US4110414A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermoplastic polymer blends of ethylene-propylene (EP) copolymer with polyethylene
Assignee: Goodrich Corp
•
Filing: 1976-09-01
•
Granted: 1978-08-29
•
Expires: 1996-09-01
Abstract
Abstract Polymer blends of (1) high molecular weight ethylene-propylene (EP) copolymers having a high methylene run index with (2) low density polyethylenes are prepared by physically mixing the polymer components under conditions of heat and shear. The resultant blends are thermoplastic in nature and readily moldable and remoldable. The blends exhibit exceptionally high tensile strength without the use of curing or crosslinking agents. Products made from the polymer blends include liners and molded products such as tubing, toys, and household and automotive items.
Inventors
- 👤 Geoffrey A. Lindsay
- 👤 Paul T. Stricharczuk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:35
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L23/16
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
97 words
A thermoplastic polymer blend comprising (1) an EP copolymer consisting essentially of interpolymerized units of about 65 to about 75 percent by weight of ethylene and about 25 percent to about 35 percent by weight of propylene, said polymer having a Mooney Viscosity (ML-4 at 150° C.) of from about 30 to about 80 and a methylene run index of over about 20/1 and (2) from about 5 parts to about 200 parts by weight per 100 parts by weight of the EP copolymer of a polyethylene polymer having a density of about 0.91 to 0.94 grams/cc.
Claim 2
Dependent Claim
97 words
A thermoplastic polymer blend comprising (1) an EP copolymer consisting essentially of interpolymerized units of about 65 to about 75 percent by weight of ethylene and about 25 percent to about 35 percent by weight of propylene, said polymer having a Mooney Viscosity (ML-4 at 150° C.) of from about 30 to about 80 and a methylene run index of over about 20/1 and (2) from about 5 parts to about 200 parts by weight per 100 parts by weight of the EP copolymer of a polyethylene polymer having a density of about 0.91 to 0.94 grams/cc.
Claim 3
Dependent Claim
33 words
A thermoplastic polymer blend of claim 1 wherein the polyethylene polymer is present in from about 10 parts to about 100 parts by weight per 100 parts by weight of the EP copolymer.
Claim 4
Dependent Claim
23 words
A thermoplastic polymer blend of claim 2 wherein the EP polymer has a methylene run index of from about 22/1 to about 40/1.
Claim 5
Dependent Claim
22 words
A thermoplastic polymer blend of claim 3 wherein the EP copolymer has a Mooney Viscosity of from about 40 to about 70.
Claim 6
Dependent Claim
74 words
A thermoplastic polymer blend of claim 4 comprising (1) an EP copolymer consisting essentially of interpolymerized units of about 72 percent by weight of ethylene and about 28 percent by weight of propylene, and having a methylene run index of about 39, and (2) from about 10 parts to about 100 parts by weight per 100 parts by weight of the EP copolymer, of a polyethylene polymer having a density of about 0.92 gram/cc.
Claim 7
Dependent Claim
74 words
A thermoplastic polymer blend of claim 4 comprising (1) an EP copolymer consisting essentially of interpolymerized units of about 68 percent by weight of ethylene and about 32 percent by weight of propylene, and having a methylene run index of about 29, and (2) from about 10 parts to about 100 parts by weight per 100 parts by weight of the EP copolymer, of a polyethylene polymer having a density of about 0.92 gram/cc.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |