Claim 3

The method of claim 1 wherein said high vacuum environment is within the range from about 0.1 to about 2.0 mm Hg.

Claim 4

The method of claim 1 wherein said predistilling temperature and said vacuum distillation temperature are each within the range of about 480° F. to about 650° F.

Claim 5

The method of claim 1 wherein said predistilling is carried out at approximately atmospheric pressure.

Claim 6

The method of claim 1 further comprising distilling said vacuum distilled stock in the presence of a clay, filtering the clay distilled stock; and collecting the filtered stock.

Claim 7

The method of claim 1 further comprising treating the vacuum distilled stock with a strong acid or base to form and remove a sludge therefrom; distilling the chemically treated stock in the presence of a clay; filtering the clay distilled stock; and collecting the filtered stock.

Claim 8

The method of claim 1 wherein said predistilling step is preceded by a flashing step including heating the stock to approximately 100-200° F., permitting materials volatile at this temperature to expand to gases, and collecting and incinerating said gases.

Claim 9

The method of claim 1, further comprising collecting said separated viscous concentrate as a useful by-product having a very low vapor pressure.

Claim 10

A viscous concentrate formed by the steps of: predistilling a used lubricating oil stock by steam stripping said stock at a temperature between about 480° F. and about 650° F. and below the cracking temperature thereof for at least 4 hours, said predistilling step removing NO x gases, a light oil component and residual water from the stock to leave a predistilled stock; thereafter vacuum distilling the predistilled stock by forming a thin film of the predistilled stock on a heated surface and wiping said film to assist in evaporating the stock and to avoid coking, fouling and buildup of impurities, said vacuum distilled taking place below the cracking temperature of the predistilled stock in a high vacuum environment, whereby a viscous concentrate is formed and removed from a vaporized, vacuum distilled stock; and collecting said viscous concentrate.

Claim 11

A viscous concentrate formed by the steps of: predistilling a used lubricating oil stock by steam stripping said stock at a temperature between about 480° F. and about 650° F. and below the cracking temperature thereof for at least 4 hours, said predistilling step removing NO x gases, a light oil component and residual water from the stock to leave a predistilled stock; thereafter vacuum distilling the predistilled stock by forming a thin film of the predistilled stock on a heated surface and wiping said film to assist in evaporating the stock and to avoid coking, fouling and buildup of impurities, said vacuum distilled taking place below the cracking temperature of the predistilled stock in a high vacuum environment, whereby a viscous concentrate is formed and removed from a vaporized, vacuum distilled stock; and collecting said viscous concentrate.

Claim 12

The viscous concentrate of claim 9 wherein said concentrate is an anti-corrosion concentrate suitable for coating vehicle frames and the lubricating oil stock contains heavy lube hydrocarbons, additives and metal compounds.

Claim 13

The concentrate of claim 10 wherein the additives and metal components remain substantially unaltered during the processing steps.

Claim 14

The anti-corrosion concentrate of claim 10 wherein the concentrate has a viscosity within the range of 4,000 to 20,000 SUS at 210° F.

Claim 15

The anti-corrosion concentrate of claim 10 in diluted form with a petroleum solvent making it easily adaptable to spray or aerosol applications.