High solids pigment coating composition
Assignee: Akzo NV
•
Filing: 1976-12-10
•
Granted: 1978-08-01
•
Expires: 1996-12-10
Abstract
Abstract A high solids pigmented coating composition is prepared from a curing agent and an ester diol binder which is a mixture of (A) 20-80 MOLE % OF A COMPOUND HAVING THE GENERAL FORMULA: <IMAGE> where R1 represents the group formed by abstraction of the two carboxyl groups from a cycloaliphatic and/or aromatic dicarboxylic acid having 8 to 20 carbon atoms and R2 and R3 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and m is a number of 1 - 3, and (B) 80-20 MOLE % OF A COMPOUND HAVING THE GENERAL FORMULA: <IMAGE> where R4 represents the group formed by abstraction of the two carboxyl groups from an aliphatic dicarboxylic acid having 2 to 12 carbon atoms, and R5 and R6 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and n is a number of 1 - 3.
Inventors
- 👤 Roelof Buter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 02:59
CPC Classifications
C; C09; C09D; C09D167/00; C09D167/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
224 words
A high solids pigmented coating composition prepared from a blend of an ester diol as binder and a curing agent for the binder, characterized in that (1) the ester diol is a mixture of (a) 20-80 mole % of an ester diol having the general formula: ##STR5## where R 1 represents the group formed by abstraction of the carboxyl groups from a cycloaliphatic and/or aromatic dicarboxylic acid having 8 to 20 carbon atoms and R 2 and R 3 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and m is a number of 1-3, and (b) 80-20 mole % of an ester diol having the general formula: ##STR6## where R 4 represents the group formed by abstraction of the two carboxyl groups from an aliphatic dicarboxylic acid having 2 to 12 carbon atoms, and R 5 and R 6 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and n is a number of 1-3, (2) the curing agent for the binder is an aminoplast, and (3) the amount of pigment in said coating composition is at least 30% by weight, based on the total solids content.
Claim 2
Dependent Claim
224 words
A high solids pigmented coating composition prepared from a blend of an ester diol as binder and a curing agent for the binder, characterized in that (1) the ester diol is a mixture of (a) 20-80 mole % of an ester diol having the general formula: ##STR5## where R 1 represents the group formed by abstraction of the carboxyl groups from a cycloaliphatic and/or aromatic dicarboxylic acid having 8 to 20 carbon atoms and R 2 and R 3 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and m is a number of 1-3, and (b) 80-20 mole % of an ester diol having the general formula: ##STR6## where R 4 represents the group formed by abstraction of the two carboxyl groups from an aliphatic dicarboxylic acid having 2 to 12 carbon atoms, and R 5 and R 6 may be the same or different and represent groups formed by abstraction of the two hydroxyl groups from a divalent alcohol having 2 to 12 carbon atoms, and n is a number of 1-3, (2) the curing agent for the binder is an aminoplast, and (3) the amount of pigment in said coating composition is at least 30% by weight, based on the total solids content.
Claim 3
Dependent Claim
21 words
The coating composition of claim 1 characterized in that the molar ratio of the ester diols is between 3:1 and 1:3.
Claim 4
Dependent Claim
21 words
The coating composition of claim 1 characterized in that the molar ratio of the ester diols is between 2:1 and 1:2.
Claim 5
Dependent Claim
38 words
The coating composition of claim 1 characterized in that one of the ester diols is formed from a cycloaliphatic or aromatic dicarboxylic acid containing 8 to 10 carbon atoms and a diol containing 2 to 9 carbon atoms.
Claim 6
Dependent Claim
36 words
The coating composition of claim 1 characterized in that one of the ester diols is formed from an aliphatic dicarboxylic acid containing 2 to 10 carbon atoms and a diol containing 2 to 9 carbon atoms.
Claim 7
Dependent Claim
36 words
The coating composition of claim 1 characterized in that the molar ratio of the hydroxyl groups of the ester diol mixture to the reactive groups of the curing agent is between about 0.7 and about 1.5.
Claim 8
Dependent Claim
28 words
The process for the preparation of a coating composition having a high solids content characterized in that it comprises the preparation of the coating composition of claim 1.
Claim 9
Dependent Claim
49 words
The coating composition of claim 1 wherein said curing agent for the binder is a methylol melamine containing 4 to 6 methylol groups per molecule of melamine, at least 3 of said methylol groups being etherified with an alcohol selected from the group consisting of methanol, ethanol, and butanol.
Claim 10
Dependent Claim
38 words
The coating composition of claim 1 wherein said curing agent for the binder is an N-methylol group- and/or N-methylol ether group- containing amino resin formed by reacting an aldehyde with a compound containing amino groups or amido groups.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-31 | 1982-01-30 | 1982-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-31 | 1986-01-30 | 1986-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-31 | 1990-01-30 | 1990-08-01 | $7700.00 | Window Closed / Lapsed |