Enhancement of promoted copper catalyst
Assignee: Dow Chemical Co
•
Filing: 1977-01-19
•
Granted: 1978-07-18
•
Expires: 1997-01-19
Abstract
Abstract The activity and resistance to sulfur poisoning of a catalyst consisting essentially of copper and one or more activator metals supported on high surface area gamma-alumina and suitable for selectively hydrogenating alpha-acetylenes in a hydrocarbon stream is enhanced by impregnating the catalyst with aqueous alkali metal hydroxide and heating the impregnated catalyst at about 350° C-650° C. This treatment is effective to increase catalytic activity both in freshly prepared catalyst and in used catalyst poisoned by sulfur which has been regenerated by treatment with aqueous alkali metal hydroxide, heating to an elevated temperature, and leaching with water.
Inventors
- 👤 Ludo K. Frevel
- 👤 Leonard J. Kressley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:48
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/89; B01J23/892; B01J23/76; B01J23/78; B01J23/84; B01J23/889; B01J23/8892; C; C07; C07C; C07C5/00; C07C5/02; C07C5/08; C07C2521/00; C07C2521/02; C07C2521/04; C07C2523/00; C07C2523/16; C07C2523/24; C07C2523/26; C07C2523/32; C07C2523/34; C07C2523/38; C07C2523/48; C07C2523/50; C07C2523/70; C07C2523/72; C07C2523/74; C07C2523/75; C07C2523/755
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
136 words
A process for improving an active catalyst consisting essentially of a mixture of finely divided copper metal and a minor proportion of at least one activator metal of the group consisting of silver, platinum, palladium, manganese, cobalt, nickel, chromium, and molybdenum supported on gamma-alumina having a surface area of at least about 10 sq meters per gram, which process consists essentially of impregnating said catalyst with about 0.01-0.3 gram mole of alkali metal hydroxide solution per 100 grams of catalyst, roasting the impregnated catalyst at a temperature up to about 650° C sufficient to cause a reaction between the alkali metal hydroxide and the alumina surface, and contacting the roasted alkali-impregnated catalyst with hydrogen at about 100° C-400° C for a time sufficient to convert essentially all copper and activator metal present to the metallic state.
Claim 2
Dependent Claim
136 words
A process for improving an active catalyst consisting essentially of a mixture of finely divided copper metal and a minor proportion of at least one activator metal of the group consisting of silver, platinum, palladium, manganese, cobalt, nickel, chromium, and molybdenum supported on gamma-alumina having a surface area of at least about 10 sq meters per gram, which process consists essentially of impregnating said catalyst with about 0.01-0.3 gram mole of alkali metal hydroxide solution per 100 grams of catalyst, roasting the impregnated catalyst at a temperature up to about 650° C sufficient to cause a reaction between the alkali metal hydroxide and the alumina surface, and contacting the roasted alkali-impregnated catalyst with hydrogen at about 100° C-400° C for a time sufficient to convert essentially all copper and activator metal present to the metallic state.
Claim 3
Dependent Claim
26 words
The process of claim 1 wherein the roasted alkali-impregnated catalyst is contacted at about 250° C-300° C with a mixture of hydrogen and an inert gas.
Claim 4
Dependent Claim
13 words
The process of claim 1 wherein the alkali metal hydroxide is sodium hydroxide.
Claim 5
Dependent Claim
19 words
The process of claim 1 wherein an aqueous solution of alkali metal hydroxide is used to impregnate the catalyst.
Claim 6
Dependent Claim
105 words
The process of claim 1 wherein the catalyst contains about 3-13 percent of copper based on the weight of alumina and the activator metal content is about 1-20 percent of the combined weight of copper and activator metal, said catalyst is impregnated with about 0.01-0.3 gram mole of aqueous solution of sodium hydroxide per 100 grams of catalyst, the impregnated catalyst is roasted at about 400° C-500° C, and the roasted catalyst is contacted at about 250° C-300° C with a mixture of hydrogen and an inert gas for a time sufficient to convert essentially all copper and activator metal present to the metallic state.
Claim 7
Dependent Claim
19 words
The process of claim 5 wherein the activator metal is a mixture of silver, chromium, nickel, cobalt, and manganese.
References Cited (Backward Citations)
US3327013A
Cited
US3912789A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |