Process for making water diluted electroinsulation enamels
Assignee: Beck Dr and Co GmbH
•
Filing: 1976-08-24
•
Granted: 1978-08-01
•
Expires: 1996-08-24
Abstract
Abstract Water dilutable electroinsulation enamels are made by reacting a hydroxyl group containing polyesteramide of low acid number with at least one amine in an amount of 5 to 30% by weight relative to the weight of the ester imide whereupon the reaction product is diluted with water until it has the desired viscosity for lacquering purposes.
Inventors
- 👤 Harald Janssen
- 👤 Ferdinand Hansch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:03
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/303; H01B3/306; C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/16; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
112 words
A process of making electro-insulation enamels which are adapted for water dilution, the said process comprising reacting an aromatic tricarboxylic acid monoanhydride with about equivalent amounts of a diamine, a difunctional alcohol and a trifunctional alcohol which latter in its structure includes an isocyanurate ring so as to obtain a hydroxyl groups containing polyesterimide of an acid number of at most 10, and then reacting the said polyesterimide with at least one amine and/or aminoalcohol in an amount of 5 to 30% by weight relative to the weight of the esterimide to effect an aminolysis, whereupon the reaction product is diluted with water until it has the desired viscosity for enameling purposes.
Claim 2
Dependent Claim
112 words
A process of making electro-insulation enamels which are adapted for water dilution, the said process comprising reacting an aromatic tricarboxylic acid monoanhydride with about equivalent amounts of a diamine, a difunctional alcohol and a trifunctional alcohol which latter in its structure includes an isocyanurate ring so as to obtain a hydroxyl groups containing polyesterimide of an acid number of at most 10, and then reacting the said polyesterimide with at least one amine and/or aminoalcohol in an amount of 5 to 30% by weight relative to the weight of the esterimide to effect an aminolysis, whereupon the reaction product is diluted with water until it has the desired viscosity for enameling purposes.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the dicarboxylic acid or ester is terephthalic acid, dimethylterephthalate or isophthalic acid.
Claim 4
Dependent Claim
22 words
The process of claim 2 wherein the polyester imide is the reaction product of trimellitic acid anhydride, diaminodiphenylmethane, dimethylterephthalate, tris(hydroxyethyl)isocyanurate and ethyleneglcyol.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein the said viscosity is between 100 and 10,000 cP.
Claim 6
Dependent Claim
11 words
The process of claim 1 wherein the tribasic alcohol is tris(hydroxyethyl)isocyanurate.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein the tricarboxylic acid is trimelliticanhydride.
Claim 8
Dependent Claim
40 words
The process of claim 1 wherein the reaction between the polyesterimide resin and the amine is carried out in a solvent for the polyesterimide in an amount of 5 to 20% by weight relative to the weight of the polyesterimide.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein the amine is used in an amount of 20 to 30% by weight relative to the weight of the polyesterimide.
Claim 10
Dependent Claim
36 words
The process of claim 1 wherein the amino alcohol has a tertiary amino group, a vapor pressure of not more than 50 mm Hg at 20° C and a boiling point between 100° and 200° C.
Claim 11
Dependent Claim
21 words
The process of claim 1 wherein the aminoalcohol is selected from the group consisting of 2-dimethylamino-2-methylpropanol, 2-dimethylamino-ethanol, 2-diethylaminoethanol, 3-dimethylaminopropanol and dimethylisopropanolamine.
Claim 12
Dependent Claim
40 words
The process of claim 1 wherein a water soluble stoving catalyst is added prior to or during the water dilution of the reaction product in an amount of 0.1 to 5% by weight relative to the weight of the polyesterimide.
Claim 13
Dependent Claim
10 words
The process of claim 11 wherein the catalyst is triethanolaminotitanate.
Claim 14
Dependent Claim
59 words
The process of claim 1 wherein the polyesterimide resin is first reacted at 140° to 190° C with about a third of the total amine aminoalcohol, the remainder of the amine aminoalcohol being added after cooling of the reaction product to 70 to 100° C while the product is simultaneously or subsequently diluted with water to about 50% concentration.
Claim 15
Dependent Claim
12 words
A polyimide base lacquer composition produced by the process of claim 1.
Claim 16
Dependent Claim
10 words
The process of claim 1 wherein the diamine is diaminodiphenylmethane.
Claim 17
Dependent Claim
22 words
The process of claim 1 wherein the formation of the polyesterimide includes a dicarboxylic acid or ester thereof as a further reactant.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-31 | 1982-01-30 | 1982-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-31 | 1986-01-30 | 1986-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-31 | 1990-01-30 | 1990-08-01 | $7700.00 | Window Closed / Lapsed |