Expandable ethylenically unsaturated polymer particle compositions
Assignee: Sekisui Kaseihin Kogyo KK
•
Filing: 1975-07-17
•
Granted: 1978-08-29
•
Expires: 1995-07-17
Abstract
Abstract Expandable ethylenically unsaturated polymer particle compositions containing an expanding agent, said polymer particles having the surfaces thereof coated with a layer of a compound comprising calcium carbonate having a particle size of from 0.02 to 0.2 microns and the surfaces of said calcium carbonate particles having chemically attached thereto organic compounds selected from the group consisting of higher fatty acids, resin acid, lignin sulfonic acid and mixtures thereof.
Inventors
- 👤 Toshiki Ikeda
- 👤 Yoshitsugu Beppu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:19
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/22; C08J9/224
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
159 words
Expandable ethylenically unsaturated polymer particle compositions which can be pre-expanded and molded to form cellular shaped articles, which comprises ethylenically unsaturated polymer particles containing an expanding agent, said particles having the surfaces thereof coated with a layer of a compound comprising calcium carbonate, said compound having a particle size of from 0.02 to 0.2 microns and the surfaces of said calcium carbonate particles having chemically attached thereto an organic compound selected from the group consisting of higher fatty acids, resin acid, lignin sulfonic acid and alkaline metal salts thereof and mixtures thereof, said organic compound being present in an amount of from 0.5 to 6 parts by weight per 100 parts by weight of calcium carbonate, and said calcium carbonate compound being present in the amount of from 0.005% to 0.3% by weight of said polymer particles, whereby said polymer particles are substantially free of lumping or agglomerating during pre-expansion and are capable of being easily fused when molded.
Claim 2
Dependent Claim
159 words
Expandable ethylenically unsaturated polymer particle compositions which can be pre-expanded and molded to form cellular shaped articles, which comprises ethylenically unsaturated polymer particles containing an expanding agent, said particles having the surfaces thereof coated with a layer of a compound comprising calcium carbonate, said compound having a particle size of from 0.02 to 0.2 microns and the surfaces of said calcium carbonate particles having chemically attached thereto an organic compound selected from the group consisting of higher fatty acids, resin acid, lignin sulfonic acid and alkaline metal salts thereof and mixtures thereof, said organic compound being present in an amount of from 0.5 to 6 parts by weight per 100 parts by weight of calcium carbonate, and said calcium carbonate compound being present in the amount of from 0.005% to 0.3% by weight of said polymer particles, whereby said polymer particles are substantially free of lumping or agglomerating during pre-expansion and are capable of being easily fused when molded.
Claim 3
Dependent Claim
70 words
The composition of claim 1, wherein the expanding agent is a hydrocarbon which does not dissolve or may slightly swell the said ethylenically unsaturated polymer particles, and has a boiling point lower than the softening point of the said ethylenically unsaturated polymer particles and is selected from the group consisting of propane, n-butane, isobutane, n-pentane, neopentane, isopentane, n-hexane, cyclopentane, cyclohexane, dichlorofluomethane, chlorotrifluoromethane, dichlorofluoromethane, chlorodifluoromethane, trichlorofluoromethane, methyl chloride and ethyl chloride.
Claim 4
Dependent Claim
33 words
The composition of claim 1, wherein the expanding agent is impregnated into the ethylenically unsaturated polymer particles in an amount of from 2 to 15 % by weight of the said polymer particles.
Claim 5
Dependent Claim
34 words
The composition of claim 1, wherein the ethylenically unsaturated polymer particles are polymer particles prepared by the polymerization of a vinyl monomer selected from the group consisting of styrene, methyl methacrylate and ethyl methacrylate.
Claim 6
Dependent Claim
61 words
The composition of claim 1, wherein the ethylenically unsaturated polymer particles are copolymer particles prepared by the copolymerization of a vinyl monomer selected from the group consisting of styrene, methyl methacrylate and ethyl methacrylate with a copolymerizable monomer selected from the group consisting of methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, ethyl methacrylate, acrylonitrile, α-methylstyrene, divinylbenzene, 1,3-butadiene and vinyl acetate.
Claim 7
Dependent Claim
28 words
The composition of claim 1, wherein the ethylenically unsaturated polymer particles are polymer particles selected from cross-linked ethylene polymer particles and copolymer particles prepared from ethylene and styrene.
Claim 8
Dependent Claim
48 words
The composition of claim 1, wherein the higher fatty acids having from 10 to 20 carbon atoms are compounds selected from the group consisting of capric acid, lauric acid, myristic acid, palmitic acid, stearic acid, palmitoic acid, oleic acid, linolic acid, linolenic acid and alkaline metal salts thereof.
Claim 9
Dependent Claim
31 words
The composition of claim 1, wherein the resin acid is a compound which contains abietic acid, neoabietic acid, dihydroabietic acid, d-primaric acid, levo-pimaric acid, mixtures thereof and alkaline metal salts thereof.
Claim 10
Dependent Claim
55 words
The composition of claim 1, wherein the calcium carbonate has a particle size of from 0.02 to 0.2 microns in diameter and the surfaces of said calcium carbonate particles have chemically attached thereto organic compounds selected from the group consisting of higher fatty acids having from 10 to 20 carbon atoms and sodium salts thereof.
Claim 11
Dependent Claim
47 words
The composition of claim 1, wherein the calcium carbonate has a particle size of from 0.02 to 0.2 microns in diameter and the surfaces of said calcium carbonate particles have chemically attached thereto organic compounds selected from the group consisting of resin acids and sodium salts thereof.
Claim 12
Dependent Claim
30 words
The composition of claim 1, wherein the organic compound is used in an amount of from 1 to 5 parts by weight per 100 parts by weight of calcium carbonate.
Claim 13
Dependent Claim
41 words
The composition of claim 1, wherein the calcium carbonate particles having chemically attached thereto an organic compound are used in an amount of from 0.005 to 0.3 parts by weight per 100 parts by weight of the ethylenically unsaturated polymer particles.
Claim 14
Dependent Claim
34 words
The composition of claim 12, wherein the calcium carbonate particles are used in an amount of from 0.01 to 0.1 parts by weight per 100 parts by weight of the ethylenically unsaturated polymer particles.
Claim 15
Dependent Claim
56 words
A process for the preparation of expandable ethylenically unsaturated polymer particle compositions which comprises coating onto the surfaces of an expandable ethylenically unsaturated polymer particles containing an expanding agent calcium carbonate particles having chemically attached to the surfaces thereof organic compounds selected from the group consisting of higher fatty acids, resin acids and lignin sulfonic acids.
Claim 16
Dependent Claim
56 words
A process for the preparation of expandable ethylenically unsaturated polymer particle compositions which comprises coating onto the surfaces of an expandable ethylenically unsaturated polymer particles containing an expanding agent calcium carbonate particles having chemically attached to the surfaces thereof organic compounds selected from the group consisting of higher fatty acids, resin acids and lignin sulfonic acids.
Claim 17
Dependent Claim
23 words
The process of claim 14, wherein the calcium carbonate particles are prepared by introducing carbon dioxide into a suspension medium containing calcium hydroxide.
Claim 18
Dependent Claim
36 words
The process of claim 14, wherein the calcium carbonate particles having chemically attached to the surfaces thereof organic compounds are prepared by introducing carbon dioxide into a suspension medium containing calcium hydroxide and an organic compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |