Method for the manufacture of glass
Assignee: Saint Gobain Industries SA
•
Filing: 1977-03-28
•
Granted: 1978-08-29
•
Expires: 1997-03-28
Abstract
Abstract This invention relates to a process and an apparatus for the manufacture of fused glass, suitable for molding, wherein the total time of manufacture is reduced to about one hour. The process accelerates the homogenization and refining of glass by eliminating unfused particles and gas bubbles which are the main factors limiting the production rate of industrial glass. This is accomplished by increasing the temperature of the molten glass to produce foaming throughout its mass while maintaining its viscosity below 1,000 poises.
Inventors
- 👤 Francois E. Chevallier
- 👤 Jean M. P. Fenouillet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:03
CPC Classifications
C; C03; C03B; C03B5/00; C03B5/16; C03B5/173; C03B3/00; C03B3/02; C03B3/023; C03B5/12; C03B5/18; C03B5/183; C03B5/185; C03B5/225; C03B5/235; C03B5/2353; C03C; C03C1/00; C03C1/004; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y10; Y10S; Y10S65/00; Y10S65/04
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
93 words
A process for the manufacture of glass from a foamable vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume while maintaining its viscosity below about 1000 poises; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 2
Dependent Claim
93 words
A process for the manufacture of glass from a foamable vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume while maintaining its viscosity below about 1000 poises; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 3
Dependent Claim
28 words
The process of claim 1 wherein: (a) the expansion of the molten mass is between about 2 and 3 times its normal volume in the unfoamed molten state.
Claim 4
Dependent Claim
17 words
The process of claim 1 wherein: (a) the progress of the molten mass occurs without return flow.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein: (a) the vitrifiable material is sintered.
Claim 6
Dependent Claim
18 words
The process of claim 4 wherein: (a) the vitrifiable material is prepared by subjecting it to rapid melting.
Claim 7
Dependent Claim
14 words
The process of claim 5 wherein: (a) the melting takes less than 10 minutes.
Claim 8
Dependent Claim
20 words
The process of claim 6 wherein: (a) the vitrifiable mixture is in the form of granules, balls, pellets or strips.
Claim 9
Dependent Claim
29 words
The process of claim 7 wherein: (a) the thickness of the layer of vitrifiable material during melting is the size of the smallest of the sintered elements undergoing melting.
Claim 10
Dependent Claim
129 words
A process for the manufacture of glass from a vitrifiable material containing a foaming and refining agent which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises; (b) foaming the molten mass throughout its volume while maintaining its viscosity below about 1000 poises by heating the molten mass to increase its temperature at the rate of at least about 20° C per minute from a temperature just below the foaming temperature; (c) continuing the foaming until the material has been expanded to at least 1.5 times its initial molten volume; (d) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (e) recovering the fused liquid glass.
Claim 11
Dependent Claim
129 words
A process for the manufacture of glass from a vitrifiable material containing a foaming and refining agent which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises; (b) foaming the molten mass throughout its volume while maintaining its viscosity below about 1000 poises by heating the molten mass to increase its temperature at the rate of at least about 20° C per minute from a temperature just below the foaming temperature; (c) continuing the foaming until the material has been expanded to at least 1.5 times its initial molten volume; (d) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (e) recovering the fused liquid glass.
Claim 12
Dependent Claim
24 words
The process of claim 9 wherein: (a) the solubility of the gas forming the foam in the molten glass increases as the temperature decreases.
Claim 13
Dependent Claim
21 words
The process of claim 10 wherein: (a) at least one of the foaming agents is a refining compound soluble in glass.
Claim 14
Dependent Claim
26 words
The process of claim 1 wherein: (a) the foaming agent is selected from the group consisting of sodium sulfate, potassium chloride, antimony trioxide and arsenic trioxide.
Claim 15
Dependent Claim
108 words
A process for the manufacture of glass from a foamable vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises and wherein said molten mass contains a number of solid or gaseous nuclei favoring foaming; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume while maintaining its viscosity below about 1000 poises; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at at viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 16
Dependent Claim
108 words
A process for the manufacture of glass from a foamable vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a viscosity below about 1000 poises and wherein said molten mass contains a number of solid or gaseous nuclei favoring foaming; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume while maintaining its viscosity below about 1000 poises; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at at viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 17
Dependent Claim
27 words
The process of claim 13 wherein: (a) the nuclei are distributed throughout the vitreous mass at a concentration of at least about 10 visible nuclei per cc.
Claim 18
Dependent Claim
17 words
The process of claim 14 wherein: (a) cullet or colored cullet is added to the vitrifiable material.
Claim 19
Dependent Claim
131 words
A process for the manufacture of glass from a vitrifiable material containing a foaming and refining agent which comprises: (a) melting the vitrifiable material in less than 10 minutes at a temperature below the foaming temperature to form a molten mass having a viscosity below about 1000 poises; (b) foaming the molten mass throughout its volume by rapidly heating the molten mass to increase its temperature at a rate of at least about 20° C per minute while maintaining its viscosity below about 1000 poises and until the material has been expanded to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 20
Dependent Claim
131 words
A process for the manufacture of glass from a vitrifiable material containing a foaming and refining agent which comprises: (a) melting the vitrifiable material in less than 10 minutes at a temperature below the foaming temperature to form a molten mass having a viscosity below about 1000 poises; (b) foaming the molten mass throughout its volume by rapidly heating the molten mass to increase its temperature at a rate of at least about 20° C per minute while maintaining its viscosity below about 1000 poises and until the material has been expanded to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 21
Dependent Claim
50 words
The process of claim 16 wherein: (a) the mixture is heated to 1300° C in about 6 minutes and then from 1300 to 1500° C at the rate of 30° C per minutes, the temperature being kept at 1500° C for 10 minutes before separation of the fused liqud glass.
Claim 22
Dependent Claim
76 words
A process for the manufacture of glass from a vitrifiable foamable material which comprises: (a) melting the vitrifiable material to form a molten mass at a temperature just below the foaming temperature; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam; and (d) recovering the fused liquid glass.
Claim 23
Dependent Claim
76 words
A process for the manufacture of glass from a vitrifiable foamable material which comprises: (a) melting the vitrifiable material to form a molten mass at a temperature just below the foaming temperature; (b) heating at an increased rate to rapidly foam the molten mass throughout its volume to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam; and (d) recovering the fused liquid glass.
Claim 24
Dependent Claim
131 words
A process for the manufacture of glass comprising: (a) forming a vitrifiable mixture of materials having distributed therethrough a foaming and refining agent; (b) rapidly melting the vitrifiable material at a temperature below the foaming temperature thereof to form a molten vitreous mass having visible nuclei distributed therethrough and a viscosity below about 1000 poises; (c) foaming the molten mass throughout its volume by rapidly heating the molten mass to increase the temperature above the foaming temperature at a rate sufficient to produce rapid thermal convection and expansion throughout the molten mass to at least 1.5 times its initial molten volume; (d) controlling the heating until the foamed glass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (e) recovering the fused liquid glass.
Claim 25
Dependent Claim
131 words
A process for the manufacture of glass comprising: (a) forming a vitrifiable mixture of materials having distributed therethrough a foaming and refining agent; (b) rapidly melting the vitrifiable material at a temperature below the foaming temperature thereof to form a molten vitreous mass having visible nuclei distributed therethrough and a viscosity below about 1000 poises; (c) foaming the molten mass throughout its volume by rapidly heating the molten mass to increase the temperature above the foaming temperature at a rate sufficient to produce rapid thermal convection and expansion throughout the molten mass to at least 1.5 times its initial molten volume; (d) controlling the heating until the foamed glass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (e) recovering the fused liquid glass.
Claim 26
Dependent Claim
92 words
A process for the manufacture of glass from vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a temperature just below the foaming temperature; (b) continuously flowing the molten mass along a predetermined path; (c) heating at an increased rate to rapidly foam the flowing molten mass throughout its volume until the material has been expanded to at least about 1.5 times its initial molten volume; (d) controlling the heating until the foamed mass subsides to dissipate the foam; and (e) recovering the fused liquid glass.
Claim 27
Dependent Claim
92 words
A process for the manufacture of glass from vitrifiable material which comprises: (a) melting the vitrifiable material to form a molten mass having a temperature just below the foaming temperature; (b) continuously flowing the molten mass along a predetermined path; (c) heating at an increased rate to rapidly foam the flowing molten mass throughout its volume until the material has been expanded to at least about 1.5 times its initial molten volume; (d) controlling the heating until the foamed mass subsides to dissipate the foam; and (e) recovering the fused liquid glass.
Claim 28
Dependent Claim
111 words
A continuous process for the manufacture of glass from a granular vitrifiable material having distributed therethrough a foaming and refining agent which comprises: (a) rapidly melting the vitrifiable material to form a flowing molten mass having foam producing nuclei distributed therethrough; (b) foaming the flowing molten mass throughout its volume by rapidly heating it to about 1500° C and above to produce rapid thermal convection and expansion throughout the flowing molten mass to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 29
Dependent Claim
111 words
A continuous process for the manufacture of glass from a granular vitrifiable material having distributed therethrough a foaming and refining agent which comprises: (a) rapidly melting the vitrifiable material to form a flowing molten mass having foam producing nuclei distributed therethrough; (b) foaming the flowing molten mass throughout its volume by rapidly heating it to about 1500° C and above to produce rapid thermal convection and expansion throughout the flowing molten mass to at least 1.5 times its initial molten volume; (c) controlling the heating until the foamed mass subsides to dissipate the foam while maintaining it at a viscosity below about 1000 poises; and (d) recovering the fused liquid glass.
Claim 30
Dependent Claim
29 words
The process of claim 21 wherein: (a) the molten mass is heated at a rate of at least 20° C per minute to produce said foaming and thermal convection.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |