Abstract
Abstract Diffusants are applied onto semiconductor solar cell substrates using screen printing techniques. The method is applicable to square and rectangular cells and can be used to apply dopants of opposite types to the front and back of the substrate. Then, simultaneous diffusion of both dopants can be performed with a single furnace pass.
Inventors
- 👤 John C. Evans, Jr.
- 👤 Henry W. Brandhorst, Jr.
- 👤 George A. Mazaris
- 👤 Larry R. Scudder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:49
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/121; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/141; H10P32/17; H10P32/171; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
142 words
An automatable method for doping a solar cell substrate of the flat wafer type having opposed surfaces which comprises screen printing onto each of said opposed surfaces a layer of a glass-forming chemical containing an electrical-type dopant which molecularly bonds to a resulting glass coating, the dopant in said chemical on one of said surfaces being of a first electrical type and the dopant in said chemical on the opposed surface being of a second electrical type, heating said printed substrate at a first elevated temperature to remove volatiles from said layer and to dry the same, and thereafter heating said printed substrate at a second elevated temperature greater than said first elevated temperature to form said glass coating of said opposed surfaces of said substrate, said second elevated temperature being effective to simultaneously diffuse both of the dopants into said substrate.
Claim 2
Dependent Claim
142 words
An automatable method for doping a solar cell substrate of the flat wafer type having opposed surfaces which comprises screen printing onto each of said opposed surfaces a layer of a glass-forming chemical containing an electrical-type dopant which molecularly bonds to a resulting glass coating, the dopant in said chemical on one of said surfaces being of a first electrical type and the dopant in said chemical on the opposed surface being of a second electrical type, heating said printed substrate at a first elevated temperature to remove volatiles from said layer and to dry the same, and thereafter heating said printed substrate at a second elevated temperature greater than said first elevated temperature to form said glass coating of said opposed surfaces of said substrate, said second elevated temperature being effective to simultaneously diffuse both of the dopants into said substrate.
Claim 3
Dependent Claim
24 words
The method of claim 1, wherein the second elevated heating step is conducted at 850° to 950° C for about 11/2 to 3/4 hours.
Claim 4
Dependent Claim
14 words
The method of claim 1, wherein said solar cell substrate is rectangular in shape.
Claim 5
Dependent Claim
40 words
The method of claim 1, wherein said chemical comprises a paste having a viscosity of 50 to 150 cps and the resulting print comprises from 10 to 30% by weight of the dopant and from 90 to 70% of silica.
Claim 6
Dependent Claim
22 words
The method of claim 1, wherein the thickness of the screen printed layer on the solar cell substrate is less than 1μ.
Claim 7
Dependent Claim
115 words
An automated method for doping a square or rectangular silicon solar cell substrate suitable for space applications which comprises: screen printing and drying onto one surface of said substrate a solution containing a dopant, screen printing and drying onto an opposite surface a solution containing another dopant of opposite conductivity to said first dopant, wherein said solutions have a viscosity of 50 to 150 cps. and the concentration of said dopants in the print is from 10 to 30% and wherein said solutions are printed to a thickness less than 1μM, and thereafter heating said substrate at 850° to 950° C for about 11/2 to 3/4 hours to simultaneously diffuse said dopants into said substrate.
Claim 8
Dependent Claim
115 words
An automated method for doping a square or rectangular silicon solar cell substrate suitable for space applications which comprises: screen printing and drying onto one surface of said substrate a solution containing a dopant, screen printing and drying onto an opposite surface a solution containing another dopant of opposite conductivity to said first dopant, wherein said solutions have a viscosity of 50 to 150 cps. and the concentration of said dopants in the print is from 10 to 30% and wherein said solutions are printed to a thickness less than 1μM, and thereafter heating said substrate at 850° to 950° C for about 11/2 to 3/4 hours to simultaneously diffuse said dopants into said substrate.
References Cited (Backward Citations)
US3287187A
Cited
US3518756A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-31 | 1982-01-30 | 1982-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-31 | 1986-01-30 | 1986-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-31 | 1990-01-30 | 1990-08-01 | $7700.00 | Window Closed / Lapsed |