Process for preparation of grafted unsaturated polyester liquid resin dispersion

Claim 2

A process for preparing a liquid resin dispersion, which comprises the steps of: (1) preparing a surface active, unsaturated polyester by reacting and condensing a polyester-forming dicarboxylic acid component containing at least 30 mole % of an unsaturated dicarboxylic acid or anhydride thereof, with a mixture of polyol components consisting essentially of (A) at least one ester-forming polyol selected from the group consisting of 4,4'-bis(β-hydroxyethoxyphenyl)-2,2-propane, 4,4'-bis(β-hydroxypropoxyphenyl)-2,2-propane, diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane, di-β-methylglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane and 2,2-bis(4-hydroxycyclohexyl)propane, and (B) at least one member having the formula ##STR4## wherein R is H or CH 3 and n is from 3 to 100, wherein the amount of (B) is from 10 to 50% by weight, based on the weight of A, whereby to form a surface active, unsaturated polyester having a number average molecular weight of from 500 to 5000; (2) dispersing the unsaturated polyester obtained in step (1) in the colloidal state in water to form an oil-in-water colloidal dispersion, said dispersion being free of water-soluble protective colloids and emulsifiers, (3) adding to the dispersion obtained in step (2) from 0.1 to 50% by weight, based on the weight of said polyester, of at least one water-insoluble monomer selected from the group consisting of (a) monomers having the formula CH.sub.2 ═CHX wherein X is --OOCR" wherein R" is alkyl having one to 8 carbon atoms, ##STR5## wherein R' is H, CH 3 or CH═CH 2 , --Cl, --CN, --Si(OCH 3 ) 3 , --Si(OC 2 H 5 ) 3 , --Si(OCH 2 CH 2 OCH 3 ) 3 or --Si(OOCCH 3 ) 3 , and (b) monomers having the formula ##STR6## wherein R'" is --H or --CH 3 , and Y is alkyl having 3 to 8 carbon atoms, --(CH 2 ) 2 OR"" wherein R"" is alkyl having one to 4 carbon atoms, glycidyl, --(CH 2 ) 3 Si(OCH 3 ) 3 or --(CH 2 ) 3 Si(OCH 2 CH 2 OCH 3 ) 3 , so that said monomer is solubilized by said polyester, and adding a radical polymerization initiator and grafting said monomer to said polyester whereby to obtain an aqueous dispersion of said polyester having said monomer grafted thereto.

Claim 3

A process according to claim 1 wherein the weight ratio of (B) to (A) is in the range of from 15 to 35%.

Claim 4

A process according to claim 1 wherein the total amount of carboxyl groups in the dicarboxylic acid component is 0.8 to 1.2 equivalents per equivalent of the sum of hydroxyl and glycidyl groups in the components (A) and (B).

Claim 5

A process according to claim 1 wherein the unsaturated dicarboxylic acid is fumaric acid or maleic acid.

Claim 6

A process according to claim 1 wherein the surface active polyester has a number average molecular weight of 1,000 to 3,000.

Claim 7

A process according to claim 1 wherein in the oil-in-water colloidal dispersion of the surface active polyester, the concentration of the polyester is 10 to 45% by weight, based on the weight of said dispersion.

Claim 8

A process as claimed in claim 1, in which n is in the range of 3 to 10.

Claim 9

A process according to claim 1 in which the acid value of said polyester is from 10 to 60.

Claim 10

A process according to claim 5 in which the acid value of said polyester is from 15 to 40.

Claim 11

A process according to claim 8 in which in step (2), there is added to the dispersion a base in an amount of smaller than 1.2 equivalents per equivalent of the acid value of the polyester.

Claim 12

A process according to claim 8 in which in step (2) there is added to the dispersion less than 20% by weight of a lower alcohol, based on the weight of the colloidal dispersion.

Claim 13

A process for preparing a liquid resin dispersion, which comprises the steps of (1) preparing a surface active, unsaturated polyester by reacting and condensing at from 180° to 210° C, a polyester-forming dicarboxylic acid component containing at least 30 mole % of an unsaturated dicarboxylic acid or anhydride thereof selected from the group consisting of fumaric acid, maleic acid, maleic anhydride and itaconic acid, with a mixture of polyol components consisting essentially of (A) at least one ester-forming polyol selected from the group consisting of 4,4'-bis(β-hydroxyethoxyphenyl)-2,2-propane, 4,4'-bis(β-hydroxypropoxyphenyl)-2,2-propane, diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane, di-β-methylglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane and 2,2-bis(4-hydroxycyclohexyl)-propane, and (B) at least one member having the formula ##STR7## wherein R is H or CH 3 and n is from 3 to 10 wherein the amount of (B) is from 15 to 35% by weight, based on the weight of (A), wherein the amount of said dicarboxylic acid component is from 0.8 to 1.2 equivalents per equivalent of the sum of the hydroxyl and glycidyl groups of said polyol mixture, whereby to form a surface active unsaturated polyester having a number average molecular weight of from 1000 to 3000 and an acid value of from 15 to 40; (2) melting the unsaturated polyester obtained in step (1) and mixing said molten unsaturated polyester with hot water to form an oil-in-water colloidal dispersion containing from 10 to 45% by weight of said polyester in the oil phase, said dispersion being free of water-soluble protective colloids and emulsifiers, (3) adding to the dispersion obtained in step (2) at least one water-insoluble monomer selected from the group consisting of vinyl acetate, vinyl propionate, vinyl butyrate, vinyl-2-ethyl hexoate, styrene, vinyl toluene, divinyl benzene, vinyl chloride, acrylonitrile, vinyltrimethoxysilane, vinyltriethoxysilane, vinyl-tris(β-methoxyethoxy)-silane, propyl acrylate, propyl methacrylate, butyl acrylate, butyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, octyl acrylate, octyl methacrylate, methoxyethyl acrylate, methoxyethyl methacrylate, ethoxyethyl acrylate, ethoxyethyl methacrylate, butoxyethyl acrylate, butoxyethyl methacrylate, glycidyl acrylate, glycidyl methacrylate, γ-acryloxypropyltrimethoxysilane, γ-methacryloxypropyl-trimethoxysilane, γ-acryloxypropyl-tris(β-methoxyethoxy)-silane and γ-methacryloxypropyl-tris(β-methoxyethoxy)-silane, wherein the amount of said monomer is from 0.1 to 50% by weight, based on the weight of said polyester, so that said monomer is solubilized by said polyester, and adding a radical polymerization initiator and then reacting same at 50° to 70° C for about 1 to 4 hours whereby to obtain an aqueous dispersion of said polyester having said monomer grafted thereto and useful as a film-forming material which film, after drying, cannot be re-emulsified by contact with water.

Claim 14

A process for preparing a liquid resin dispersion, which comprises the steps of (1) preparing a surface active, unsaturated polyester by reacting and condensing at from 180° to 210° C, a polyester-forming dicarboxylic acid component containing at least 30 mole % of an unsaturated dicarboxylic acid or anhydride thereof selected from the group consisting of fumaric acid, maleic acid, maleic anhydride and itaconic acid, with a mixture of polyol components consisting essentially of (A) at least one ester-forming polyol selected from the group consisting of 4,4'-bis(β-hydroxyethoxyphenyl)-2,2-propane, 4,4'-bis(β-hydroxypropoxyphenyl)-2,2-propane, diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane, di-β-methylglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane and 2,2-bis(4-hydroxycyclohexyl)-propane, and (B) at least one member having the formula ##STR7## wherein R is H or CH 3 and n is from 3 to 10 wherein the amount of (B) is from 15 to 35% by weight, based on the weight of (A), wherein the amount of said dicarboxylic acid component is from 0.8 to 1.2 equivalents per equivalent of the sum of the hydroxyl and glycidyl groups of said polyol mixture, whereby to form a surface active unsaturated polyester having a number average molecular weight of from 1000 to 3000 and an acid value of from 15 to 40; (2) melting the unsaturated polyester obtained in step (1) and mixing said molten unsaturated polyester with hot water to form an oil-in-water colloidal dispersion containing from 10 to 45% by weight of said polyester in the oil phase, said dispersion being free of water-soluble protective colloids and emulsifiers, (3) adding to the dispersion obtained in step (2) at least one water-insoluble monomer selected from the group consisting of vinyl acetate, vinyl propionate, vinyl butyrate, vinyl-2-ethyl hexoate, styrene, vinyl toluene, divinyl benzene, vinyl chloride, acrylonitrile, vinyltrimethoxysilane, vinyltriethoxysilane, vinyl-tris(β-methoxyethoxy)-silane, propyl acrylate, propyl methacrylate, butyl acrylate, butyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, octyl acrylate, octyl methacrylate, methoxyethyl acrylate, methoxyethyl methacrylate, ethoxyethyl acrylate, ethoxyethyl methacrylate, butoxyethyl acrylate, butoxyethyl methacrylate, glycidyl acrylate, glycidyl methacrylate, γ-acryloxypropyltrimethoxysilane, γ-methacryloxypropyl-trimethoxysilane, γ-acryloxypropyl-tris(β-methoxyethoxy)-silane and γ-methacryloxypropyl-tris(β-methoxyethoxy)-silane, wherein the amount of said monomer is from 0.1 to 50% by weight, based on the weight of said polyester, so that said monomer is solubilized by said polyester, and adding a radical polymerization initiator and then reacting same at 50° to 70° C for about 1 to 4 hours whereby to obtain an aqueous dispersion of said polyester having said monomer grafted thereto and useful as a film-forming material which film, after drying, cannot be re-emulsified by contact with water.