Transparent impact styrene polymer structure

Claim 1

A method for the preparation of a generally transparent impact resistant polymer structure, the steps of the method comprising providing a rubbery reinforcing diene polymer which is a polymer prepared from 1,3-butadiene, isoprene or mixtures thereof, the diene rubber having an inherent viscosity in the range of 0.9-2.5 as determined at 25° C employing 0.3 gram of rubber per deciliter of toluene, the diene rubber being employed in a proportion of from about 4 to 12 parts by weight, preparing a solution of the diene rubber in a mixture of (a) styrene and methylmethacrylate, the styrene being present in a proportion from about 65 to 95 parts by weight and the methylmethacrylate being present in a proportion from about 5 to 35 parts by weight of methylmethacrylate, (b) from about 0.01 to 0.5 weight percent of a bromine-containing compound selected from the group consisting of: allyl bromide, 2-(bromomethyl)-3-bromopropene, 3,3-dibromo-1-propene, 1-bromo-1-propene, 1-bromo-1-butene, 1-bromo-1-pentene 1-bromo-1-hexene 3-bromo-1-pentene, 3,4-dibromo-1-butene, 2-(dibromomethyl)-1-pentene, 2-(bromomethyl)-1-butene, 2-(bromomethyl)-1-pentene, 2-(dibormomethyl)-1-pentene, 2-(bromomethyl)-1-hexane, 3-bromo-1-hexene, 2-(dibromomethyl)-1-hexene, 3-bromocyclohexene, and 3-bromocyclopentene, and mixtures of such compounds, heating the mixture with agitation to a temperature to initiate free radical polymerization, maintaining agitation until at least about 30 weight percent of the combined weight of the styrene and methylmethacrylate is converted to polymer and subsequently polymerizing the mixture until about 70 to 95 percent conversion of monomer to polymer to thereby provide in an improved synthetic resinous structure or body, the structure comprising a continuous matrix of a polymer of about 65 to 95 parts by weight of styrene and 5 to 35 parts by weight of methylmethacrylate, the structure having a dispersed phase of a diene rubber, the diene rubber being present in a proportion of from 4 to about 12 parts by weight per hundred parts by weight of the combined weight of styrene and methylmethacrylate, the rubber being in the form of a plurality of particles dispersed throughout a styrene-methylmethacrylate polymer continuous phase, the rubber particles being of a generally cellular nature and containing occulusions of the styrene-methylmethacrylate polymer, the particles being of both monocellular and multicellular configurations, the rubber particles having a weight average particle diameter not exceeding 2 microns and the cell walls of the rubber particles having a thickness not exceeding 0.15 microns, the dimensions and configuration of the rubber particles being determined by means of an electron microscope on a sample of the polymer which has been treated with osmium tetraoxide, [K. Kato, Polymer Engineering and Science, 7, 38(1967)], with the further limitation that when the structure has a thickness of about 10 mils, the light absorbance, as measured using a wavelength of 640 millimicrons, is not greater than about 0.07, and the structure has a notched Izod impact value, when measured in accordance with The American Society for Testing Materials Specification D256A, of at least 0.65 foot pounds per inch of notch.

Claim 2

A method for the preparation of a generally transparent impact resistant polymer structure, the steps of the method comprising providing a rubbery reinforcing diene polymer which is a polymer prepared from 1,3-butadiene, isoprene or mixtures thereof, the diene rubber having an inherent viscosity in the range of 0.9-2.5 as determined at 25° C employing 0.3 gram of rubber per deciliter of toluene, the diene rubber being employed in a proportion of from about 4 to 12 parts by weight, preparing a solution of the diene rubber in a mixture of (a) styrene and methylmethacrylate, the styrene being present in a proportion from about 65 to 95 parts by weight and the methylmethacrylate being present in a proportion from about 5 to 35 parts by weight of methylmethacrylate, (b) from about 0.01 to 0.5 weight percent of a bromine-containing compound selected from the group consisting of: allyl bromide, 2-(bromomethyl)-3-bromopropene, 3,3-dibromo-1-propene, 1-bromo-1-propene, 1-bromo-1-butene, 1-bromo-1-pentene 1-bromo-1-hexene 3-bromo-1-pentene, 3,4-dibromo-1-butene, 2-(dibromomethyl)-1-pentene, 2-(bromomethyl)-1-butene, 2-(bromomethyl)-1-pentene, 2-(dibormomethyl)-1-pentene, 2-(bromomethyl)-1-hexane, 3-bromo-1-hexene, 2-(dibromomethyl)-1-hexene, 3-bromocyclohexene, and 3-bromocyclopentene, and mixtures of such compounds, heating the mixture with agitation to a temperature to initiate free radical polymerization, maintaining agitation until at least about 30 weight percent of the combined weight of the styrene and methylmethacrylate is converted to polymer and subsequently polymerizing the mixture until about 70 to 95 percent conversion of monomer to polymer to thereby provide in an improved synthetic resinous structure or body, the structure comprising a continuous matrix of a polymer of about 65 to 95 parts by weight of styrene and 5 to 35 parts by weight of methylmethacrylate, the structure having a dispersed phase of a diene rubber, the diene rubber being present in a proportion of from 4 to about 12 parts by weight per hundred parts by weight of the combined weight of styrene and methylmethacrylate, the rubber being in the form of a plurality of particles dispersed throughout a styrene-methylmethacrylate polymer continuous phase, the rubber particles being of a generally cellular nature and containing occulusions of the styrene-methylmethacrylate polymer, the particles being of both monocellular and multicellular configurations, the rubber particles having a weight average particle diameter not exceeding 2 microns and the cell walls of the rubber particles having a thickness not exceeding 0.15 microns, the dimensions and configuration of the rubber particles being determined by means of an electron microscope on a sample of the polymer which has been treated with osmium tetraoxide, [K. Kato, Polymer Engineering and Science, 7, 38(1967)], with the further limitation that when the structure has a thickness of about 10 mils, the light absorbance, as measured using a wavelength of 640 millimicrons, is not greater than about 0.07, and the structure has a notched Izod impact value, when measured in accordance with The American Society for Testing Materials Specification D256A, of at least 0.65 foot pounds per inch of notch.