Method of and apparatus for producing hollow-cylindrically shaped fibrous articles
Assignee: JNC Corp
•
Filing: 1977-05-06
•
Granted: 1978-07-11
•
Expires: 1997-05-06
Abstract
Abstract A method for producing a hollow-cylindrically shaped fibrous article stabilized by hot adhesion and an apparatus suitable to produce the same are provided. Said method comprises passing a web of gathered fiber layer carried on a conveyor belt through a heating zone, heating said web in such a way that a lower-melting component of composite fiber contained in the lower part of said web contacting the conveyor belt is not in the molten state and a lower-melting component contained in the upper part of said web is in the molten state, while separating said web from the conveyor belt, winding up said web on a take-up rod or tube in such a way that the upper surface thereof occupies the inner side of the winding, while heating the web further, cooling the wound up article and drawing out the take-up rod or tube from the shaped product. The production method of the present invention is simple and does not require complicated apparatus and the resultant product is useful for filtration.
Inventors
- 👤 Takayoshi Nakajima
- 👤 Hiroshi Sonoda
- 👤 Katsutoshi Sasaki
- 👤 Teruaki Hane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:43
CPC Classifications
B; B29; B29C; B29C67/00; B29C67/02; B29C67/04; B01; B01D; B01D17/00; B01D17/02; B01D17/04; B01D17/045; B01D29/00; B01D29/11; B01D29/111; B01D29/13; B01D29/15; B01D29/21; B01D29/216; B01D29/23; B01D29/232; B01D29/237; B01D39/00; B01D39/08; B01D39/083; B01D39/086; B01D39/14; B01D39/16; B01D39/1607; B01D39/1623; B01D39/163; B01D2201/00; B01D2201/18; B01D2201/182; B01D2239/00; B01D2239/04; B01D2239/0457; B01D2239/0471; B01D2239/0478; B01D2239/06; B01D2239/065; B01D2239/069; B01D2239/0695; B01D2239/08; B01D2239/10; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1369
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
227 words
A process for producing a hollow-cylindrically shaped fibrous articles stabilized by hot melt adhesion which comprises passing a web of gathered fiber layer having a fixed width, carried on a conveyer belt through a heating zone, heating said web of gathered fiber layer in such a way that a lower-melting component of composite fiber contained in the lower part of said web contacting the conveyer belt is in the state close to its melting point but not in the molten state and a lower-melting component contained in the upper part of said web is in the molten state, while separating said web from the conveyer belt, winding up said web on a take-up rod in such a way that the upper surface thereof occupies the inner side of the winding, further heating, during the course of winding, the lower part of the web having been contacted with the surface of the conveyer belt which is exposed to the air after the separation, adjusting the vacant space proportion during the course of the above-mentioned steps or after completion of winding, cooling the wound up article after the adjustment of the vacant space proportion of final winding, and drawing out the take-up rod from the shaped product, said web of gathered fiber layer containing at least 10% hot-melt-adhesive composite fiber consisting of a lower-melting component, and a higher-melting component.
Claim 2
Dependent Claim
227 words
A process for producing a hollow-cylindrically shaped fibrous articles stabilized by hot melt adhesion which comprises passing a web of gathered fiber layer having a fixed width, carried on a conveyer belt through a heating zone, heating said web of gathered fiber layer in such a way that a lower-melting component of composite fiber contained in the lower part of said web contacting the conveyer belt is in the state close to its melting point but not in the molten state and a lower-melting component contained in the upper part of said web is in the molten state, while separating said web from the conveyer belt, winding up said web on a take-up rod in such a way that the upper surface thereof occupies the inner side of the winding, further heating, during the course of winding, the lower part of the web having been contacted with the surface of the conveyer belt which is exposed to the air after the separation, adjusting the vacant space proportion during the course of the above-mentioned steps or after completion of winding, cooling the wound up article after the adjustment of the vacant space proportion of final winding, and drawing out the take-up rod from the shaped product, said web of gathered fiber layer containing at least 10% hot-melt-adhesive composite fiber consisting of a lower-melting component, and a higher-melting component.
Claim 3
Dependent Claim
68 words
A process for producing hollow-cylindrically shaped fibrous articles described in claim 1 wherein a web of gathered fiber layer is wound up by rotating a take-up rod by means of surface driving of the conveyer belt which is exerted to said take-up rod through the medium of said web at a certain position on the conveyer belt and pressing said web by the own weight of resulting winding.
Claim 4
Dependent Claim
33 words
A process for producing hollow-cylindrically shaped fibrous articles described in claim 1 wherein a desirable vacant space proportion is obtained by the adjustment of heating grade to said web of gathered fiber layer.
Claim 5
Dependent Claim
45 words
A process for producing hollow-cylindrically shaped fibrous articles described in claim 1 wherein said web of gathered fiber layer is wound up on a take-up rod by changing gradually the heating grade to said web to give the gradient vacant space proportion to the product.
Claim 6
Dependent Claim
76 words
A process for producing a hollow-cylindrically shaped fibrous article described in claim 4 wherein said web of gathered fiber layer is wound up while keeping the heating grade to said web constant during its travel on the conveyer belt and changing the heating grade after separation from the conveyer belt by changing a distance of location of heating sources from said web with elapse of time to give a gradient vacant space proportion to the product.
Claim 7
Dependent Claim
37 words
A process for producing a hollow-cylindrically shaped fibrous article described in claim 1 wherein ruggedness is imparted to the surface of the shaped article by rolling it on a rugged surface while holding a temperature of winding.
Claim 8
Dependent Claim
49 words
A process for producing a hollow-cylindrically shaped fibrous article described in claim 6 wherein said shaped fibrous article is caused to contact with a roller having on the surface many adjacent ridges and grooves on the circumference thereof, corresponding to the above-mentioned ridges and grooves on the outer surface.
Claim 9
Dependent Claim
66 words
A process for producing a hollow-cylindrically shaped fibrous article stabilized by hot melt adhesion described in claim 1 wherein the width of said web of gathered fiber layer is an integer time as wide as that of the length of resultant hollow-cylindrically shaped fibrous article and said web, after being heated, wound up, cooled, and separated from a take-up rod, is cut into a necessary length.
Claim 10
Dependent Claim
141 words
A method for producing a hollow-cylindrically shaped fibrous article according to claim 1 wherein production is carried out in continuous manner without stopping heating and movement of said web of gathered fiber layer by moving a formed winding from a winding site after cutting a web of gathered fiber layer at a position before said winding site when winding is complete, supplying pre-heated empty take-up rod to a empty winding site to cause it to rotate, starting the next winding by allowing the loading end of said web of gathered fiber layer to coil around the take-up rod by the formation of adhesion of the hot-melt-adhesive fiber included in the web of gathered fiber layer present near the cut end with the hot take-up rod, subjecting said moved winding to the steps of cooling and others which follows said cooling step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |