Process for improving the heat resistance of zirconium and its alloys
Assignee: Ugine Aciers SA
•
Filing: 1976-12-02
•
Granted: 1978-08-22
•
Expires: 1996-12-02
Abstract
Abstract A method for treating zirconium and zirconium alloys, in particular the zirconium alloys used in nuclear reactors which are water cooled, as a structural or casing material for fuels. The method consists in dissolving or maintaining a solid solution of the majority of carbon contained in these alloys by thermal or thermo-mechanical treatments carried out in the α + β range or if necessary in the β range followed by a rolling in α phase if necessary. The products obtained have a highly improved mechanical resistance under heat, in particular with regard to resistance to creep; they are particularly suitable for constructing casing tubes for fuels in water cooled nuclear reactors having a better resistance to distortion in relation to time.
Inventors
- 👤 Marcel Armand
- 👤 Daniel Charquet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:35
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/16; C22F1/18; C22F1/186; G; G21; G21C; G21C3/00; G21C3/02; G21C3/04; G21C3/06; G21C3/07; Y; Y02; Y02E; Y02E30/00; Y02E30/30; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
190 words
In a process for improving the mechanical and corrosion resistance properties under heat of zirconium and zirconium alloys including up to about 3% hafnium by weight as an impurity and alloying elements selected from the group consisting of Fe, Cr, Ni, Mo, Cu, V, Sn and Nb, and wherein the zirconium or zirconium alloys comprise a significant portion of α phase within the temperature range of 830° to 950° C and which contain between about 150 and 400 ppm of carbon to strengthen the resistance to creep, the improvement comprising: casting the zirconium and zirconium alloys into ingots; effecting carbon solubilization by thermal or themo-mechanical treatment of said zirconium and zirconium alloys within said temperature range during transformation of the ingot into an intermediate product shape wherein a significant portion of α phase is present to solubilize at least a part of the carbon; subsequently transforming the intermediate product shape to a finished product shape by carrying out a further reduction of the intermediate product in the α temperature range to effect ingot dimension reduction of at least about 50%; and annealing the finished product in the α temperature range.
Claim 2
Dependent Claim
190 words
In a process for improving the mechanical and corrosion resistance properties under heat of zirconium and zirconium alloys including up to about 3% hafnium by weight as an impurity and alloying elements selected from the group consisting of Fe, Cr, Ni, Mo, Cu, V, Sn and Nb, and wherein the zirconium or zirconium alloys comprise a significant portion of α phase within the temperature range of 830° to 950° C and which contain between about 150 and 400 ppm of carbon to strengthen the resistance to creep, the improvement comprising: casting the zirconium and zirconium alloys into ingots; effecting carbon solubilization by thermal or themo-mechanical treatment of said zirconium and zirconium alloys within said temperature range during transformation of the ingot into an intermediate product shape wherein a significant portion of α phase is present to solubilize at least a part of the carbon; subsequently transforming the intermediate product shape to a finished product shape by carrying out a further reduction of the intermediate product in the α temperature range to effect ingot dimension reduction of at least about 50%; and annealing the finished product in the α temperature range.
Claim 3
Dependent Claim
30 words
A process as defined in claim 1, wherein at least one of said thermal solubilization treatments is carried out for of a total duration of from 2 to 30 hours.
Claim 4
Dependent Claim
23 words
A process as defined in claim 1, wherein from 10 to 100 ppm of phosphorus is introduced into the zirconium or zirconium alloy.
Claim 5
Dependent Claim
23 words
A process as defined in claim 1, wherein from 10 to 100 ppm of silicon is introduced into the zirconium or zirconium alloy.
Claim 6
Dependent Claim
116 words
In a process for improving the mechanical properties under heat of zirconium with or without hafnium and zirconium alloys, each of which contain between about 150 and 400 ppm of carbon, to strengthen the resistance to creep, the improvement comprising: casting the material into ingots ; effecting carbon solubilization by thermal or thermo-mechanical treatment during transformation of the ingot in the solid state into an intermediate product shape at a temperature in excess of 1100° C to solubilize at least part of the carbon; rapidly cooling the material to below 950° C; and subsequently carrying out an additional thermal or thermo-mechanical treatment at a temperature of not greater than 950° C to produce a finished product.
Claim 7
Dependent Claim
116 words
In a process for improving the mechanical properties under heat of zirconium with or without hafnium and zirconium alloys, each of which contain between about 150 and 400 ppm of carbon, to strengthen the resistance to creep, the improvement comprising: casting the material into ingots ; effecting carbon solubilization by thermal or thermo-mechanical treatment during transformation of the ingot in the solid state into an intermediate product shape at a temperature in excess of 1100° C to solubilize at least part of the carbon; rapidly cooling the material to below 950° C; and subsequently carrying out an additional thermal or thermo-mechanical treatment at a temperature of not greater than 950° C to produce a finished product.
Claim 8
Dependent Claim
23 words
A process as defined in claim 5, wherein from 10 to 100 ppm of silicon is introduced into the zirconium or zirconium alloy.
Claim 9
Dependent Claim
23 words
A process as defined in claim 5, wherein from 10 to 100 ppm of phosphorus is introduced into the zirconium or zirconium alloy.
References Cited (Backward Citations)
US2772964A
Cited
US2894866A
Cited
US3148055A
Cited
US3097094A
Cited
US3782924A
Cited
US3664825A
Cited
US3865635A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-21 | 1982-02-20 | 1982-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-21 | 1986-02-20 | 1986-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-21 | 1990-02-20 | 1990-08-22 | $7700.00 | Window Closed / Lapsed |