Uniform filament and method of making the same
Assignee: RCA Licensing Corp
•
Filing: 1976-04-05
•
Granted: 1978-07-11
•
Expires: 1996-04-05
Abstract
Abstract A line electron filament is provided which is cylindrically shaped and substantially uniform in cross section about its longitudinal axis. The filament can be of the type known as directly heated or of the type known as indirectly heated. The uniformity of the filament is obtained through cataphoretic deposition in a rotating cylindrical tube. The filament is useful as a cathode in a display which employs space charge limited emission operation.
Inventors
- 👤 Robert Allen Gange
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 17:12
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/02; H01J9/04
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
51 words
An electron filament, which comprises: a cylindrical body of refractory metal, said body being substantially uniform in cross section about its longitudinal axis, and a layer of emissive material concentrically disposed on and around said cylindrical body and along the longitudinal axis thereof with said layer being substantially uniform in thickness.
Claim 2
Dependent Claim
51 words
An electron filament, which comprises: a cylindrical body of refractory metal, said body being substantially uniform in cross section about its longitudinal axis, and a layer of emissive material concentrically disposed on and around said cylindrical body and along the longitudinal axis thereof with said layer being substantially uniform in thickness.
Claim 3
Dependent Claim
25 words
A filament in accordance with claim 1 in which the ratio of the length to diameter of said filament is at least 100 to 1.
Claim 4
Dependent Claim
28 words
A filament in accordance with claim 1 in which said filament has a diameter which varies by less than about 25 microns along the length of said filament.
Claim 5
Dependent Claim
14 words
A filament in accordance with claim 3 in which said refractory metal comprises tungsten.
Claim 6
Dependent Claim
15 words
A filament in accordance with claim 4 in which said emissive material comprises emission carbonate.
Claim 7
Dependent Claim
95 words
A filament in accordance with claim 1, which further comprises: (a) a body of insulating material concentrically disposed on and around said cylindrical body and along the longitudinal axis thereof with said body of insulating material being disposed between said cylindrical body and said layer of emissive material, said body of insulating material being substantially uniform in thickness, (b) a first layer of electrolessly deposited metal concentrically disposed on and around said body of insulating material, and (c) a second layer of electroplated metal concentrically disposed on and around said layer of electrolessly deposited metal.
Claim 8
Dependent Claim
28 words
A filament in accordance with claim 6 in which said filament has a diameter which varies by less than about 25 microns along the length of said filament.
Claim 9
Dependent Claim
17 words
A filament in accordance with claim 7 in which said first and second metal layers comprise nickel.
Claim 10
Independent Claim
156 words
A method of making an electron filament, which comprises: (a) placing a cylindrical body of refractory metal into a cylindrical tube with said cylindrical body being disposed with its major axis along the longitudinal axis of said tube and maintained under tension in fixed relation to said tube, said tube including an electrically conductive body on and along its inner circumference, said tube being substantially filled with a suspension of emissive material, (b) rotating said tube about its longitudinal axis at a substantially constant rate with said tube being oriented such that the force of gravity acts orthogonally to the longitudinal axis of said tube, and then (c) establishing an electrical field between said cylindrical body and said electrically conductive body on said inner circumference so as to cataphoretically deposit a layer of said emissive material on and around said cylindrical body while rotating said tube, said layer of emissive material being substantially uniform in thickness.
Claim 11
Independent Claim
156 words
A method of making an electron filament, which comprises: (a) placing a cylindrical body of refractory metal into a cylindrical tube with said cylindrical body being disposed with its major axis along the longitudinal axis of said tube and maintained under tension in fixed relation to said tube, said tube including an electrically conductive body on and along its inner circumference, said tube being substantially filled with a suspension of emissive material, (b) rotating said tube about its longitudinal axis at a substantially constant rate with said tube being oriented such that the force of gravity acts orthogonally to the longitudinal axis of said tube, and then (c) establishing an electrical field between said cylindrical body and said electrically conductive body on said inner circumference so as to cataphoretically deposit a layer of said emissive material on and around said cylindrical body while rotating said tube, said layer of emissive material being substantially uniform in thickness.
Claim 12
Dependent Claim
14 words
A method in accordance with claim 9 in which said refractory metal comprises tungsten.
Claim 13
Dependent Claim
15 words
A method in accordance with claim 10 in which said emissive material comprises emission carbonate.
Claim 14
Dependent Claim
24 words
A method in accordance with claim 11 in which step (b) includes rotating said tube for at least 24 hours before performing step (c).
Claim 15
Dependent Claim
45 words
A method in accordance with claim 11 in which said electrical field established in step (c) is of a direction so as to cause said cylindrical body to function as a cathode and said conductive body on said inner circumference to function as an anode.
Claim 16
Dependent Claim
43 words
A method in accordance with claim 11 in which said electrical field established in step (c) is of a magnitude so as to establish an electrical field gradient within said tube which is in the range of about 50 to about 150 volt/cm.
Claim 17
Independent Claim
247 words
A method of making an electron filament, which comprises: (a) placing a cylindrical body of refractory metal into a cylindrical tube with said cylindrical body being disposed with its major axis along the longitudinal axis of the tube and maintained under tension in fixed relation to said tube, said tube including an electrically conductive body on and along its inner circumference, said tube being substantially filled with a suspension of insulating material to be deposited, (b) rotating said tube about its longitudinal axis at a substantially constant rate with said tube being oriented such that the force of gravity acts orthogonally to the longitudinal axis of said tube, then (c) establishing an electrical field between said cylindrical body and said electrically conductive body so as to cataphoretically deposit a body of said material on and around said cylindrical body while rotating said tube, said body of insulating material being substantially uniform in thickness, (d) removing said cylindrical body from said tube, then (e) electrolessly plating a first metal layer on and around said body of insulating material, (f) electroplating a second metal layer on and around said first metal layer, said second metal layer being thicker than said first layer, and then (g) repeating steps (a), (b) and (c) but with said material to be deposited being an emission carbonate so as to cataphoretically deposit a layer of emissive material on and around said second metal layer, said layer of emissive material being substantially uniform in thickness.
Claim 18
Independent Claim
247 words
A method of making an electron filament, which comprises: (a) placing a cylindrical body of refractory metal into a cylindrical tube with said cylindrical body being disposed with its major axis along the longitudinal axis of the tube and maintained under tension in fixed relation to said tube, said tube including an electrically conductive body on and along its inner circumference, said tube being substantially filled with a suspension of insulating material to be deposited, (b) rotating said tube about its longitudinal axis at a substantially constant rate with said tube being oriented such that the force of gravity acts orthogonally to the longitudinal axis of said tube, then (c) establishing an electrical field between said cylindrical body and said electrically conductive body so as to cataphoretically deposit a body of said material on and around said cylindrical body while rotating said tube, said body of insulating material being substantially uniform in thickness, (d) removing said cylindrical body from said tube, then (e) electrolessly plating a first metal layer on and around said body of insulating material, (f) electroplating a second metal layer on and around said first metal layer, said second metal layer being thicker than said first layer, and then (g) repeating steps (a), (b) and (c) but with said material to be deposited being an emission carbonate so as to cataphoretically deposit a layer of emissive material on and around said second metal layer, said layer of emissive material being substantially uniform in thickness.
Claim 19
Dependent Claim
14 words
A method in accordance with claim 15 in which said refractory metal comprises tungsten.
Claim 20
Dependent Claim
15 words
A method in accordance with claim 15 in which said emissive material comprises emission carbonate.
Claim 21
Dependent Claim
20 words
A method in accordance with claim 15 in which step (b) includes rotating said tube for at least 24 hours.
Claim 22
Dependent Claim
39 words
A method in accordance with claim 15 in which said electrical field during the cataphoretic deposition of said insulating material is of a magnitude so as to establish an electrical field gradient of about 10 volt/cm within said tube.
Claim 23
Dependent Claim
42 words
A method in accordance with claim 15 in which said electrical field during the cataphoretic deposition of said emissive material is of a magnitude so as to establish an electrical field gradient of about 50 to about 150 volt/cm within said tube.
Claim 24
Dependent Claim
10 words
An electron filament made by the method of claim 15.
Claim 25
Dependent Claim
10 words
An electron filament made by the method of claim 9.
References Cited (Backward Citations)
US1719988A
Cited
US2227046A
Cited
US2321439A
Cited
US2489367A
Cited
US2831140A
Cited
US3936532A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |