of an essentially dry powder of a first frit composition adapted to form a glass adherent to said substrate, applying to said first coat a second coat of an essentially dry powder of a second frit composition normally not adapted as a glass to adhere to said substrate, subjecting said substrate and coats to a single firing operation, initially fusing and completely stabilizing said first frit composition within a temperature range below that at which said second frit composition first fuses and stabilizes, then fusing and stabilizing said second frit composition within a temperature range higher than said first temperature range, whereby said first coat reaches a state of neither tension nor compression at a temperature below that at which said second coat first reaches a state of neither tension nor compression, and finally cooling to form a coherent ceramic layer of two substantially continuous coats on said substrate from the two frit compositions.
Claim 3
Dependent Claim
18 words
The process of claim 1 in which said substrate is a carbon-rich metallic substrate adapted for porcelain enameling.
Claim 4
Dependent Claim
22 words
The process of claim 1 in which said firing operation is within the range of about 1300° F to about 1600° F.
Claim 5
Dependent Claim
17 words
The process of claim 1 in which said first frit composition forms an alkaline oxide borosilicate glass.
Claim 6
Dependent Claim
40 words
The process of claim 1 in which said first frit compositions forms an alkaline oxide borosilicate glass comprising in weight percent: B 2 o 3 : 8 to 25% SiO 2 : 20 to 50% Alkaline Oxide: 15 to 40%
Claim 7
Dependent Claim
17 words
The process of claim 1 in which said first frit composition forms an alkaline oxide borofluorosilicate glass.
Claim 8
Dependent Claim
60 words
The process of claim 1 in which said first frit composition forms an alkaline oxide borofluorosilicate glass comprising in weight percent: Alkaline Oxide: 12 to 30% Boron Oxide: 10 to 30% Fluorine: 0.1 to 10% Silica: 20 to 50% said fluorine being present as a fluoride of at least one metal of the glass replacing an equivalent amount of oxygen.
Claim 9
Dependent Claim
59 words
The process of claim 1 in which said first frit composition forms an alkaline borofluorosilicate glass comprising in weight percent: Alkaline Oxide: 15 to 26% Boron Oxide: 12 to 20% Fluorine: 0.5 to 5% Silica: 25 to 40% said fluorine being present as a fluoride of at least one metal of the glass replacing an equivalent amount of oxygen.
Claim 10
Dependent Claim
147 words
The process of claim 1 in which said first frit composition forms a glass comprising in weight percent 55% to about 95% of an alkaline borofluorosilicate glass and from about 5% to about 45% of additives, said borofluorosilicate glass comprising in weight percent: Alkaline Oxide: 12 to 30% Boron Oxide: 10 to 30% Fluorine: 0.1 to 10% Silica: 20 to 50% said fluorine being present as a fluoride of at least one metal of the glass replacing an equivalent amount of oxygen, and said additives comprising in weight percent: Cobalt Oxide: 0 to 7% Nickel Oxide: 0 to 7% Manganese Oxide: 0 to 7% Iron Oxide: 0 to 3% Aluminum Oxide: 0 to 15% Zirconium Oxide: 0 to 25% Zinc Oxide: 0 to 10% P 2 o 5 : 0 to 5% Calcium Oxide: 0 to 15% Cesium Oxide: 0 to 5% Strontium Oxide: 0 to 3%
Claim 11
Dependent Claim
42 words
The process of claim 9 in which said first frit composition forms a glass comprising in weight percent from about 60% to about 80% by weight of said borofluorosilicate glass and from about 20% to about 40% by weight of said additives.
Claim 12
Dependent Claim
143 words
The process of claim 1 in which said second frit composition forms a glass comprising in weight percent: Al 2 O 3 : 0 to 20% BaO: 0 to 20% B 2 o 3 : 0 to 30% CaO: 0 to 30% K 2 o: 0 to 20% Li 2 O: 0 to 15% Na 2 O: 0 to 20% P 2 o 5 : 0 to 20% Sb 2 O 3 : 0 to 30% SiO 2 : 10 to 60% TiO 2 : 0 to 30% ZnO: 0 to 20% F: 0 to 10% Metal Oxides: 10 to 70% said fluorine being present as a fluoride of at least one metal of the glass replacing an equivalent amount of oxygen, and the metal of said metal oxides being selected from the group consisting of copper, cobalt, manganese, chromium, and mixtures thereof.
Claim 13
Dependent Claim
45 words
The process of claim 1 in which said first frit composition fuses and stabilizes in a temperature range of about 1100° F to about 1600° F, and second frit composition fuses and stabilizes in a temperature range of about 1200° F to about 1650° F.
Claim 14
Dependent Claim
49 words
The process of claim 1 in which prior to said firing step the layer of the first frit composition has a thickness of about 0.4 mil to about 8 mils, and the layer of the second frit composition has a thickness from about 8 mils to about 30 mils.
Claim 15
Dependent Claim
23 words
The process of claim 1 in which at least one of said powders is completely dry and is applied to the substrate electrostatically.
Claim 16
Dependent Claim
21 words
The process of claim 1 in which both of said powders are completely dry and are applied to the substrate electrostatically.
Claim 17
Dependent Claim
131 words
A process for applying a dual coat ceramic layer to a substrate in a single firing operation, comprising applying to the substrate a first coat of an essentially dry powder of a first frit composition adapted to form a glass adherent to said substrate, applying to said first coat a second coat of an essentially dry powder of a second frit composition normally not adapted as a glass to adhere to said substrate, subjecting said substrate and coats to a single firing operation, sequentially fusing and completely stabilizing in turn said first frit composition within a first temperature range and then said second frit composition at a second and higher temperature range, and then cooling to form a dual coat coherent ceramic layer on said substrate from the two frit compositions.
Claim 18
Dependent Claim
131 words
A process for applying a dual coat ceramic layer to a substrate in a single firing operation, comprising applying to the substrate a first coat of an essentially dry powder of a first frit composition adapted to form a glass adherent to said substrate, applying to said first coat a second coat of an essentially dry powder of a second frit composition normally not adapted as a glass to adhere to said substrate, subjecting said substrate and coats to a single firing operation, sequentially fusing and completely stabilizing in turn said first frit composition within a first temperature range and then said second frit composition at a second and higher temperature range, and then cooling to form a dual coat coherent ceramic layer on said substrate from the two frit compositions.
References Cited (Backward Citations)
US1459357A
Cited
US1898500A
Cited
US2864721A
Cited
US3086880A
Cited
US3216847A
Cited
US3513012A
Cited
GB1236614A
Cited
FR1582316A
Cited
US3647509A
Cited
US3671278A
Cited
US3928668A
Cited
US3930062A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |