Method for fabricating reflection infrared holograms
Assignee: Raytheon Co
•
Filing: 1976-12-30
•
Granted: 1978-07-11
•
Expires: 1996-12-30
Abstract
Abstract Infrared (IR) holograms are fabricated from holograms recorded with visible light in photographic silver halide emulsions. The process facilitates image reconstruction at longer IR wavelength than presently considered possible with conventional IR holographic materials.
Inventors
- 👤 Andrejs Graube
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:35
CPC Classifications
G; G03; G03H; G03H1/00; G03H1/04; G03H1/18; G03C; G03C11/00; G03H2001/186; G03H2222/00; G03H2222/10; G03H2222/16; G03H2260/00; G03H2260/16
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
123 words
A method of forming a reflective latent hologram suitable for reconstruction at infrared wavelengths comprising: (a) first exposing a photographic silver halide emulsion film to the coherent beams emanating from a visible light source to form a latent image in said film comprised of fringe lines having preselected spacings and orientations, (b) causing said exposed film to be developed and fixed in a manner suitable for conventional photographic processes, (c) treating said film with swelling agents which cause said film to expand until a preselected volume is obtained and said fringe line spacings have been increased to a preselected distance thereby enabling said film to reflect IR radiation, and (d) geometrically fixing said expanded film to prevent further expansion or loss in volume.
Claim 2
Independent Claim
123 words
A method of forming a reflective latent hologram suitable for reconstruction at infrared wavelengths comprising: (a) first exposing a photographic silver halide emulsion film to the coherent beams emanating from a visible light source to form a latent image in said film comprised of fringe lines having preselected spacings and orientations, (b) causing said exposed film to be developed and fixed in a manner suitable for conventional photographic processes, (c) treating said film with swelling agents which cause said film to expand until a preselected volume is obtained and said fringe line spacings have been increased to a preselected distance thereby enabling said film to reflect IR radiation, and (d) geometrically fixing said expanded film to prevent further expansion or loss in volume.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said swelling agents are selected from the group consisting of water, glycerol and aqueous glycerol mixtures.
Claim 4
Dependent Claim
13 words
The method of claim 1 wherein said swelling agent is H 2 O.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein said mixture is an aqueous glycerol-mixture.
Claim 6
Independent Claim
147 words
A method of preparing reflective holograms for reconstruction as infrared holographic optical elements comprising: (a) forming a latent image in a silver halide emulsion film by exposing said film to the coherent wavefronts emanating from a visible light source calculated to produce fringe lines within said film of a prelected spacing and orientation; (b) developing, fixing and, if desired, bleaching said exposed film, by exposing said film to selected conventional developing and fixing agents; (c) treating said exposed and developed film with a swelling agent, which causes the thickness and volume of said film to be expanded to a pre-selected thickness and volume thereby increasing the spacing between the fringe lines recorded in said film to a point where IR radiation will be reflected, and (d) geometrically fixing said expanded film thickness polymerizing a monomer diffused into the film to prevent further expansion or loss in volume.
Claim 7
Independent Claim
147 words
A method of preparing reflective holograms for reconstruction as infrared holographic optical elements comprising: (a) forming a latent image in a silver halide emulsion film by exposing said film to the coherent wavefronts emanating from a visible light source calculated to produce fringe lines within said film of a prelected spacing and orientation; (b) developing, fixing and, if desired, bleaching said exposed film, by exposing said film to selected conventional developing and fixing agents; (c) treating said exposed and developed film with a swelling agent, which causes the thickness and volume of said film to be expanded to a pre-selected thickness and volume thereby increasing the spacing between the fringe lines recorded in said film to a point where IR radiation will be reflected, and (d) geometrically fixing said expanded film thickness polymerizing a monomer diffused into the film to prevent further expansion or loss in volume.
Claim 8
Dependent Claim
30 words
The method of claim 5 wherein said swelling agent is selected from the group consisting of a high relative humidity, an aqueous bath, an aqueous mixture of glycerol, and glycerol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |