Urea-urethane-acrylate radiation curable coating compositions and methods of making same
Assignee: PPG Industries Inc
•
Filing: 1977-04-15
•
Granted: 1978-08-22
•
Expires: 1997-04-15
Abstract
Abstract Urea-linked urethane-modified acrylate-capped resins provide radiation curable coating compositions of exceptional durability and flexibility and which are essentially free of volatile solvents. These resins, typically produced by controlled addition of water to an isocyanato-terminated urethane- or thiocarbamate-containing prepolymer moiety to form an intermediate which is reacted with a hydroxyl-containing acrylic monomer that furnishes ethylenic unsaturation crosslinking sites to the resin, are further characterized by the resin composition substantially comprising molecules wherein the urea group has directly adjacent radicals derived from the prepolymer moiety.
Inventors
- 👤 Charles B. Friedlander
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:55
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08F; C08F299/00; C08F299/02; C08F299/06; C08G18/28; C08G18/67; C08G18/671; C08G18/672
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
96 words
Radiation polymerizable resin comprising the reaction product of: a. a prepolymer moiety having a plurality of isocyanato groups; b. water in an amount sufficient to react with only a portion of the isocyanato groups of said prepolymer moiety to form in said reaction product at least one urea group linking two prepolymer moieties; and c. a polyfunctional compound containing at least one functional group which is reactive with an isocyanato group of said prepolymer moiety and which polyfunctional compound after reaction with said isocyanato group provides at least one ethylenic functional group in said reaction product.
Claim 2
Dependent Claim
96 words
Radiation polymerizable resin comprising the reaction product of: a. a prepolymer moiety having a plurality of isocyanato groups; b. water in an amount sufficient to react with only a portion of the isocyanato groups of said prepolymer moiety to form in said reaction product at least one urea group linking two prepolymer moieties; and c. a polyfunctional compound containing at least one functional group which is reactive with an isocyanato group of said prepolymer moiety and which polyfunctional compound after reaction with said isocyanato group provides at least one ethylenic functional group in said reaction product.
Claim 3
Dependent Claim
21 words
The resin of claim 1 in which said prepolymer moiety is the reaction product of a polyol and an organic polyisocyanate.
Claim 4
Dependent Claim
60 words
The resin of claim 2 in which said polyol is selected from the group consisting of a polyester polyol, a polyamide polyol, a polyether polyol, a polyurethane polyol, a polyacrylate polyol, a polyol derived from the polymerization of monomeric aliphatic or aromatic diols, triols and multi-functional hydroxyl-containing compounds, and the alkoxylated derivatives of said diols, triols and multi-functional hydroxyl-containing compounds.
Claim 5
Dependent Claim
14 words
The resin of claim 3 in which said polyester polyol is a polycaprolactone polyol.
Claim 6
Dependent Claim
30 words
The resin of claim 3 in which said alkoxylated derivative of a polyol is 1,1,1-trimethylolpropane alkoxylated with ethylene or propylene oxide, or pentaerythritol alkoxylated with ethylene oxide or propylene oxide.
Claim 7
Dependent Claim
15 words
The resin of claim 3 is which said polyol contains two to six hydroxyl groups.
Claim 8
Dependent Claim
26 words
The resin of claim 6 in which said polyol has an atomic weight ratio of carbon to hydroxyl-radical oxygen in the range of 0.5:1 to 140:1.
Claim 9
Dependent Claim
22 words
The resin of claim 1 in which said prepolymer moiety is the reaction product of a polyfunctional mercaptan with an organic polyisocyanate.
Claim 10
Dependent Claim
31 words
The resin of claim 1 in which said water is in an amount between about 0.2 equivalent and about 0.75 equivalent per equivalent of isocyanato groups present in said prepolymer moiety.
Claim 11
Dependent Claim
18 words
The resin of claim 1 in which said polyfunctional compound is acrylic acid or a hydroxyl-containing acrylic ester.
Claim 12
Dependent Claim
27 words
The resin of claim 10 in which said hydroxyl-containing acrylic ester is selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, 2-hydroxyethyl methacrylate and 2-hydroxypropyl methacrylate.
Claim 13
Independent Claim
81 words
A method for preparing a radiation polymerizable resin comprising the steps of: (a) forming a prepolymer moiety having a plurality of isocyanato groups; and (b) reacting said prepolymer moiety with water and with a polyfunctional compound containing (1) ethylenic unsaturation, and (2) at least one functional group which is reactive with an isocyanato group; said water and said polyfunctional compound each being present in an amount sufficient to react with only a portion of the isocyanato groups of said prepolymer moiety.
Claim 14
Independent Claim
81 words
A method for preparing a radiation polymerizable resin comprising the steps of: (a) forming a prepolymer moiety having a plurality of isocyanato groups; and (b) reacting said prepolymer moiety with water and with a polyfunctional compound containing (1) ethylenic unsaturation, and (2) at least one functional group which is reactive with an isocyanato group; said water and said polyfunctional compound each being present in an amount sufficient to react with only a portion of the isocyanato groups of said prepolymer moiety.
Claim 15
Dependent Claim
28 words
The method of claim 12 wherein said prepolymer moiety is reacted with water to form an intermediate product having at least one urea group linking two prepolymer moieties.
Claim 16
Dependent Claim
38 words
The method of claim 12 wherein said prepolymer moiety is reacted with said polyfunctional compound to form an intermediate product having at least one urethane group, at least one reactive isocyanato group and a site of ethylenic unsaturation.
Claim 17
Dependent Claim
16 words
The method of claim 12 in which said water is added gradually to said prepolymer moiety.
Claim 18
Dependent Claim
20 words
The method of claim 12 in which said prepolymer is the reaction product of a polyol and an organic polyisocyanate.
Claim 19
Dependent Claim
61 words
The method of claim 16 in which said polyol is selected from the group consisting of a polyester polyol, a polyamide polyol, a polyether polyol, a polyurethane polyol, a polyacrylate polyol, and a polyol derived from the polymerization of monomeric aliphatic or aromatic diols, triols and multi-functional hydroxyl-containing compounds, and the alkoxylated derivatives of said diols, triols and multi-functional hydroxyl-containing compounds.
Claim 20
Dependent Claim
14 words
The method of claim 17 in which said polyester polyol is a polycaprolactone polyol.
Claim 21
Dependent Claim
31 words
The method of claim 17 in which said alkoxylated derivative of a polyol is 1,1,1-trimethylolpropane alkoxylated with ethylene oxide or propylene oxide, or pentaerythritol alkoxylated with ethylene oxide or propylene oxide.
Claim 22
Dependent Claim
15 words
The method of claim 17 in which said polyol contains two to six hydroxyl groups.
Claim 23
Dependent Claim
26 words
The method of claim 20 in which said polyol has an atomic weight ratio of carbon to hydroxyl-radical oxygen in the range of 0.5:1 to 140:1.
Claim 24
Dependent Claim
22 words
The method of claim 12 in which said prepolymer moiety is the reaction product of a polyfunctional mercaptan with an organic polyisocyanate.
Claim 25
Dependent Claim
31 words
The method of claim 12 in which said water is in an amount between about 0.2 equivalent and about 0.75 equivalent per equivalent of isocyanato groups present in said prepolymer moiety.
Claim 26
Dependent Claim
18 words
The method of claim 12 in which said polyfunctional compound is acrylic acid or a hydroxyl-containing acrylic ester.
Claim 27
Dependent Claim
46 words
A coating composition having resin comprising the reaction product of claim 1 and having a diluent which is co-reactive with said reaction product upon exposure of said reaction product and said diluent to curing conditions, said diluent being an ethylenically unsaturated polyfunctional compound of low viscosity.
Claim 28
Dependent Claim
29 words
The coating composition of claim 25 wherein said reaction product comprises between about 20 and about 80 percent of the total weight of said reaction product and said diluent.
References Cited (Backward Citations)
US3457326A
Cited
US3624020A
Cited
US3600359A
Cited
US3864133A
Cited
US3700643A
Cited
US3948665A
Cited
US4038239A
Cited
US3939126A
Cited
US4038257A
Cited
US4049632A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-21 | 1982-02-20 | 1982-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-21 | 1986-02-20 | 1986-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-21 | 1990-02-20 | 1990-08-22 | $7700.00 | Window Closed / Lapsed |