Fire-resistant composition
Assignee: Shell USA Inc
•
Filing: 1976-05-27
•
Granted: 1978-07-18
•
Expires: 1996-05-27
Abstract
Abstract An oil-resistant, fire-resistant polymer composition is disclosed which is useful in coating electrical conductors. The composition comprises a block copolymer, extending oil, polymeric alpha-olefin, filler and fire retardant package comprising antimony trioxide, an adduct of hexachlorocyclopentadiene and a zinc borate.
Inventors
- 👤 John L. Snyder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:08
CPC Classifications
H; H01; H01B; H01B7/00; H01B7/17; H01B7/29; H01B7/295; C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/38; C08K5/00; C08K5/02; C08L; C08L23/00; C08L23/02; C08L53/00; C08L53/02; C09; C09D; C09D153/00; C09D153/02; C09D153/025; H01B3/00; H01B3/18; H01B3/30; H01B3/44; H01B3/441; H01B7/28; H01B7/2806
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
148 words
An oil-resistant, fire-resistant polymer composition comprising: (a) 100 parts by weight of a block copolymer having at least two polymer end blocks A and at least one polymer mid block B, each block A being a non-elastomeric polymer block of a monoalkenyl arene having an average molecular weight of between about 2,000 and about 125,000 and each block B being an elastomeric hydrogenated polymer block of a conjugated diene, having an average molecular weight between about 10,000 and about 250,000; (b) 0-200 parts by weight of an extending oil; (c) 10-300 parts by weight of a polymeric alpha-olefin; (d) 0-200 parts by weight of an inorganic filler; (e) 5-100 parts by weight of antimony trioxide; (f) 5-100 parts by weight of a zinc borate; and (g) 20-300 parts by weight of a flame retardant selected from the group consisting of a perchloropentacyclodecane, the adduct ##STR3## and mixtures thereof.
Claim 2
Dependent Claim
148 words
An oil-resistant, fire-resistant polymer composition comprising: (a) 100 parts by weight of a block copolymer having at least two polymer end blocks A and at least one polymer mid block B, each block A being a non-elastomeric polymer block of a monoalkenyl arene having an average molecular weight of between about 2,000 and about 125,000 and each block B being an elastomeric hydrogenated polymer block of a conjugated diene, having an average molecular weight between about 10,000 and about 250,000; (b) 0-200 parts by weight of an extending oil; (c) 10-300 parts by weight of a polymeric alpha-olefin; (d) 0-200 parts by weight of an inorganic filler; (e) 5-100 parts by weight of antimony trioxide; (f) 5-100 parts by weight of a zinc borate; and (g) 20-300 parts by weight of a flame retardant selected from the group consisting of a perchloropentacyclodecane, the adduct ##STR3## and mixtures thereof.
Claim 3
Dependent Claim
13 words
A composition according to claim 1 wherein said polymeric alpha-olefin is isotactic polypropylene.
Claim 4
Dependent Claim
22 words
A composition according to claim 1 wherein said inorganic filler is selected from the group consisting of talc, calcium carbonate, and clay.
Claim 5
Dependent Claim
19 words
A composition according to claim 1 wherein the A block is styrene and the conjugated diene block is butadiene.
Claim 6
Dependent Claim
22 words
A composition according to claim 1 wherein the amount of extending oil varies from about 50 to about 100 parts by weight.
Claim 7
Dependent Claim
33 words
A composition according to claim 1 wherein the molecular weight of the A blocks are between about 5,000 and 50,000 and the molecular weight of the B blocks are between 30,000 and 150,000.
Claim 8
Dependent Claim
12 words
A composition according to claim 1 wherein the flame retardant is perchloropentacyclodecane.
Claim 9
Dependent Claim
25 words
A composition according to claim 1 wherein the zinc borate has the formula 2Z n O . 3B 2 O 3 . 3.5H 2 O.
Claim 10
Dependent Claim
15 words
A composition according to claim 1 wherein the flame retardant (g) is the adduct ##STR4##
Claim 11
Dependent Claim
49 words
A composition according to claim 1 wherein the amount of antimony trioxide is from about 10 to about 25 parts, the amount of zinc borate is from about 10 to about 25 parts, and the amount of the flame retardant (g) is from about 80 to about 200 parts.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |