Unsaturated polyester resin compositions
Assignee: Societa Italiana Resine SpA SIR
•
Filing: 1977-08-05
•
Granted: 1978-07-11
•
Expires: 1997-08-05
Abstract
Abstract Unsaturated polyester resin compositions comprising: (a) an unsaturated polyester resin, (b) from 5 to 15 parts by weight for each 100 parts by weight of polyester resin (a), of vinyl chloride polymer, and (c) from 10 to 20 parts by weight for each 100 parts by weight of polyester resin (a), of an epoxy Novolak resin having an epoxy function higher than 2, or of a mixture of the latter with a liquid epoxy resin in such amount that the average epoxy function of the mixture be higher than 2. These compositions hardenable by means of peroxides have low shrinkage values on hardening and yield hardened products having high resistance to bending and to heat.
Inventors
- 👤 Beppino Passalenti
- 👤 Giorgio Brumat
- 👤 Silvio Vargiu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:18
CPC Classifications
C; C08; C08F; C08F299/00; C08F299/02; C08F299/04
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
182 words
An unsaturated polyester resin composition hardenable by means of peroxides, which comprises: (a) an unsaturated polyester resin, (b) a vinyl chloride polymer in an amount of from 5 to 15 parts by weight for each 100 parts by weight of unsaturated polyester resin, and (c) from 10 to 20 parts by weight for each 100 parts by weight of unsaturated polyester resin, of an epoxy Novolak resin having an epoxy function greater than 2, or of a mixture of the latter with a liquid epoxy resin, said liquid epoxy resin being present in the mixture in an amount not exceeding 50% by weight and such that the average epoxy function of the mixture be higher than 2, and said epoxy Novolak resin being the product of the epoxidation with epichlorohydrin of a Novolak phenolic resin chosen from the following classes: ##STR6## wherein n 1 is from 0.2 to 4 ##STR7## wherein n 2 is from 1 to 8 and R 1 is an alkyl radical with from 2 to 10 carbon atoms, and ##STR8## wherein n 3 is from 0 to 1.
Claim 2
Dependent Claim
182 words
An unsaturated polyester resin composition hardenable by means of peroxides, which comprises: (a) an unsaturated polyester resin, (b) a vinyl chloride polymer in an amount of from 5 to 15 parts by weight for each 100 parts by weight of unsaturated polyester resin, and (c) from 10 to 20 parts by weight for each 100 parts by weight of unsaturated polyester resin, of an epoxy Novolak resin having an epoxy function greater than 2, or of a mixture of the latter with a liquid epoxy resin, said liquid epoxy resin being present in the mixture in an amount not exceeding 50% by weight and such that the average epoxy function of the mixture be higher than 2, and said epoxy Novolak resin being the product of the epoxidation with epichlorohydrin of a Novolak phenolic resin chosen from the following classes: ##STR6## wherein n 1 is from 0.2 to 4 ##STR7## wherein n 2 is from 1 to 8 and R 1 is an alkyl radical with from 2 to 10 carbon atoms, and ##STR8## wherein n 3 is from 0 to 1.
Claim 3
Dependent Claim
81 words
The composition of claim 1, wherein said component (a) is a solution in an unsaturated acrylic or vinylic monomer, of the polycondensation product of a mixture comprising one or more polycarboxylic acids and one or more polyhydric alcohols, in which one or the other class of the above compounds is unsaturated, the said polycondensation product having an acid value of from 18 to 25 and a Gardner viscosity V, as measured at 25° C in a 35 wt.% solution in styrene.
Claim 4
Dependent Claim
11 words
The composition of claim 2, wherein said unsaturated monomer is styrene.
Claim 5
Dependent Claim
43 words
The composition of claim 1, wherein said epoxy Novolak resin has an epoxy equivalent of from 165 to 185 and a viscosity of from 170 to 250 cps, as measured at 25° C in a 70 wt.% solution in ethylene glycol monobutyl ether.
Claim 6
Dependent Claim
37 words
The composition of claim 1, in which said component (b) is polyvinyl chloride or a copolymer of vinyl chloride with small amounts of other monomers selected from the group consisting maleic anhydride, allyl alcohol and vinylidene chloride.
Claim 7
Dependent Claim
15 words
The composition of claim 1, wherein said liquid epoxy resin is an epichlorohydrin-bisphenol A resin.
Claim 8
Dependent Claim
35 words
The composition of claim 1, which comprises from 0.5 to 3 parts by weight of oxide of alkaline earth metal for each 100 parts by weight of the sum of components (a), (b) and (c).
Claim 9
Dependent Claim
36 words
The composition of claim 1, which comprises from 100 to 300 parts by weight of inert fillers, lubricants, dyes and/or pigments for each 100 parts by weight of the sum of components (a), (b) and (c).
References Cited (Backward Citations)
US3300543A
Cited
US3100758A
Cited
US3513222A
Cited
DE1915026A1
Cited
US3786004A
Cited
US4038339A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |