Pigmented air drying latex paints having superior gloss
Assignee: Sherwin Williams Co
•
Filing: 1977-06-06
•
Granted: 1978-08-29
•
Expires: 1997-06-06
Abstract
Abstract A high gloss, water base, pigmented latex is provided by grinding a pigment into a water-free solution of a carboxyl-functional addition solution copolymerized copolymer of monoethylenically unsaturated monomers including at least about 10% by weight of monoethylenically unsaturated carboxylic acid in water miscible alcoholic organic solvent, the copolymer being at least partially neutralized at the time of grinding with an hydroxy amine, to render the said copolymer dispersible in water, and thereby form a nonaqueous pigment paste, and then mixing the nonaqueous pigment paste with an air drying aqueous latex of aqueous emulsion copolymerized copolymer particles. The invention includes the latex paint so-produced.
Inventors
- 👤 Kazys Sekmakas
- 👤 Kenneth K. Hesler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:12
CPC Classifications
C; C09; C09D; C09D157/00; C09D157/06; C09D157/10; C08; C08K; C08K3/00; C08K3/01; C08K3/013; C08K3/18; C08K3/20; C08K3/22; C09D133/00; C09D133/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
167 words
A method of producing a high gloss, air drying water base, pigmented latex paint comprising, grinding 3-12 parts of pigment into a water-free solution containing 1 part of an at least partially neutralized carboxyl-functional addition solution copolymerized copolymer of 10% to 40% of monoethylenically unsaturated carboxylic acid, the major proportion of said pigment being titanium dioxide and said solution containing 40% to 70% of alcoholic organic solvent based on the weight of the solution copolymer, said copolymer being at least partially neutralized with an hydroxy amine having the formula: ##STR2## in which R is hydrogen or an alkyl group, R' is an alkylene group, and X is either R or R'OH, to render the said copolymer dispersible in water, and thereby form a nonaqueous pigment paste, and then mixing the nonaqueous pigment paste with an air drying aqueous latex consisting essentially of emulsified aqueous emulsion copolymer particles having a T g below 20° C., the copolymer of said latex containing less than about 4% of reactive monomers.
Claim 2
Independent Claim
167 words
A method of producing a high gloss, air drying water base, pigmented latex paint comprising, grinding 3-12 parts of pigment into a water-free solution containing 1 part of an at least partially neutralized carboxyl-functional addition solution copolymerized copolymer of 10% to 40% of monoethylenically unsaturated carboxylic acid, the major proportion of said pigment being titanium dioxide and said solution containing 40% to 70% of alcoholic organic solvent based on the weight of the solution copolymer, said copolymer being at least partially neutralized with an hydroxy amine having the formula: ##STR2## in which R is hydrogen or an alkyl group, R' is an alkylene group, and X is either R or R'OH, to render the said copolymer dispersible in water, and thereby form a nonaqueous pigment paste, and then mixing the nonaqueous pigment paste with an air drying aqueous latex consisting essentially of emulsified aqueous emulsion copolymer particles having a T g below 20° C., the copolymer of said latex containing less than about 4% of reactive monomers.
Claim 3
Dependent Claim
27 words
A method as recited in claim 1 in which said hydroxy amine is a tertiary amine and said R and R' groups contain from 1-4 carbon atoms.
Claim 4
Dependent Claim
16 words
A method as recited in claim 2 in which said hydroxy amine is dimethyl ethanol amine.
Claim 5
Dependent Claim
22 words
A method as recited in claim 1 in which said solution copolymer contains from 15% to 30% of monoethylenically unsaturated carboxylic acid.
Claim 6
Dependent Claim
38 words
A method as recited in claim 1 in which said solution copolymer and said aqueous emulsion copolymer each include more than 50% by weight of a blend of methyl methacrylate and C 1 - C 8 alkyl acrylate.
Claim 7
Dependent Claim
32 words
A method as recited in claim 1 in which from 5-10 parts of pigment are ground into said water free solution containing 1 part of said at least partially neutralized solution copolymer.
Claim 8
Dependent Claim
21 words
A method as recited in claim 6 in which said alcoholic organic solvent consists essentially of 2-ethoxy ethanol and 2-butoxy ethanol.
Claim 9
Dependent Claim
46 words
A method as recited in claim 1 in which said aqueous emulsion copolymer consists of a blend of methyl methacrylate and C 2 - C 4 alkyl acrylate, up to about 1% of monoethylenic carboxylic acid and up to about 2% of a monoethylenic amine-functional monomer.
Claim 10
Dependent Claim
17 words
The high gloss, water base, pigmented air drying latex paint produced by the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |