Prevention of anode bag clogging in nickel iron plating
Assignee: M&T HARSHAW
•
Filing: 1977-03-30
•
Granted: 1978-07-18
•
Expires: 1997-03-30
Abstract
Abstract This invention relates to a process and composition for the preparation of an electrodeposit which contains at least one metal selected from the group consisting of nickel, cobalt and iron, which comprises passing current from an anode to a cathode through an aqueous plating solution containing at least one member selected from the group consisting of cobalt compounds and nickel compounds and iron compounds to provide cobalt, nickel and ferrous ions for electrodepositing cobalt, nickel, nickel-cobalt alloys, nickel-iron alloys, or nickel-cobalt-iron alloys the improvement comprising the presence of an effective amount of at least one compound or salt which in solution yields at least one member selected from the group consisting of cations of lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium in the said baths in a single or combined concentration of 0.1 gram per liter to 20 grams per liter.
Inventors
- 👤 Hyman Chessin
- 👤 Edgar J. Seyb, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:26
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/562; C25D3/12
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
130 words
In a process for the preparation of an electrodeposit which contains at least one metal selected from the group consisting of nickel, cobalt and iron, which comprises passing current from an anode to a cathode through an aqueous acidic plating solution containing at least one member selected from the group consisting of nickel compounds, cobalt compounds, and ferrous compounds providing ions for electrodepositing nickel, cobalt, nickel-cobalt alloy, nickel-iron alloy, or nickel-cobalt-iron alloy, and containing an amount of oxalic acid break-down product the improvement comprising the presence of at least one cation selected from the group consisting of cations of lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium in single or combined concentration of 0.1 gram per liter to 20 grams per liter.
Claim 2
Dependent Claim
130 words
In a process for the preparation of an electrodeposit which contains at least one metal selected from the group consisting of nickel, cobalt and iron, which comprises passing current from an anode to a cathode through an aqueous acidic plating solution containing at least one member selected from the group consisting of nickel compounds, cobalt compounds, and ferrous compounds providing ions for electrodepositing nickel, cobalt, nickel-cobalt alloy, nickel-iron alloy, or nickel-cobalt-iron alloy, and containing an amount of oxalic acid break-down product the improvement comprising the presence of at least one cation selected from the group consisting of cations of lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium in single or combined concentration of 0.1 gram per liter to 20 grams per liter.
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein said nickel compounds are nickel sulfate and nickel chloride.
Claim 4
Dependent Claim
15 words
The process of claim 1 wherein said nickel compounds are nickel sulfamate and nickel chloride.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein said cobalt compounds are cobalt sulfate and cobalt chloride.
Claim 6
Dependent Claim
15 words
The process of claim 1 wherein said cobalt compounds are cobalt sulfamate and cobalt chloride.
Claim 7
Dependent Claim
15 words
The process of claim 1 wherein said ferrous compound is ferrous sulfate or ferrous chloride.
Claim 8
Dependent Claim
95 words
In an aqueous plating solution containing nickel compounds and at least one member selected from the group consisting of cobalt compounds and ferrous compounds, providing ions for electrodepositing nickel, cobalt, nickel-cobalt alloy, nickel-iron alloy, or nickel-cobalt-iron alloy, and containing an amount of oxalic acid break-down product the improvement comprising the presence of at least one cation selected from the group consisting of cations of lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium in single or combined concentration of 1.0 gram per liter to 10 grams per liter.
Claim 9
Dependent Claim
95 words
In an aqueous plating solution containing nickel compounds and at least one member selected from the group consisting of cobalt compounds and ferrous compounds, providing ions for electrodepositing nickel, cobalt, nickel-cobalt alloy, nickel-iron alloy, or nickel-cobalt-iron alloy, and containing an amount of oxalic acid break-down product the improvement comprising the presence of at least one cation selected from the group consisting of cations of lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, and lutetium in single or combined concentration of 1.0 gram per liter to 10 grams per liter.
Claim 10
Dependent Claim
17 words
The composition as claimed in claim 7 wherein said nickel compounds are nickel sulfate and nickel chloride.
Claim 11
Dependent Claim
17 words
The composition as claimed in claim 7 wherein said nickel compounds are nickel sulfamate and nickel chloride.
Claim 12
Dependent Claim
17 words
The composition as claimed in claim 7 wherein said cobalt compounds are cobalt sulfate and cobalt chloride.
Claim 13
Dependent Claim
17 words
The composition as claimed in claim 7 wherein said cobalt compounds are cobalt sulfamate and cobalt chloride.
Claim 14
Dependent Claim
17 words
The composition as claimed in claim 7 wherein said ferrous compound is ferrous sulfate or ferrous chloride.
References Cited (Backward Citations)
US3506547A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |